A forging method for improving the mesh shape of roll blank by using radial forging machine

A radial forging machine and mesh technology, which is applied in the forging field of using a radial forging machine to improve the mesh shape of roll blanks, can solve the problems of limited forging precision, high cost, and long production cycle, and achieve precise control and reduced tensile stress , The effect of improving the mesh pass rate

Active Publication Date: 2022-02-01
建龙北满特殊钢有限责任公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the problems of high cost, long production cycle and limited forging precision of the existing method for improving the mesh shape, the present invention provides a forging method for improving the mesh shape of the roll billet by using a radial forging machine. The steps are as follows: after the billet is heated to a certain temperature, Carry out upsetting and elongation treatment in sequence, transfer the treated blank to the forging area of ​​the radial forging machine and ensure that the surface temperature of the blank is controlled at 900-920°C, and use the radial forging machine to carry out the roll body forging pass and the A-side roll neck forging in sequence Pass, B-side roll neck forging pass and finishing forging pass, air cooling for a certain period of time before the finishing forging pass to control the forging temperature at the lower limit of the final forging temperature of 850±10°C, and control the pressure of the finishing forging pass Forging the billet to the finished product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A forging method for improving the mesh shape of roll blank by using radial forging machine
  • A forging method for improving the mesh shape of roll blank by using radial forging machine
  • A forging method for improving the mesh shape of roll blank by using radial forging machine

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The specific forging method steps are as follows:

[0024] Step 1. Heating with gas furnace, the heating temperature is 1190-1210°C, the holding time is 14-18h, and the furnace temperature is raised to 1210-1230°C 2-3h before upsetting;

[0025] Step 2. Use 30MN fast forging machine to upsetting and elongating;

[0026] Step 3. Transfer the upsetting and elongated billet to the forging area of ​​the radial forging machine by using the transfer roller table, and control the surface temperature of the billet at 900°C to 920°C;

[0027] Step 4: forging with a 16MN radial forging machine, and heat-treating the forged billet to obtain a forged product. The forging frequency of the hammer head is 180 times / min. The roll body forging pass, the A-side roll neck forging pass, the B-side roll neck forging pass, and the finish forging pass are sequentially carried out by using a radial forging machine. Air cooling is performed before the finish forging pass. 30s to control the f...

Embodiment 2

[0036] The specific forging method steps are as follows:

[0037] Steps 1 to 3 are the same as in Example 1, and Step 4 is forging with a 16MN diameter forging machine, and heat-treating the forged billet to obtain a forged product. The forging frequency of the hammer head is 180 times / min. The roll body forging pass, the A-side roll neck forging pass, the B-side roll neck forging pass, and the finish forging pass are sequentially carried out by using a radial forging machine. Air cooling is performed before the finish forging pass. 30s to control the forging temperature at the lower limit of the final forging temperature of 850±10°C, control the deformation of the finishing forging pass to 20mm, and forge the blank to the finished product. The specific forging steps are:

[0038] (1) Roll body forging passes: first pass: φ520mm→φ485mm, reduction 35mm, feed speed 3.5m / min, discharge speed 4.0m / min; second pass: φ485mm→φ480mm, reduction 5mm , feed speed 3.4m / min, discharge sp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a forging method for improving the mesh level of a roll billet by using a radial forging machine, and belongs to the technical field of metallurgical machinery manufacturing. In order to solve the problems of high cost, long production cycle and limited forging precision in the existing method for improving the mesh shape, the present invention provides a forging method for improving the mesh level of the roll billet by using a radial forging machine, which includes: heating the billet to a certain temperature and then upsetting Thickening and elongation, heat the obtained billet to the forging area of ​​the radial forging machine and ensure that the surface temperature of the billet is controlled at 900-920°C, use the radial forging machine to carry out the forging pass of the roll body, the forging pass of the roll neck of the A side, and the forging pass of the B side Roll neck forging pass and finishing forging pass, air cooling for a certain period of time before finishing to control the forging temperature at the lower limit of the final forging temperature of 850±10°C, and control the reduction of the finishing forging pass according to the deformation rate of 87.3%. The billet is forged to the finished product. Applying it to the manufacture and production of roll blanks can not only achieve the purpose of improving the net shape, but also achieve the effects of reducing costs and enabling mass production.

Description

technical field [0001] The invention belongs to the technical field of metallurgical machinery manufacturing, and in particular relates to a forging method for improving the network shape of a roll blank by using a radial forging machine. Background technique [0002] For a long time, the problem of excessive network carbides that has plagued major roll blank production plants has always existed, and has become the second most difficult problem after ultrasonic flaw detection. Overweight network carbides will be used as a Fatigue crack sources exist, and accidents such as spalling and roll holding may occur at any time during the use of the rolling mill, which will bring incalculable losses to the entire rolling mill production line. At present, it can be normalized twice, and the mesh level can be further reduced by adding another normalizing, but the method has a great impact on the cost and production cycle, and is rarely used in actual production. It is also possible to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B21J5/06B21J5/08B21J1/06B21J13/06B21K27/00B21K29/00
CPCB21J5/06B21J5/08B21J1/06B21J13/06B21K27/00B21K29/00
Inventor 唐刚曹立军马园园姚凤祥刘道献李殿生陈列董贵文刘光辉于瑞芝杨云志翟书研李庆斌毛威昂贾俊林牛震张泽春赵艳荣王长志
Owner 建龙北满特殊钢有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products