A kind of welding wire suitable for ti62a alloy used in manned submersible and its preparation method

A manned submersible, alloy technology, used in welding equipment, metal processing equipment, manufacturing tools, etc., can solve problems such as lack of

Active Publication Date: 2022-01-28
725TH RES INST OF CHINA SHIPBUILDING INDAL CORP
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problem of lack of welding wire for Ti62A alloy used in manned submersibles in the prior art, the invention provides a welding wire suitable for Ti62A alloy used in manned submersibles and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of welding wire suitable for ti62a alloy used in manned submersible and its preparation method
  • A kind of welding wire suitable for ti62a alloy used in manned submersible and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0024] Above-mentioned a kind of welding wire preparation method applicable to manned submersible Ti62A alloy comprises the following steps:

[0025] Step 1: Select grade 0 sponge titanium, aluminum-vanadium master alloy, aluminum-chromium master alloy, aluminum-zirconium master alloy, aluminum-molybdenum master alloy and aluminum-tin master alloy as raw materials for mixing treatment, and then press and assemble welding, using vacuum electron Beam welding to obtain consumable electrodes.

[0026] Step 2: The consumable electrode obtained in Step 1 is smelted twice successively to obtain a secondary ingot.

[0027] Step 3: peeling off the secondary ingot obtained in step 2, cutting off the riser, and then forging the billet to obtain a billet.

[0028] Step 4: Perform free forging on the blank obtained in step 3. The free forging temperature is 950~1100°C, the forging ratio is not greater than 2:1, the forging times are not less than 20 times, and the holding time is 30~60 mi...

Embodiment 1

[0031] The welding wire is made of 0-grade sponge titanium, aluminum-vanadium master alloy, aluminum-chromium master alloy, aluminum-zirconium master alloy, aluminum-molybdenum master alloy and aluminum-tin master alloy. The components include Al: 6% and V: 1% by weight , Cr: 0.5%, Zr: 2%, Mo: 2%, Sn: 1%, O: 0.08%, and the balance is Ti and unavoidable impurities.

[0032] Grade 0 sponge titanium, aluminum-vanadium master alloy, aluminum-chromium master alloy, aluminum-zirconium master alloy, aluminum-molybdenum master alloy and aluminum-tin master alloy are respectively pressed into electrodes according to the above mass percentages, and the electrodes are welded by vacuum electron beam welding. Electric arc furnace consumption.

[0033] The ingot is prepared by vacuum consumable arc melting technology, and the pre-melting vacuum degree should reach 10 -2 Pa, in order to ensure the uniform composition of the alloy, the number of smelting times is ≥ 2 times, after the cast in...

Embodiment 2

[0043] The welding wire is made of 0-grade sponge titanium, aluminum-vanadium master alloy, aluminum-chromium master alloy, aluminum-zirconium master alloy, aluminum-molybdenum master alloy and aluminum-tin master alloy. The components include Al: 5%, V: 1% by weight , Cr: 1%, Zr: 2%, Mo: 2.5%, Sn: 1.5%, O: 0.08%, and the balance is Ti and unavoidable impurities.

[0044] Grade 0 sponge titanium, aluminum-vanadium master alloy, aluminum-chromium master alloy, aluminum-zirconium master alloy, aluminum-molybdenum master alloy and aluminum-tin master alloy are respectively pressed into electrodes according to the above mass percentages, and the electrodes are welded by vacuum electron beam welding. Electric arc furnace consumption.

[0045] The ingot is prepared by vacuum consumable arc melting technology, and the pre-melting vacuum degree should reach 10 -2 Pa, in order to ensure the uniform composition of the alloy, the number of smelting times is ≥ 2 times, after the cast ing...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
impact absorption energyaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

A welding wire suitable for Ti62A alloy used in manned submersibles and its preparation method, the welding wire is made of 0-grade sponge titanium, aluminum vanadium master alloy, aluminum chromium master alloy, aluminum zirconium master alloy, aluminum molybdenum master alloy and aluminum tin master alloy , each component includes Al: 4.5-6.75%, V: 0.5-1.5%, Cr: 0.3-1.75%, Zr: 1.5-2.5%, Mo: 1.5-3.0%, Sn: 0.5-2.0%, The balance is Ti and unavoidable impurities. It is suitable for manned diving after pressing, assembly welding, double melting, blank forging, free forging, rolling, drawing, straightening and polishing, and finally vacuum annealing. The welding wire of Ti62A alloy is used for the device, and the performance of the welding wire meets the impact absorption energy KV 2 ≥20J, tensile strength Rm≥1010MPa, suitable for Ti62A alloy TIG welding and MIG welding, etc., meeting the needs of Ti62A alloy special matching welding wire for manned submersibles in my country.

Description

technical field [0001] The invention relates to the field of welding of Ti62A alloys for manned submersibles, in particular to a welding wire suitable for Ti62A alloys for manned submersibles and a preparation method thereof. Background technique [0002] Titanium and titanium alloys have excellent properties such as high specific strength, corrosion resistance, and non-magnetism, especially in seawater and acidic hydrocarbons. They have good corrosion resistance and are the preferred materials for ships and ocean engineering. Therefore, titanium alloys are known as for "Ocean Metal". Marine titanium alloy is an important research and development direction of my country's titanium industry, and it is an extremely important application field in the future. [0003] With the substantial increase in the diving depth of my country's manned submersibles, its service environment has become harsher, and the spherical shell of the manned cabin has higher and higher requirements for...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B23K35/32B23K35/40
CPCB23K35/325B23K35/40
Inventor 吕逸帆雷家峰刘希林安飞鹏
Owner 725TH RES INST OF CHINA SHIPBUILDING INDAL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap