A casting system for complex thin-walled parts of superalloy

A gating system and high-temperature alloy technology, which is applied in the field of alloy investment casting, can solve the problems of thin-walled parts forming difficulty, casting process difficulty, and alloy mushy area, etc., achieve good results, save master alloy materials, and improve casting The effect of pass rate

Active Publication Date: 2022-07-26
SHENYANG LIMING AERO-ENGINE GROUP CORPORATION
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the characteristics of the alloy, such as large mushy area, high liquid viscosity, and serious loosening tendency, it is especially used in the production of thin-walled parts. During the casting process, thin-walled parts are difficult to form (under-cast), easy to loosen and crack, and the casting process is difficult. great

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A casting system for complex thin-walled parts of superalloy
  • A casting system for complex thin-walled parts of superalloy
  • A casting system for complex thin-walled parts of superalloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] like figure 2 As shown, a casting system for complex thin-walled parts of superalloy, the casting system is composed of a two-piece type:

[0032] The pouring system is provided with a basic pouring unit, a pouring cup 8 and an exhaust channel 9. The basic pouring unit consists of a sprue 1, a runner A2, a runner B5, a runner C6, a runner D7, It is composed of anti-deformation rod M4 and anti-deformation rod N10. The specific structure of the casting system is as follows:

[0033] The basic pouring unit structure is that two runners C6 are symmetrically arranged on the left and right sides of the bottom of the sprue 1, and two runners B5 and two runners A2 are arranged symmetrically on the front and rear sides of the sprue 1 in turn, and The runner A2 is located below the runner B5, a pair of runners D7 are symmetrically arranged at the outer ends of the front and rear sides of the runner C6, and the anti-deformation rod M4 is arranged between the two front pin holes ...

Embodiment 2

[0044] like image 3 As shown in the figure, a casting system for complex thin-walled parts of superalloy, the casting method of the casting system is a set of four parts:

[0045] The pouring system is provided with two basic pouring units, a pouring cup 8 and an exhaust channel 9. The basic pouring unit consists of a sprue 1, a runner A2, a runner B5, a runner C6, a runner D7. It is composed of anti-deformation rod M4 and anti-deformation rod N10. The specific structure of the pouring system is as follows:

[0046] The basic pouring unit structure is that two runners C6 are symmetrically arranged on the left and right sides of the bottom of the sprue 1, and two runners B5 and two runners A2 are arranged symmetrically on the front and rear sides of the sprue 1 in turn, and The runner A2 is located below the runner B5, a pair of runners D7 are symmetrically arranged at the outer ends of the front and rear sides of the runner C6, and the anti-deformation rod M4 is arranged bet...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of alloy investment casting, in particular to a casting system for complex thin-walled parts of high-temperature alloys. Two runners B and two runners A are set, and the runners A are located below the runners B, a pair of runners D are symmetrically arranged at the outer ends of the front and rear sides of the runners C, and the anti-deformation rods M are set Between the two front pin hole seats of the casting wax mold, the anti-deformation rod N is arranged in the rotating pin hole seat of the device in the casting wax mold. It is integrally formed with the casting wax mold; the sprue cup is directly connected with the sprue of the basic pouring unit, and two exhaust ducts are symmetrically arranged, both of which are connected to the sprue C and the sprue cup. The risk of defects such as porosity and cracks is improved, and the casting qualification rate of casting products is improved.

Description

technical field [0001] The invention relates to the field of alloy investment casting, in particular to a casting system for complex thin-walled parts of high-temperature alloys. Background technique [0002] JG4246A alloy has a series of advantages such as light specific gravity, high high temperature strength, excellent oxidation resistance and high temperature microstructure stability, which well meets the special needs of high temperature bearing capacity and ablation resistance of a certain type of thin-walled parts of the third and fourth generation machines. However, due to the characteristics of the alloy's large mushy area, high liquid viscosity, and serious loosening tendency, especially in the production of thin-walled parts, there are difficulties in forming thin-walled parts (under-casting), easy loosening and cracking during the casting process, and the casting process is difficult. great. The present invention involves many reinforcing ribs of the casting, an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B22C9/08B22C7/02B22C9/04B22C9/20B22C9/22
CPCB22C9/082B22C9/088B22C7/02B22C9/20B22C9/22B22C9/04
Inventor 孙长波王健楠吴晓娟尚伟周君华
Owner SHENYANG LIMING AERO-ENGINE GROUP CORPORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap