A kind of wear-resistant frit, preparation method of frit and glaze using same

A technology of frit and raw materials, applied in the field of preparation methods and glazes using it, to achieve the effects of high transparency, good transparency, and improved wear resistance

Active Publication Date: 2022-03-25
佛山市东鹏陶瓷发展有限公司 +2
View PDF16 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In view of the problems raised by the background technology, the purpose of the present invention is to propose a wear-resistant frit with good transparency and good wear resistance, which solves the contradiction between the high transparency and good wear resistance of the existing transparent frit. question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of wear-resistant frit, preparation method of frit and glaze using same
  • A kind of wear-resistant frit, preparation method of frit and glaze using same
  • A kind of wear-resistant frit, preparation method of frit and glaze using same

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0033] The preparation method of described wear-resistant frit comprises the following steps:

[0034] The step of preparing the prefabricated frit: mixing the raw materials of the prefabricated frit according to the ratio, firing at high temperature, quenching in water to obtain the prefabricated frit, powdering the prefabricated frit, sieving, and drying;

[0035] The steps of preparing the wear-resistant frit: mixing the raw materials of the wear-resistant frit according to the ratio, firing at high temperature, and quenching in water to obtain the wear-resistant frit.

[0036] By first preparing the prefabricated frit, the prefabricated frit obtained through high-temperature firing process is added as a raw material to the raw material of the wear-resistant frit, because the chemical composition contained in the prefabricated frit is close to cordierite The chemical composition introduced into the wear-resistant frit is beneficial to the precipitation of cordierite crystal...

Embodiment 1～5

[0065] A wear-resistant frit is prepared according to the following steps:

[0066] (1) Steps for preparing prefabricated frit: mix the raw materials of prefabricated frit according to the ratio in Table 1, and perform high-temperature firing (wherein, the temperature curve of high-temperature firing is from room temperature to 1100°C, which takes 100 minutes and the heating rate 11°C / min; it takes 60 minutes to rise from 1100°C to 1530°C, and the heating rate is 7.2°C / min; keep at 1530°C for 25 minutes), quench in water to obtain prefabricated frit, and prefabricated frit is powdered and sieved (get 180 mesh sieves), drying;

[0067] (2) Steps for preparing wear-resistant frit: mix the raw materials of wear-resistant frit according to the ratio in Table 2, and perform high-temperature firing (from normal temperature to 1100°C, it takes 100min, and the heating rate is 11°C / min; It takes 60 minutes to rise from 1100°C to 1530°C, and the heating rate is 7.2°C / min; hold at 1530°...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
transmittivityaaaaaaaaaa
Mohs hardnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a wear-resistant frit, a preparation method of the frit and a glaze using the same. A wear-resistant frit is calculated according to the mass percentage, and its raw materials include the following components: prefabricated frit 20-36%, 20-38% of talc, 2-5% of zinc oxide, 8-12% of calcined alumina, 20-24% of kaolin and 7-9% of fluorite; calculated according to mass percentage, the raw materials of the prefabricated frit include the following components : Potassium feldspar 15-20%, dolomite 5-10%, talc 45-55%, zinc oxide 2-5% and aluminum oxide 20-25%. The wear-resistant frit has good transparency and good wear resistance. The preparation method of the wear-resistant frit is simple, and each raw material component is fully melted during the high-temperature firing process. The prepared wear-resistant frit is The block has high transparency and good wear resistance. Using the glaze material of the wear-resistant frit, the glaze layer has good wear resistance, and the glaze surface has good surface gloss and good light transmission performance.

Description

technical field [0001] The invention relates to the technical field of architectural ceramics, in particular to a wear-resistant frit, a preparation method of the frit and a glaze using the frit. Background technique [0002] With the rapid development of the ceramic industry, the research and development of ceramic products is not only reflected in the continuous expansion of product varieties and continuous innovation of styles, but also in the continuous improvement of the appearance and quality of glazed surfaces. Frit is one of the main raw materials for glazes. In ceramic products using frit glaze, the quality of the frit directly affects the quality of the glazed surface of the product, thus directly affecting the quality of the product. In order to improve the gloss and transparency of the glaze, transparent frit is usually added to the glaze. At present, in order to increase the transparency of the frit, a large amount of raw materials such as potassium, albite and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/06
CPCC03C8/06
Inventor 李苏波罗强钟保民徐瑜
Owner 佛山市东鹏陶瓷发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap