Conjoined reaction type reactive acrylic resin waterproof coating and coating method thereof

A technology of acrylic resin and waterproof coating, which is applied to coatings, devices for coating liquid on the surface, and special surfaces, etc. It can solve problems such as easy peeling off of the coating, cracking of the waterproof layer, and large impact on the waterproof layer, so as to improve the adhesion of the adhesive. Excellent bonding strength and toughness, improved adhesion, and excellent waterproof performance

Inactive Publication Date: 2020-05-29
左麦斯建筑科技(南京)有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

While the reactive polymer cement waterproof coating has the above-mentioned excellent properties, it also has the common problems of waterproof coatings: the waterproof layer is greatly affected by the deformation of the base layer. Once the base layer cracks and the waterproof layer is subjected to tensile stress, the waterproof layer on both sides of the crack will There is almost no peeling area, and the tensile stress cannot be transmitted to both sides and is concentrated in

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Conjoined reaction type reactive acrylic resin waterproof coating and coating method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] A conjoined reaction type reactive acrylic resin waterproof coating, comprising a first reactive acrylic resin waterproof coating and a second reactive acrylic resin waterproof coating, the main component ratio of the first reactive acrylic resin waterproof coating is as follows:

[0048] 30 parts of butyl methacrylate;

[0049] 18 parts of butyl acrylate;

[0050] 13 parts of isooctyl acrylate;

[0051] 1 part of triethylene glycol diacrylate;

[0052] 15 parts of aliphatic elastic polyurethane resin;

[0053] 1 part of meteorological silica anti-sedimentation agent;

[0054] 5 parts of rutile titanium dioxide;

[0055] 20 parts of heavy calcium carbonate;

[0056] 0.5 parts of N,N-dimethyl-p-aniline;

[0057] 2 parts of dibenzoyl peroxide powder;

[0058] 3 parts polycarbonate;

[0059] 1 part polyamide;

[0060] Micro Repair Balls 10 servings.

[0061] The main component ratio of the second reaction type acrylic resin waterproof coating is as follows:

[0...

Embodiment 2

[0075] A conjoined reaction type reactive acrylic resin waterproof coating, comprising a first reactive acrylic resin waterproof coating and a second reactive acrylic resin waterproof coating, the main component ratio of the first reactive acrylic resin waterproof coating is as follows:

[0076] 25 parts of butyl methacrylate;

[0077] 20 parts of butyl acrylate;

[0078] 10 parts of isooctyl acrylate;

[0079] 2 parts of tetraethylene glycol diacrylate;

[0080] 18 parts of aliphatic elastic polyurethane resin;

[0081] 0.5 parts of meteorological silica anti-sedimentation agent;

[0082] 7 parts of rutile titanium dioxide;

[0083] 22 parts of heavy calcium carbonate;

[0084] 0.8 parts of N, N-dimethyl-p-aniline;

[0085] 1 part of dibenzoyl peroxide powder;

[0086] 3.5 parts of polycarbonate;

[0087] 2 parts polyamide;

[0088] Micro Repair Balls 10 servings.

[0089] The main component ratio of the second reaction type acrylic resin waterproof coating is as fo...

Embodiment 3

[0103] A conjoined reaction type reactive acrylic resin waterproof coating, comprising a first reactive acrylic resin waterproof coating and a second reactive acrylic resin waterproof coating, the main component ratio of the first reactive acrylic resin waterproof coating is as follows:

[0104] 20 parts of butyl methacrylate;

[0105] 15 parts of butyl acrylate;

[0106] 12 parts of isooctyl acrylate;

[0107] 2 parts of tetraethylene glycol diacrylate;

[0108] 20 parts of aliphatic elastic polyurethane resin;

[0109] 1.5 parts of meteorological silica anti-sedimentation agent;

[0110] 8 parts of rutile titanium dioxide;

[0111] 25 parts of heavy calcium carbonate;

[0112] 1 part of N,N-dimethyl-p-aniline;

[0113] 1.5 parts of dibenzoyl peroxide powder;

[0114] 4 parts polycarbonate;

[0115] 4 parts polyamide;

[0116] Micro Repair Balls 10 servings.

[0117] The main component ratio of the second reaction type acrylic resin waterproof coating is as follows:...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a conjoined reaction type reactive acrylic resin waterproof coating and a coating method thereof, and belongs to the field of waterproof coatings; the conjoined reaction type reactive acrylic resin waterproof coating comprises a first reactive acrylic resin waterproof coating and a second reactive acrylic resin waterproof coating, and the two reactive acrylic resin waterproof coatings comprise the following main components: 15 to 30 parts of butyl methacrylate, 10 to 20 parts of butyl acrylate, 5 to 15 parts of 2-ethylhexyl acrylate, 1 to 3 parts of triethylene glycol diacrylate, 15 to 30 parts of aliphatic elastic polyurethane resin, 0.5-2 parts of a fumed silica anti-settling agent, and 5 to 10 parts of rutile type titanium dioxide. The reactive acrylic resin waterproof coating is divided into two types which are respectively used as an inner layer and an outer layer, and in the coating process, the two waterproof coatings react with each other and are bondedto form a 'connection reaction', so that the bonding degree between the two waterproof coating layers is greatly improved, the coating layer of the outer layer is not easy to fall off, and the waterproof performance is excellent.

Description

technical field [0001] The invention relates to the field of waterproof coatings, and more specifically relates to a conjoined reaction type reactive acrylic resin waterproof coating and a coating method thereof. Background technique [0002] Waterproof coating The waterproof film formed by the coating on the base layer after curing has certain strength, good extensibility, crack resistance, impermeability and weather resistance, and has good temperature adaptability, easy operation and easy maintenance. and maintenance. Compared with the waterproof membrane, the waterproof coating has strong adaptability to the base layer, and the waterproof layer has no seams, which is more reliable. Due to the above characteristics, waterproof coating is one of the main waterproof materials often used in waterproofing projects. [0003] Reactive polymer cement waterproof coating, as an improved variety of polymer cement waterproof coating, is a high-solid content coating that reacts and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D4/06C09D4/02C09D7/61C09D7/62C09D7/63C09D7/65C09D7/45B05D7/14B05D7/24B05D5/00
CPCB05D5/00B05D7/14B05D7/24B05D7/54B05D2451/00B05D2502/00B05D2601/20B05D2601/22B05D2602/00C09D4/06C09D7/45C09D7/61C09D7/62C09D7/63C09D7/65C09D7/70B05D2420/01B05D2420/02
Inventor 朱栋杰
Owner 左麦斯建筑科技(南京)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap