High-shape-preserving comfortable health-care fabric and preparation method thereof

A health-care fabric and comfortable technology, applied in the field of textile manufacturing, can solve problems such as poor environmental protection, insufficient elasticity of fabrics, and poor first-level health care functions, and achieve the ability to enhance elasticity and recover deformation, enhance elasticity, health care functions and environmental protection. Excellent effect

Inactive Publication Date: 2021-11-05
江苏派逊服饰有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a high shape-retaining comfortable health-care fabric and its preparation method, aiming to solve the problems in the prior art that the fabric has insufficient elasticity, poor environmental protection and poor first-level health care function

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-shape-preserving comfortable health-care fabric and preparation method thereof
  • High-shape-preserving comfortable health-care fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Put the PET-1 with an intrinsic viscosity of 0.8 dl / g and the PET-2 with an intrinsic viscosity of 0.4 dl / g into an oven for heating and drying, and put them into the spinning machine in a ratio of 1:1 to slice them, and heat them at 120°C Pre-crystallization for 1 hour, drying at 165°C for 12 hours, followed by melt spinning, melt spinning process parameters: high viscosity PET-1 spinning temperature is 1 zone: 280 ℃, 2 zone: 285 ℃, 3 zone: 290 ℃, four zones: 290℃; the spinning temperature of low viscosity PET-2 is zone one: 290℃, zone two: 295℃, zone three: 295℃, zone four: 290℃; the fluctuation of spinning temperature is ±0.5℃ , the drafting ratio is 3 times, and the winding speed is 600m / min.

[0032] use as figure 1 In the composite spinning assembly shown, there are two melt flow channels A and B in component 1, and a co-extrusion flow channel C. High viscosity PET-1 and low viscosity PET-2 pass through melt flow channel A and B respectively. B enters the co-ext...

Embodiment 2

[0042] Put PET-1 with an intrinsic viscosity of 1.0 dl / g and PET-2 with an intrinsic viscosity of 0.6 dl / g in an oven, heat and dry them, put them into spinning machines at a ratio of 1: 1, and put them into slices at 120°C Pre-crystallization for 1 hour, drying at 165°C for 12 hours, followed by melt spinning, melt spinning process parameters: High viscosity PET-1 spinning temperature is 1st zone: 280°C, 2nd zone: 286°C, 3rd zone: 290°C , zone four: 290°C; low-viscosity PET-2 spinning temperature is zone one: 285°C, zone two: 290°C, zone three: 290°C, zone four: 285°C; spinning temperature fluctuation is ±0.5°C, pulling The elongation ratio is 3 times, and the winding speed is 600m / min.

[0043] use as figure 1 In the composite spinning assembly shown, there are two melt flow channels A and B in component 1, and a co-extrusion flow channel C. High viscosity PET-1 and low viscosity PET-2 pass through melt flow channel A and B respectively. B enters the co-extrusion flow chan...

Embodiment 3

[0053] Put PET-1 with an intrinsic viscosity of 1.2 dl / g and PET-2 with an intrinsic viscosity of 0.8 dl / g in an oven, heat and dry them, put them into spinning machines at a ratio of 1: 1 and slice them, and heat them at 120°C Pre-crystallization for 1 hour, drying at 165°C for 12 hours, followed by melt spinning, the process parameters of melt spinning: high viscosity PET-1 spinning temperature is 1st zone: 280°C, 2nd zone: 285°C, 3rd zone: 285°C , zone four: 280°C; low-viscosity PET-2 spinning temperature is zone one: 287°C, zone two: 293°C, zone three: 293°C, zone four: 285°C; spinning temperature fluctuation is ±0.5°C, pulling The elongation ratio is 3 times, and the winding speed is 600m / min.

[0054] use as figure 1 In the composite spinning assembly shown, there are two melt flow channels A and B in component 1, and a co-extrusion flow channel C. High viscosity PET-1 and low viscosity PET-2 pass through melt flow channel A and B respectively. B enters the co-extrusio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
shrinkageaaaaaaaaaa
elastic recovery rateaaaaaaaaaa
shrinkageaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-shape-preserving comfortable health-care fabric and a preparation method thereof. In the preparation of the fabric, 60% of polyester parallel composite fibers, 30% of cotton fibers and 10% of aloe fibers are blended to serve as warp yarns, regenerated polyester fibers prepared by spinning and forming at least one of cloth, bottle flakes and foam materials serve as weft yarns, and the fabric is prepared through the procedures of warp weaving, weaving and the like. The polyester parallel composite fibers are prepared in a way that PET with different viscosities is subjected to melt extrusion by a screw rod, metering by a metering pump and composite molding by a spinneret plate according to a ratio of 1: 1, and finally is subjected to extension processing and heat treatment; the sections of the obtained polyester parallel composite fibers are splayed, so that the elasticity and resilience of the polyester parallel composite fibers are enhanced, and the high-shape-preserving comfortable health-care fabric has the advantages of high elasticity and shape preservation; and meanwhile, the added cotton fibers and aloe fibers enable the fabric to have the advantages of good moisture absorption, breathability, health-care function and environmental protection property.

Description

technical field [0001] The invention relates to a high-shape, comfortable and health-care fabric and a preparation method thereof, belonging to the technical field of textile manufacturing. Background technique [0002] With the continuous development of the economy and the continuous improvement of material living standards, people's concept of clothing has also changed, and the awareness of health care has continued to increase. Traditional classic high-end worsted fabrics no longer meet people's needs. Therefore, various textiles and The requirements for health care, comfort and warmth of clothing materials are also constantly improving. Health care performance and environmental protection performance are important functional indicators of textile fabrics, and shape retention is an important quality indicator of textile fabrics. It is well known that although natural fiber fabrics have the advantages of comfort, hygiene, environmental protection and certain health care pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D03D15/47D03D15/283D03D15/292D03D15/217D03D15/225D01D5/22D01D5/32D01D5/16D01D10/02D01F8/14
CPCD03D15/47D03D15/283D03D15/292D03D15/217D03D15/225D01D5/22D01D5/32D01D5/16D01D10/02D01F8/14D10B2331/04D10B2201/02D10B2201/22
Inventor 晋圣中丁毅
Owner 江苏派逊服饰有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap