Cross-linked polyethylene insulated anti-interference shielding naval vessel cable and preparation method thereof

A technology of cross-linked polyethylene and ships, applied in the direction of insulated cables, cable/conductor manufacturing, insulated conductors, etc., can solve the problems of communication effect influence, poor shielding effect, rapid burning, etc., and achieve increased anti-interference and high magnetic permeability The effect of high efficiency and excellent conductivity

Active Publication Date: 2021-01-12
安徽龙庵电缆集团有限公司
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The existing anti-jamming shielded naval cable is in use, because of its poor shielding effect, it will affect the communication effect, and its own flame retardancy is poor, and it will burn rapidly when exposed to an open flame

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cross-linked polyethylene insulated anti-interference shielding naval vessel cable and preparation method thereof
  • Cross-linked polyethylene insulated anti-interference shielding naval vessel cable and preparation method thereof
  • Cross-linked polyethylene insulated anti-interference shielding naval vessel cable and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] A cross-linked polyethylene insulated anti-interference shielded naval cable, comprising a conductor 1, a separate shielding layer 3, a wrapping layer 4, and a total shielding layer 5, the outer surface of the conductor 1 is covered with an insulating layer 2, and the conductor 1 and the insulating layer 2 are insulated Insulated wire cores are formed, and every two insulated wire cores are twisted groups, and the twisted groups are covered with a sub-shielding layer 3, and multiple pairs of twisted groups are covered with a wrapping layer 4, and the outer surface of the wrapping layer 4 is covered with The overall shielding layer 5, the outer surface of the overall shielding layer 5 is covered with a sheath 6;

[0044] The sub-shielding layer 3 is made of shielding material, and the shielding material is made by the following steps:

[0045] Step A1: Add concentrated sulfuric acid into the reaction kettle, add sodium nitrate and graphite at a speed of 150r / min and a te...

Embodiment 2

[0052] A cross-linked polyethylene insulated anti-interference shielded naval cable, comprising a conductor 1, a separate shielding layer 3, a wrapping layer 4, and a total shielding layer 5, the outer surface of the conductor 1 is covered with an insulating layer 2, and the conductor 1 and the insulating layer 2 are insulated Insulated wire cores are formed, and every two insulated wire cores are twisted groups, and the twisted groups are covered with a sub-shielding layer 3, and multiple pairs of twisted groups are covered with a wrapping layer 4, and the outer surface of the wrapping layer 4 is covered with The overall shielding layer 5, the outer surface of the overall shielding layer 5 is covered with a sheath 6;

[0053] The sub-shielding layer 3 is made of shielding material, and the shielding material is made by the following steps:

[0054] Step A1: Add concentrated sulfuric acid into the reaction kettle, add sodium nitrate and graphite at a speed of 180r / min and a te...

Embodiment 3

[0061] A cross-linked polyethylene insulated anti-interference shielded naval cable, comprising a conductor 1, a separate shielding layer 3, a wrapping layer 4, and a total shielding layer 5, the outer surface of the conductor 1 is covered with an insulating layer 2, and the conductor 1 and the insulating layer 2 are insulated Insulated wire cores are formed, and every two insulated wire cores are twisted groups, and the twisted groups are covered with a sub-shielding layer 3, and multiple pairs of twisted groups are covered with a wrapping layer 4, and the outer surface of the wrapping layer 4 is covered with The overall shielding layer 5, the outer surface of the overall shielding layer 5 is covered with a sheath 6;

[0062] The sub-shielding layer 3 is made of shielding material, and the shielding material is made by the following steps:

[0063] Step A1: Add concentrated sulfuric acid into the reaction kettle, add sodium nitrate and graphite at a speed of 200r / min and a te...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
electrical resistivityaaaaaaaaaa
electrical resistivityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a cross-linked polyethylene insulated anti-interference shielding naval vessel cable and a preparation method thereof, a shielding material is prepared in the process of preparing the anti-interference shielding naval vessel cable, the shielding material contains a large number of high-resistance metal objects, and the high resistivity enables electromagnetic waves to easily enter and rapidly attenuate; and the obtained cable can still keep high magnetic conductivity at high frequency. The graphene, the carbon nano tube and the copper have excellent conductivity, so that the shielding carrier has electrical loss and magnetic loss at the same time, impedance matching of electromagnetic absorption is achieved, the absorption frequency band is widened, the anti-interference performance is improved, oxygen-containing acid of phosphorus can be generated in the combustion process. Phosphorus oxyacid catalyzes a hydroxyl-containing compound to be dehydrated into carbon, then a coke layer is generated on the surface of the thermal insulation material, and the coke layer can isolate oxygen and heat to extinguish flame, so that the flame retardance of the cable is further improved.

Description

technical field [0001] The invention belongs to the technical field of cable preparation, and in particular relates to a cross-linked polyethylene insulated anti-interference shielded naval cable and a preparation method thereof. Background technique [0002] With the improvement of the automation level of ships and offshore platforms, a large number of electronic equipment and instruments need to transmit signals through various communication cables. Due to the harsh environment of ships, at present, many ships replace cables more frequently for safety reasons, which greatly While increasing the operating cost, it also restricts the execution of long-term offshore tasks, so the cable material is strengthened in the application. [0003] The existing anti-jamming shielded ship cable has poor self-shielding effect during use, which will affect the communication effect, and its own poor flame retardancy will cause rapid burning when exposed to open flames. Contents of the in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01B11/06H01B11/12H01B7/295H01B13/00H01B13/22C08L23/08C08K3/22C08K5/14
CPCH01B11/06H01B11/12H01B7/295H01B13/00H01B13/22C08L23/0853C08L2205/03C08L23/0815C08L23/0869C08K3/22C08K5/14
Inventor 魏善恒吉云星王飞陈国栋鲍超凡何夕木程龙云
Owner 安徽龙庵电缆集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com