Liquid crystal composition containing polymerizable compound and liquid crystal display element

A technology of polymeric compounds and liquid crystal compositions, applied in liquid crystal materials, chemical instruments and methods, nonlinear optics, etc., can solve problems such as burn-in screen display failure, orientation deterioration, and insufficient tilt formation, and achieve degradation suppression and voltage retention ratio (VHR) reduction, shortened UV irradiation time, and excellent display quality effects

Pending Publication Date: 2021-06-25
DIC CORP
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, by increasing the area of ​​the wiring and the light-shielding part, a considerable part of the UV light will be filtered out. In the same UV irradiation process as in the past, the formation of the inclination will become insufficient, the polymerizable compound will not be sufficiently polymerized, and a large amount of

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Liquid crystal composition containing polymerizable compound and liquid crystal display element
  • Liquid crystal composition containing polymerizable compound and liquid crystal display element
  • Liquid crystal composition containing polymerizable compound and liquid crystal display element

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0651] The following examples are given to further describe the present invention in detail, but the present invention is not limited by these examples.

[0652] The following abbreviations are used for descriptions of compounds in the following Examples and Comparative Examples.

[0653] (side chain)

[0654] -n-C n h 2n+1 straight-chain alkyl group with n carbon atoms

[0655] n-C n h 2n+1 - straight-chain alkyl group with n carbon atoms

[0656] -On-OC n h 2n+1 straight-chain alkoxy group with n carbon atoms

[0657] V-CH 2 =CH-

[0658] 1V-CH 3 -CH=CH-

[0659] -V-CH=CH 2

[0660] -V1-CH=CH-CH 3

[0661] (Linker)

[0662] -1O--CH 2 -O-

[0663] -2--CH 2 -CH 2 -

[0664] (ring structure)

[0665] [chem 89]

[0666]

[0667] The characteristics measured in the following examples and comparative examples are as follows.

[0668] T ni : Nematic-isotropic liquid phase transition temperature (°C)

[0669] Δn: Refractive index anisotropy at 20°C

[...

Embodiment 5～6

[0711] In 99 parts by mass of liquid crystal composition LC-001, add 1 part by mass of a compound represented by formula (i-1-1-4A) as a compound of formula (i) and 0.3 parts by mass of a compound of formula (RM- The polymerizable compound A represented by A1, and the obtained polymerizable compound-containing liquid crystal composition were used as Example 5.

[0712] In 99 parts by mass of liquid crystal composition LC-001, add 1 part by mass of a compound represented by formula (i-1-1-37A) as a compound of formula (i) and 0.3 parts by mass of a compound of formula (RM- The polymerizable compound A represented by A1, and the obtained polymerizable compound-containing liquid crystal composition were used as Example 6.

[0713] [chem 91]

[0714]

[0715] Regarding the polymerizable compound-containing liquid crystal compositions of Examples 5 to 6, the UV irradiation time T when the remaining amount of the polymerizable compound is less than the lower limit of detection ...

Embodiment 7～12

[0720] In 99 parts by mass of liquid crystal composition LC-002, add 1 part by mass of a compound represented by formula (i-1-1-4A) as a compound of formula (i) and 0.3 parts by mass of a compound of formula (RM- The polymerizable compound A represented by A1, and the obtained polymerizable compound-containing liquid crystal composition were used as Example 7.

[0721] In 99 parts by mass of liquid crystal composition LC-002, add 1 part by mass of a compound represented by formula (i-1-1-37A) as a compound of formula (i) and 0.3 parts by mass of a compound of formula (RM- The polymerizable compound A represented by A1, and the obtained polymerizable compound-containing liquid crystal composition were used as Example 8.

[0722] In 99 parts by mass of liquid crystal composition LC-002, add 1 part by mass of a compound represented by formula (i-1-1-4B) as a compound of formula (i) and 0.3 parts by mass of a compound of formula (RM- The polymerizable compound A represented by A1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a liquid crystal composition containing a polymerizable compound and a liquid crystal display element. The present invention addresses the problem of providing: a polymerizable liquid crystal composition which can be rapidly and sufficiently polymerized, can form a tilt with weak or little UV light, has excellent reliability after a UV irradiation step, and is useful when used in the production of a liquid crystal display element; and a liquid crystal display element using the polymerizable liquid crystal composition. [Solution] The present invention provides a liquid crystal composition containing a polymerizable compound, the composition containing one or more compounds represented by general formula (i) and one or more polymerizable compounds, the total content of the compounds represented by general formula (i) being within a predetermined range.

Description

technical field [0001] The present invention relates to a liquid crystal composition containing a polymerizable compound and a liquid crystal display device using the same. In addition, in this specification, the liquid crystal composition containing a polymeric compound is called the liquid crystal composition containing a polymeric compound. In addition, a polymeric compound means a compound which has a polymeric group. Background technique [0002] For example, the PSA (Polymer Sustained Alignment, polymer stable alignment) mode liquid crystal display element has a structure in which a polymer structure is formed in the cell in order to control the pretilt angle of the liquid crystal molecules, and has been used as a liquid crystal display due to high-speed response and high contrast. components are practical. [0003] The manufacture of a PSA mode liquid crystal display element is carried out by injecting a liquid crystal composition containing a polymerizable compound...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09K19/54G02F1/1333
CPCC09K19/542G02F1/1333
Inventor 后藤麻里奈井之上雄一野吕大树
Owner DIC CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap