A kind of defoamer of paint and ink emulsion and preparation method thereof

A technology of defoaming agent and ink, which is applied in the direction of ink, coating, household utensils, etc., can solve the problems of long defoaming time of defoaming agent, poor product stability, short foam suppression time, etc., and achieve long foam suppression time, defoaming Short foaming time, improved defoaming and anti-foaming performance

Active Publication Date: 2022-05-03
SOUTH CHINA UNIV OF TECH +1
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing silicone defoamer formula is complicated, and the defoaming time of the developed defoamer is long, and the foam suppression time is too short (the defoaming time in the prior art is generally more than 15 s, and the foam suppression time is less than 13 minutes )
[0004] CN102120108A introduces a mineral oil defoamer with polyether and white carbon black as the main defoaming substances, but white carbon black is directly added, and there is a defect of poor product stability
CN101310814A has introduced a kind of mineral oil defoamer, has added silicone grease to improve defoaming and suppressing performance, but can produce coating shrinkage cavity, edge shrinkage problem in water-based system

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] This embodiment provides a defoamer for paint and ink emulsion and its preparation method.

[0042] 1) Preparation of long-chain alkyl and polyether composite modified silicone oil;

[0043] Take 50g of hydrogen-containing silicone oil with a hydrogen content of 0.08%, add 24g of allyl polyether (EO / PO block polyether, the molar ratio of EO / PO is 1:3, end-blocked with methyl, molecular weight 300); Add 3.36g of dodecene; make Si-H in hydrogen-containing silicone oil and CH in allyl polyether and long-chain olefin 2 = The ratio of the sum of moles of CH is 1:2.5. Add 203 μL of platinum metal (the mass of platinum metal accounts for 10×10 of the total mass of hydrogen-containing silicone oil, allyl polyether, and long-chain olefin. -6 wt%), reacted at 100°C for 6 hours, took samples to detect the conversion rate of the reaction, when the conversion rate reached more than 98%, stopped the reaction, lowered to room temperature and discharged, and prepared long-chain alkan...

Embodiment 2

[0049] This embodiment provides a defoamer for paint and ink emulsion and its preparation method.

[0050] 1) Preparation of long-chain alkanes and polyether composite modified silicone oil:

[0051] Take 50g of hydrogen-containing silicone oil with a hydrogen content of 0.18%, add 65.52g of allyl polyether (EO / PO block polyether, the molar ratio of EO / PO is 1:3, end-capped with ester group, molecular weight 500) ; Add 7.34g hexadecene; Make Si-H in hydrogen-containing silicone oil and CH in allyl polyether 2 = The molar ratio of CH is 1:1.82. Add 161 μL of platinum metal (the mass of platinum metal accounts for 5×10 of the total mass of hydrogen-containing silicone oil, allyl polyether, and long-chain olefin. -6wt%), reacted at 110°C for 4 hours, and took samples to detect the conversion rate of the reaction. When the conversion rate reached more than 98%, the reaction was stopped, and the material was lowered to room temperature to prepare long-chain alkane and polyether c...

Embodiment 3

[0057] This embodiment provides a defoamer for paint and ink emulsion and its preparation method.

[0058] 1) Preparation of long-chain alkanes and polyether composite modified silicone oil:

[0059] Take 50g of hydrogen-containing silicone oil with a hydrogen content of 0.75%, add 189g of allyl polyether (EO / PO random polyether, the molar ratio of EO / PO is 1:0, no end capping, molecular weight 600); add 19.84 g Octadecene; make Si-H in hydrogen-containing silicone oil and CH in allyl polyether 2 = The molar ratio of CH is 1:1.05. Add 70.60 μL of platinum metal (the mass of platinum metal accounts for 1×10 of the sum of the mass of hydrogen-containing silicone oil, allyl polyether, and long-chain olefin. -6 wt%), reacted at 140°C for 2 hours, took a sample to detect the conversion rate of the reaction, when the conversion rate reached more than 98%, stopped the reaction, lowered to room temperature and discharged, and prepared long-chain alkane and polyether composite modifi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of fine chemical additives, and in particular relates to a defoamer for water-based paint and ink emulsion and a preparation method thereof. In this method, hydrogen-containing silicone oil, EO / PO block or random allyl polyether, and long-chain alkyl olefins are subjected to hydrosilylation reaction to prepare long-chain alkane and polyether composite modified silicone oil; Finally, modified fumed silica is added to obtain a silicone paste. Finally, mix Span 80, Tween 80, sodium hydroxymethyl cellulose, thickener and silicone paste; add water, emulsify and disperse at a high speed, and prepare a defoamer. The method does not need to add organic solvents, and the preparation method is simple. By adjusting the molar ratio and molecular weight of polyether EO / PO, the defoaming time required for the obtained defoamer is short, the foam suppression time is long, and there is no oil floating phenomenon. It has a good application prospect in the field of antifoaming agent of ink and printing ink.

Description

technical field [0001] The invention belongs to the technical field of fine chemical additives, and in particular relates to a defoamer for paint and ink emulsion and a preparation method thereof. Background technique [0002] Bubbles are a common phenomenon. Insoluble gases form bubbles, and foam occurs when many bubbles come together to form aggregates separated from each other by a thin film. Especially in the field of coatings and ink emulsions, dispersants, wetting agents, binders, thickeners, pigments and fillers are used in the production process. In the process of high-speed dispersion and blending, air enters the aqueous solution, which will generate a lot of foam. The existence of these foams will affect the construction of coatings or the use of inks, so defoamers must be added to coatings or ink products. [0003] Due to different foaming systems and production conditions, defoamers can be divided into mineral oils, pure silicone defoamers and emulsion defoame...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D7/65C09D7/62C09D11/00C08G77/46
CPCC09D7/65C09D7/61C09D11/00C08G77/46
Inventor 潘朝群肖燕平
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com