Low-temperature-resistant low-water-absorption modified nylon material and preparation method thereof

A technology of modified nylon and low water absorption, applied in the field of engineering plastic modification, can solve the problems of high water absorption, poor low temperature properties, low toughness of PA66 resin, and achieve the effects of low water absorption, good low temperature properties and excellent low temperature properties

Active Publication Date: 2021-04-02
SHANDONG NON METALLIC MATERIAL RES INST
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] PA66 is a widely used engineering plastic, which is a crystalline polymer. There are strong hydrogen bonds between the amide groups on the molecular chain, high crystallinity and melting point, and excellent mechanical properties, so

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0030]Example 1

[0031]The viscosity of 2.4 was selected from 66: 100 parts by weight; the viscosity was 2.7, 610:60 parts by weight; toughening agent: 10 parts by weight; antioxidant 1098 and an antioxidant 168 compound (1: 1): 0.5 weight Part.

[0032]The above components are respectively weighed according to the weight, and mixed 5 min in the high mixing machine, put the mixed raw material into the main feed opening of the screw machine, extruded granulation, the rotation speed of the screw machine is 300R / min, the processing temperature 230 ~ 290 ° C, resulting in the low temperature low water absorption modified nylon material according to the present embodiment, the normal temperature gap impact strength measured according to national standards 7.5kJ / m-2, Low temperature gap impact strength 8.2kJ / m-2, Water absorption is 0.4%.

Example Embodiment

[0033]Example 2

[0034]A nylon 66: 100 parts by weight of the viscosity is 2.2; the viscosity is 3.2 weight; toughen: 8 parts by weight; antioxidant 1098 and antioxidant 168 compound (1: 1): 1 weight Part.

[0035]The above components are respectively weighed according to the weight, and mixed 5 min in the high mixing machine, put the mixed raw material into the main feed opening of the screw machine, extruded granulation, the rotation speed of the screw machine is 300R / min, the processing temperature 230 ~ 290 ° C, resulting in the low temperature low water absorption modified nylon material according to the present embodiment, and the normal temperature gap impact strength is 7.2kJ / m according to the national standard-2, Low temperature gap impact strength 7.8kJ / m-2, Water absorption is 0.45%.

Example Embodiment

[0036]Example 3

[0037]The viscosity of 3.2 was selected from 66: 100 parts by weight; the viscosity was 3.5 weights 610:65 parts by weight; toughening agent: 14 parts by weight; antioxidant 1098 and antioxidant 168 compound (1: 1): 1 weight Part.

[0038]The above components are respectively weighed according to the weight, and mixed 5 min in the high mixing machine, put the mixed raw material into the main feed opening of the screw machine, extruded granulation, the rotation speed of the screw machine is 300R / min, the processing temperature From 230 ~ 290 ° C, it is obtained from the low temperature low water absorption modified nylon material, which is measured according to the national standard 8.1kj / m.-2, Low temperature gap impact strength 9.0kJ / m-2, Water absorption is 0.3%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a low-temperature-resistant low-water-absorption modified nylon material and a preparation method thereof. The modified nylon material comprises the following raw materials inparts by weight: 100 parts of nylon 66, 60-80 parts of nylon 610, 6-14 parts of a toughening agent and 0.5-1 part of an antioxidant. The water absorption rate of the modified nylon material is as lowas 0.3%, and the water absorption rate is relatively low; and meanwhile, the low-temperature performance of the modified nylon material is superior to that of normal-temperature performance, and the low-temperature characteristic is good.

Description

technical field [0001] The invention relates to the technical field of modification of engineering plastics, in particular to a modified nylon material with low temperature resistance and low water absorption and a preparation method thereof. Background technique [0002] PA66 is a widely used engineering plastic, which is a crystalline polymer. There are strong hydrogen bonds between the amide groups on the molecular chain, high crystallinity and melting point, and excellent mechanical properties, so its mechanical properties are excellent. , such as high strength, high modulus, high hardness, etc.; but pure PA66 resin has low toughness, high water absorption, and poor low temperature characteristics, so it needs to be improved urgently. Contents of the invention [0003] The technical problem to be solved by the present invention is to overcome the technical defects of the background technology, and provide a low-temperature-resistant low-water-absorbing modified nylon m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L77/06C08L23/06C08L23/12C08L73/00C08K5/20C08K5/526
CPCC08L77/06C08L2205/035C08L2205/025C08L23/06C08L23/12C08L73/00C08K5/20C08K5/526
Inventor 王旭华张友强姚立凯王宝生王强王存铎佘进娟王鑫淼诸葛炯
Owner SHANDONG NON METALLIC MATERIAL RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap