Joint body and automobile seat frame

A joint body and component technology, applied in the direction of seat frames, vehicle seats, connecting components, etc., can solve problems such as difficulty in obtaining product strength

Inactive Publication Date: 2022-03-25
NHK SPRING CO LTD
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Aluminum-based materials are suitable for lightweight, but if aluminum-based materials are used, it is difficult to obtain sufficient product strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Joint body and automobile seat frame
  • Joint body and automobile seat frame
  • Joint body and automobile seat frame

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach

[0028] First, an automobile seat frame according to an embodiment of the present invention will be described in detail with reference to the drawings. figure 1 It is a front view of an automobile seat frame according to an embodiment of the present invention. figure 2 for figure 1 rear view of car seat frame. image 3 for along figure 2 A partially enlarged cross-sectional view of line A-A.

[0029] An automobile seat frame 1 includes: a rear panel 2 formed of aluminum or an aluminum alloy; a frame tube 3 formed of iron or an iron-based alloy; and fastening pins 4 for fastening the rear panel 2 and the frame tube 3 . In the automobile seat frame 1 , the frame pipe 3 is fixed to the rear panel 2 by joining the fastening pin 4 and the frame pipe 3 in a state where the fastening pin 4 penetrates the rear panel 2 .

[0030] Figure 4 It is a rear view showing the structure of the rear panel of the automobile seat frame according to the embodiment of the present invention. ...

Embodiment 1

[0064] An aluminum panel (corresponding to the rear panel 2) formed of an aluminum alloy (A5182) with a through-hole (corresponding to the through-hole 20) and further cationic-coated on the surface is used, the plate thickness is 1.6mm, and the tensile strength Frame pipes with a strength of about 1470MPa and a Vickers hardness of HV478 (STAM (electric resistance welded carbon steel pipe for automotive structures): corresponding to frame pipe 3), and those formed of plates with a thickness of 0.8mm and a Vickers hardness of HV92 fastening pin (corresponding to fastening pin 4A), to carry out resistance spot welding with a current value of 5.0kA, an energization time of 100 milliseconds and a welding pressure of the fastening pin to the frame tube of 0.5kN, thus manufacturing such as Figure 9 The joint body shown was used as a test piece. In addition, the diameter of the protruding portion of the fastening pin is smaller than the diameter of the through-hole of the aluminum p...

Embodiment 2

[0066] In the test piece of Example 2, the wall thickness of the frame tube was set to be 1.0 mm, the tensile strength was about 980 MPa, the Vickers hardness was HV352, and the current value at the time of joining was set to 4.0 kA. In addition, it was the same as that of Example 1. same. In Example 2, the difference in hardness before joining was 260.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

A bonded body according to the present invention includes: a thin plate having a plurality of through holes formed along its outer periphery; a first member having a base and a protrusion, a part of the base is in contact with the thin plate, and the protrusion is opposed to the surface of the base. That is, the surface of the side in contact with the thin plate protrudes and is inserted into the through hole; and the second member is arranged on the opposite side of the base through the thin plate and is formed of the same type of material as the first member, wherein the thin plate is made of The specific gravity is formed of a material having a smaller specific gravity than the materials constituting the first member and the second member, and the second member and the end portion on the side opposite to the side connected to the base of the protruding portion are bonded by melting and solidifying a part thereof, and the second member is connected with the second member. The joint interface between the member and the protruding portion is centered, and the difference in hardness after joining within 30% of the range in the direction perpendicular to the joint interface is 90% or less of the difference in hardness before joining.

Description

technical field [0001] The present invention relates to a joint body and an automobile seat frame. Background technique [0002] In recent years, technologies for replacing iron-based materials with aluminum-based materials have been studied for the purpose of reducing the weight of various parts for automobiles. Aluminum-based materials are suitable for light weight, but if all aluminum-based materials are used, it is difficult to obtain sufficient product strength. Therefore, a proposal to replace part of the iron-based material with an aluminum-based material has been studied. When substituting an iron-based material with an aluminum-based material, it is necessary to join the iron-based material and the aluminum-based material. [0003] Various techniques have been proposed for suppressing the generation of intermetallic compounds that cause a decrease in joint strength when joining an iron-based material and an aluminum-based material by welding (see, for example, Pat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B60N2/68B23K11/11B23K11/20F16B11/00
CPCB23K11/11B23K11/20B60N2/682B60N2/686B23K2101/006B23K2103/20F16B5/0096F16B5/123
Inventor 山内雄一郎依田悠佐藤拓也后藤克司安藤公一佐藤文音
Owner NHK SPRING CO LTD