A kind of inorganic building sound-absorbing material and preparation method thereof

A sound-absorbing material and construction technology, applied in the field of sound-absorbing materials, can solve the problems of sound-absorbing effect decline, particle detachment, poor durability, etc., and achieve the effect of improving water repellency, avoiding shedding, and ensuring durability

Active Publication Date: 2022-01-28
深圳市广瑞基装饰工程有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide an inorganic building sound-absorbing material and its preparation method, so as to effectively solve the problems of poor durability, reduced sound-absorbing effect after being damp, and particle detachment in the existing inorganic particle-based sound-absorbing materials proposed in the background technology. question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of inorganic building sound-absorbing material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] In the embodiment of the present invention, an inorganic building sound-absorbing material provided includes the following raw materials in mass percentage:

[0033] Modified porous ceramsite 45%

[0034] Modified expanded perlite 10%

[0035] Cement (sulfoaluminate cement) 20%

[0036] Silica fume 15%

[0037] Inorganic fiber (glass fiber) 2%

[0038] Foaming agent (sodium lauryl sulfate) 5%

[0039] Tackifier (polyethylene oxide) 3%

[0040] For the above components, its preparation method is as follows:

[0041] S1. Raw material pretreatment: Prepare modified aggregate mixed with modified porous ceramsite and modified expanded perlite, including:

[0042] Mix porous ceramsite and expanded perlite at a mass ratio of 45:10 to obtain a mixture;

[0043] Mix organosilane, low-molecular organosiloxane, curing agent, surface active treatment agent and water at a ratio of 80:20:0.2:0.05:899.75 to obtain a hydrophobic treatment modifier solution;

[0044] Immerse the...

Embodiment 2

[0051] In the embodiment of the present invention, an inorganic building sound-absorbing material provided includes the following raw materials in mass percentage:

[0052] Modified porous ceramsite 40%

[0053] Modified expanded perlite 8%

[0054] Cement (sulfoaluminate cement) 27%

[0055] Silica fume 13%

[0056] Inorganic fiber (glass fiber) 3%

[0057] Foaming agent (sodium lauryl sulfate) 4%

[0058] Tackifier (polyethylene oxide) 5%

[0059] For the above components, its preparation method is as follows:

[0060] S1. Raw material pretreatment: Prepare modified aggregate mixed with modified porous ceramsite and modified expanded perlite, including:

[0061] Mix porous ceramsite and expanded perlite at a mass ratio of 10:2 to obtain a mixture;

[0062] Mix organosilane, low-molecular organosiloxane, curing agent, surface active treatment agent and water at a ratio of 80:20:0.2:0.05:899.75 to obtain a hydrophobic treatment modifier solution;

[0063]Immerse the mi...

Embodiment 3

[0070] In the embodiment of the present invention, an inorganic building sound-absorbing material provided includes the following raw materials in mass percentage:

[0071] Modified porous ceramsite 37%

[0072] Modified expanded perlite 11%

[0073] Cement (sulfoaluminate cement) 29%

[0074] Silica fume 10%

[0075] Inorganic fiber (glass fiber) 1%

[0076] Foaming agent (sodium lauryl sulfate) 8%

[0077] Tackifier (polyethylene oxide) 4%

[0078] For the above components, its preparation method is as follows:

[0079] S1. Raw material pretreatment: Prepare modified aggregate mixed with modified porous ceramsite and modified expanded perlite, including:

[0080] Mix porous ceramsite and expanded perlite at a mass ratio of 37:11 to obtain a mixture;

[0081] Mix organosilane, low-molecular organosiloxane, curing agent, surface active treatment agent and water at a ratio of 80:20:0.2:0.05:899.75 to obtain a hydrophobic treatment modifier solution;

[0082] Immerse the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of sound-absorbing materials, and discloses an inorganic building sound-absorbing material and a preparation method thereof. The sound-absorbing material includes the following raw materials in mass percentages: 45-60% of modified aggregate, 15-30% of cement, Silica fume 10-15%, inorganic fiber 1-5%, foaming agent 1-10%, tackifier 3-5%; the modified aggregate includes modified porous ceramsite and modified expanded perlite, and The mass ratio of the modified porous ceramsite to the modified expanded perlite is 10:1-3; the cement is sulfoaluminate cement; the inorganic fiber is at least one of glass fiber or ceramic fiber; the foaming The agent includes at least one of sodium lauryl sulfate or fatty alcohol polyoxyethylene ether sodium sulfate; the thickener is polyethylene oxide; in summary, the hydrophobic modification treatment is carried out by using the modifier attached to the porous aggregate , so as to effectively improve the waterproof effect of the final formed sound-absorbing material, thereby avoiding the problem that the sound-absorbing material is affected by moisture during use.

Description

technical field [0001] The invention belongs to the technical field of sound-absorbing materials, and in particular relates to an inorganic building sound-absorbing material and a preparation method thereof. Background technique [0002] Sound-absorbing material is a functional material for building decoration. It has the dual requirements of sound absorption and decoration. It must be beautiful and meet the special requirements of sound absorption. Any material can absorb sound, but the degree of absorption varies greatly. It is usually a material with an average sound absorption coefficient greater than 0.2, which is listed as a sound-absorbing material. [0003] At present, the existing inorganic sound-absorbing materials in the market mainly include fiber-type sound-absorbing materials, granular sound-absorbing materials and foam-type sound-absorbing materials; among them, particle-type sound-absorbing materials are taken as an example, which have good sound absorption ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/06C04B14/42C04B14/38C04B24/32C04B20/10C04B38/02C04B111/52
CPCC04B28/06C04B14/42C04B14/46C04B24/32C04B20/1051C04B2201/50C04B2111/52C04B18/027C04B14/185C04B18/146C04B24/16C04B38/02C04B20/1037C04B20/1022
Inventor 肖忠平刘雁
Owner 深圳市广瑞基装饰工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap