Graphene heating fabric and preparation method thereof

A heating fabric, graphene technology, applied in the direction of electric heating devices, ohmic resistance heating, textiles and papermaking, etc., to achieve good heating effect, broad market prospects, and good heating performance

Inactive Publication Date: 2021-02-09
陈建华
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to provide a graphene heating fabric and a preparation method thereof, to solve the problem that the existing graphene electric heating film proposed in the above background technology cannot be combined with wall coverings to replace indoor wall heating because it is based on PVC film

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Graphene heating fabric and preparation method thereof
  • Graphene heating fabric and preparation method thereof
  • Graphene heating fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] see Figure 2-3 , a graphene heating fabric, comprising: a substrate, a conductive graphene ink layer arranged on the substrate and a copper foil wire, and an insulating adhesive layer coated on the surface of the conductive graphene ink layer, the substrate is An insulating film with a thickness of 30 microns, and the conductive graphene ink layer is composed of graphene and conductive ink according to a mass ratio of 13:1.

[0029] Further, in this embodiment, the insulating glue is a kind of composite glue with good electrical insulation performance, which can be used for pouring cable joints, impregnating motors, electrical appliances, generator windings, and making transformers, capacitors or radio devices, etc. Sealing and insulation can be existing products, such as insulating glue such as polyester, epoxy, polyurethane, polybutadiene acid, silicone, polyesterimide and polyimide, which can be selected according to the specific needs, and are not specified here. ...

Embodiment 2

[0034] see Figure 2-3 , a graphene heating fabric, comprising: a substrate, a conductive graphene ink layer arranged on the substrate and a copper foil wire, and an insulating adhesive layer coated on the surface of the conductive graphene ink layer, the substrate is An insulating film with a thickness of 200 microns, and the conductive graphene ink layer is composed of graphene and conductive ink in a mass ratio of 19:1.

[0035] Further, in this embodiment, the insulating glue is a kind of composite glue with good electrical insulation performance, which can be used for pouring cable joints, impregnating motors, electrical appliances, generator windings, and making transformers, capacitors or radio devices, etc. Sealing and insulation can be existing products, such as insulating glue such as polyester, epoxy, polyurethane, polybutadiene acid, silicone, polyesterimide and polyimide, which can be selected according to the specific needs, and are not specified here. limited. ...

Embodiment 3

[0039] see Figure 1-3 , a preparation method of graphene heating fabric, the steps are as follows:

[0040] 1) Weigh graphene and conductive ink according to the ratio of 13-19:1 by mass and stir and mix them evenly to obtain conductive graphene slurry;

[0041] 2) Coating the conductive graphene slurry obtained in the copper foil wire and step 1) on the substrate at the same time, and drying at a temperature of 150° C. to obtain a substrate provided with a conductive graphene ink layer and a copper foil wire ;

[0042] 3) the base material provided with the conductive graphene ink layer and the copper foil wire obtained in step 2) is cooled to room temperature, then coated with insulating glue on the surface of the conductive graphene ink layer and dried to form an insulating glue layer, to obtain final product Graphene heating fabric.

[0043] Further, the use voltage of the graphene heating fabric is 5V-36V, so as to improve the safety performance of the graphene heatin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of electric heating materials, and particularly discloses a graphene heating fabric, which comprises a base material, a conductive graphene ink layer and acopper foil wire arranged on the base material, and an insulating glue layer coated on the surface of the conductive graphene ink layer. The invention further discloses a preparation method of the graphene heating fabric. According to the invention, the high-conductivity graphene slurry and the copper foil wire are arranged on the surface of the insulating film together based on the graphene electrifying heating technology, the insulating glue is coated for sealing after drying to obtain the graphene heating fabric; and the graphene heating fabric can be used for 5-36V direct-current voltageand has a good heating effect, can keep the flexibility and toughness of the heating film, can be compounded with wall cloth to replace indoor wall heating, can also be applied to special tents, carpets, mattresses, wooden heatable brick beds, clothes and other products to solve the heating problem of outdoor operators, and has wide market prospects.

Description

technical field [0001] The invention relates to the technical field of electric heating materials, in particular to a graphene heating fabric and a preparation method thereof. Background technique [0002] With the development of society and the advancement of science and technology, people's requirements for heating are also increasing. Among them, graphene, as a good conductor of electricity and heat, can be used in the heating film to play a conductive role, combined with other components such as resin to form a resistance part, and then the graphene electric heating film can generate heat after electrification. For heating or heating. [0003] At present, most of the existing graphene electric heating films are based on PVC films, that is, a graphene-coated heating wire is applied between two layers of PVC films and a conductive copper foil is applied. However, due to the insufficient flexibility of PVC film in any direction, and the disadvantages of flammability and p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H05B3/34H05B3/36D06N3/18D06N3/00
CPCH05B3/34H05B3/36D06N3/183D06N3/0077D06N3/0088D06N2209/041D06N2211/125D06N2211/066D06N2211/063
Inventor 陈建华
Owner 陈建华
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com