A kind of water-based glass colored jade sand material and preparation method thereof

A technology of glass and color, applied in the field of glass colored jade sand material and its preparation, water-based glass colored jade sand material and its preparation, to achieve the effect of coating energy saving, material environmental protection, and good adhesion

Active Publication Date: 2022-03-15
SUZHOU DEODAR SPECIAL BUILDING MATERIALS
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Similarly, the comprehensive properties of the composite coating of the invention, such as scratch resistance, pollution resistance, cleaning agent resistance, water washing resistance, and outdoor weather aging resistance, need to be improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of water-based glass colored jade sand material and preparation method thereof
  • A kind of water-based glass colored jade sand material and preparation method thereof
  • A kind of water-based glass colored jade sand material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0074] The water-based glass colored jade sand material of this embodiment includes component A and component B, and the mass ratio of component A to component B is 1:6.

[0075] Among them, in terms of mass percentage, component A is composed of 80% of XP2487 hydrophilic aliphatic isocyanate, 15% of N3900 low-viscosity aliphatic isocyanate, and 5% of GF40 isocyanate silane coupling agent.

[0076] Among them, in terms of mass percentage, component B consists of 20% of A2695 hydroxyl acrylic dispersion, 10% of U2766 hydroxyl polyurethane dispersion, 10% of EPICLON H502 epoxy resin dispersion, 32.1% of deionized water, 18% of silicon micropowder, silicon dioxide Microsphere 4%, bentonite 0.5%, FX365 polyether copolymer dispersant 0.1%, TEGO845 polysiloxane defoamer 0.6%, W469 silicone wetting agent 0.5%, HX6008 polyurethane rheological agent 1.2%, BYK381 acrylic copolymer It consists of 0.1% logistics agent, 1.5% Z6040 epoxy silane coupling agent, 0.1% TINUVINS292 light stabili...

Embodiment 2

[0088] The water-based glass colored jade sand material of this embodiment includes component A and component B, and the mass ratio of component A to component B is 1:6.

[0089] Among them, in terms of mass percentage, component A is composed of 75% of XP2487 hydrophilic aliphatic isocyanate, 17% of N3900 low-viscosity aliphatic isocyanate, and 8% of GF40 isocyanate silane coupling agent.

[0090] Among them, in terms of mass percentage, component B consists of 27% of A2695 hydroxyl acrylic dispersion, 11% of U2766 hydroxyl polyurethane dispersion, 8% of EPICLON H502 epoxy resin dispersion, 24% of deionized water, 16% of silicon micropowder, silicon dioxide Microspheres 8%, bentonite 0.2%, FX365 polyether copolymer dispersant 0.5%, TEGO845 polysiloxane defoamer 0.8%, W469 silicone wetting agent 0.3%, HX6008 polyurethane rheology agent 1.5%, BYK381 acrylic copolymer It consists of 0.3% logistics agent, 1.3% Z6040 epoxy silane coupling agent, 0.3% TINUVINS292 light stabilizer, ...

Embodiment 3

[0102] The water-based glass colored jade sand material of this embodiment includes component A and component B, and the mass ratio of component A to component B is 1:6.

[0103] Among them, in terms of mass percentage, component A is composed of 85% of XP2487 hydrophilic aliphatic isocyanate, 10% of N3900 low-viscosity aliphatic isocyanate, and 5% of GF40 isocyanate silane coupling agent.

[0104]Among them, in terms of mass percentage, component B consists of 40% of A2695 hydroxyl acrylic dispersion, 10% of U2766 hydroxyl polyurethane dispersion, 5% of EPICLON H502 epoxy resin dispersion, 28.6% of deionized water, 10% of silicon micropowder, silicon dioxide Microsphere 2%, bentonite 0.3%, FX365 polyether copolymer dispersant 0.3%, TEGO845 polysiloxane defoamer 0.6%, W469 silicone wetting agent 0.1%, HX6008 polyurethane rheological agent 1%, BYK381 acrylic copolymer It consists of 0.2% logistics agent, 1% Z6040 epoxy silane coupling agent, 0.2% TINUVINS292 light stabilizer, 0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a water-based glass colored jade sand material and a preparation method thereof. The water-based glass colored jade sand material of the present invention comprises A component and B component, and by mass percentage, A component comprises the following components: hydrophilic aliphatic isocyanate is 70-85%, low-viscosity aliphatic isocyanate is 10% ‑20%, isocyanate-based silane coupling agent 5‑10%; component B contains the following components: hydroxyl resin dispersion 30‑50%, epoxy resin dispersion 5‑10%, silicon micropowder 10‑18%, two Silica microspheres 2‑8%, bentonite 0.1‑0.5%, additives 1‑10%, color paste, water balance; wherein, the mass ratio of A component to B component is (1‑3):6. The water-based colored jade sand glass material of the present invention has excellent comprehensive properties, excellent adhesion to the glass surface, excellent scratch resistance of the jade sand coating, anti-pollution and easy cleaning, resistance to cleaning by cleaning agents, water washing resistance, and outdoor weather aging resistance .

Description

technical field [0001] The invention relates to the technical field of functional glass, and relates to a glass colored jade sand material and a preparation method thereof, in particular to a water-based glass colored jade sand material and a preparation method thereof. Background technique [0002] At present, the surface treatment of glass light-transmitting and opaque mainly includes glass frosting, glass jade sand (frosting), and glass film. Frosted glass is gradually eliminated by the market because the surface is too rough and the stains are not easy to clean. Jade sand glass has a delicate surface, excellent comprehensive performance, and high production costs. Since the production process requires pickling and etching, the process does not meet environmental protection standards, and it is also facing pressure to withdraw from the market. Glass film is prone to warping and obvious seams, which is the last choice of users. [0003] The jade sand glass made of glass ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C17/00
Inventor 党文生查春梅杨永顾
Owner SUZHOU DEODAR SPECIAL BUILDING MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com