Preparation method and application of a magnetic covalent organic framework compound for adsorbing triphenylmethane dyes

A technology of covalent organic framework and triphenylmethane, applied in alkali metal compounds, chemical instruments and methods, inorganic chemistry, etc., can solve the problems of complicated operation and long reaction time, and achieve simplified synthesis process, short synthesis time and preparation The effect of simple method

Active Publication Date: 2022-05-17
HARBIN INST OF TECH
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention provides a preparation method and application of a magnetic covalent organic framework compound that adsorbs triphenylmethane dyes in order to solve the technical problems of complex operation and long reaction time in the existing method for synthesizing covalent organic framework (COFs) compounds

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and application of a magnetic covalent organic framework compound for adsorbing triphenylmethane dyes
  • Preparation method and application of a magnetic covalent organic framework compound for adsorbing triphenylmethane dyes
  • Preparation method and application of a magnetic covalent organic framework compound for adsorbing triphenylmethane dyes

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0045] Embodiment 1: A method for preparing a magnetic covalent organic framework compound that adsorbs triphenylmethane dyes in this embodiment is carried out in the following steps:

[0046] 1. Superparamagnetic carboxylation of Fe 3 o 4 Magnetic nanoparticles Fe 3 o 4 Preparation of -COOH:

[0047] ①.Weigh 16.5g of FeCl 3 ·6H 2 O and 25g Na 3 Cit·2H 2 O was dissolved in 500mL of ethylene glycol, and ultrasonically treated at 40kHz for 40min to obtain a yellow transparent solution;

[0048] ②. Under the condition that the temperature of the water bath is 50° C. and the stirring speed is 200 rpm, add 30 g of sodium acetate to the yellow transparent solution obtained in step ①, and stir for 30 minutes to obtain a brown transparent solution;

[0049] ③.Transfer the brown transparent solution obtained in step ② into a stainless steel reaction kettle, and react at a temperature of 200°C for 10h;

[0050] ④. Collect the product obtained in step ③ with a magnet, and then w...

specific Embodiment approach 2

[0092] Specific embodiment two: the application of a magnetic covalent organic framework compound that adsorbs triphenylmethane dyes in this embodiment: the Fe prepared in specific embodiment one 3 o 4 -COOH@COF is used as a material for detecting triphenylmethane dyes in the field of aquaculture.

[0093] The application effect of this embodiment is verified by the following tests, and the specific test process is as follows:

[0094] Test a: the Fe prepared by the specific embodiment one 3 o 4 -COOH@COF was applied to the adsorption detection of five triphenylmethane dyes standards of MG, RB, CV, BG and VPBO, and then the detection method of the dye was constructed by HPLC, and the linearity, LOD and RSD of the detection method were evaluated .

[0095] Conclusion: as shown in Table 6, the linear relationship of the 5 dyes is good, and the linear correlation coefficient (R 2 ) are higher than 0.9990. The LOD and LOQ of these dyes were calculated at S / N ratios of 3 and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
adsorption capacityaaaaaaaaaa
adsorption capacityaaaaaaaaaa
adsorption capacityaaaaaaaaaa
Login to View More

Abstract

A preparation method and application of a magnetic covalent organic framework compound for adsorbing triphenylmethane dyes. The invention belongs to the field of preparation of magnetic covalent organic framework compounds. The invention aims to solve the technical problems of complicated operation and long reaction time of the existing methods for synthesizing covalent organic framework (COFs) compounds. Method: 1) Preparation of carboxylated magnetic nanoparticles (Fe 3 o 4 ‑COOH); 2) Synthesis of magnetic covalent organic frameworks (Fe 3 o 4 ‑COOH@COF). The preparation method of the invention is simple, the synthesis time is short, and only 3 hours are needed at a high temperature of 120°C. Prepared Fe 3 o 4 ‑COOH@COF has magnetic responsiveness, high specific surface area, thermal stability, and high adsorption performance (42.8mg / g~500mg / g), and can quickly extract triphenylmethane cationic dyes from complex samples within 10 minutes. Realize the multi-residue detection of triphenylmethane dyes, simplify the pretreatment process of complex samples, and greatly improve the separation efficiency.

Description

technical field [0001] The invention belongs to the field of preparation of magnetic covalent organic framework compounds, in particular to a preparation method and application of magnetic covalent organic framework compounds for adsorbing triphenylmethane dyes. Background technique [0002] Triphenylmethane dyes, such as malachite green (MG) and crystal violet (CV), have been widely used in aquaculture because of their excellent efficacy in preventing and treating infectious diseases of fish and other aquatic products. However, in follow-up studies, it was found that MG and CV are carcinogenic and mutagenic, so their use is prohibited. Since 2002, we can find that the MG and CV in the Food and Feed Rapid Alert Report (RARFF) have been significantly reduced, that is, its prohibition effect has been reflected, but there are still a small number of unscrupulous merchants using it. Some researchers proposed to use bright green BG instead of MG, but BG with a structure similar ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/22B01J20/28B01J20/30C02F1/28C02F1/48C02F101/30
CPCB01J20/226B01J20/06B01J20/28009B01J20/28057C02F1/285C02F1/488C02F2101/308
Inventor 杨鑫赵海田刘婧怡
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com