Dyeing method of blended fabric

A technology of blended fabrics and dyeing methods, applied in dyeing methods, textiles and papermaking, etc., can solve the problems of high temperature instability of direct dyes, difficulty in color matching, poor level dyeing and dyeing depth, etc., to achieve reduction of dyes and level dyeing The use of additives, saving cost and dyeing time, improving the effect of coloring effect

Pending Publication Date: 2021-11-12
QINGDAO XUEDA GRP
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Polyester fiber, such as micro-denier polyester fiber, has high strength, wear resistance, excellent resilience and heat setting characteristics, can maintain the bending deformation formed when heated, and is light and thin, so it is a popular material in sportswear, but , its level dyeing and dyeing depth are poor, so it is easy to cause uneven dyeing in the dyeing process
The basic chemical composition of viscose fiber is the same as that of cotton fiber, so it is close to cotton fiber in some properties, for example, it has better softness; at the same time, viscose fiber has the smoothness of silk fiber, and its hygroscopicity and air permeability And the gloss is better than cotton fiber. Therefore, the dyeing performance of viscose fiber is better, it is easier to color than cotton fiber, and the color is pure and bright, and the color spectrum is the most complete; however, the biggest disadvantage of viscose fiber is that it is wet. Poor strength, the fabric is easy to wrinkle and difficult to restore
By blending micro-denier polyester fiber and viscose fiber, a soft, moisture-absorbing, breathable and strong blended fabric can be obtained. However, the properties of these two fibers are quite different. The traditional dyeing and finishing process needs to remove the blended fabric. Oil, polyester dyeing, cleaning, viscose dyeing, soaping and other processes can complete the dyeing, which consumes a lot of energy. With the increasing pressure of environmental protection, various production costs are also increasing
[0003] For the dyeing of micro-denier polyester and viscose fibers, the traditional method is to use the "two-bath method", first dyeing micro-denier polyester fibers, and then dyeing viscose fibers after draining, which consumes a lot of energy; Bath two-step method", select salt-resistant disperse dyes and high-temperature-resistant direct dyes for dyeing, but because of the need to use multiple dyes, add in several times, resulting in long process time, complicated operation, direct dyes are unstable at high temperatures, viscose At the same time, in order to solve the dyeing defects of direct reactive dyes under high temperature conditions, multiple dyes are generally used. However, the disadvantage of using multiple dyes is that it is difficult to match colors and poor reproducibility
Therefore, there is currently no method to realize the one-step dyeing of micro-denier polyester and viscose fibers in the same bath.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dyeing method of blended fabric
  • Dyeing method of blended fabric
  • Dyeing method of blended fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] The micro-denier polyester / viscose fiber (65 / 35) blended fabric was dyed by traditional dyeing process (two-bath method).

[0030] The components and dosage of dyeing materials are as follows:

[0031] Disperse dye black SW-VIP 3%, leveling agent 0.5g / L, glacial acetic acid 1g / L, hydrosulfite 3g / L, caustic soda 3g / L, reactive dye black WNN 5%, sodium sulfate 80g / L, sodium carbonate 20g / L, degreasing agent 1g / L, soaping agent 1g / L, color fixing agent 3g / L;

[0032] Wherein, disperse dye black SW-VIP is purchased from: Shanghai Yayun Chemical Co., Ltd., reactive dye black WNN is purchased from: Taixing Jinji Chemical Dyestuff Co., Ltd., leveling agent DL-200: Qingdao Guowei Textile Chemical Co., Ltd.; 85%): Yantai Jinhe Sodium Powder Factory Co., Ltd.; degreasing agent MRZ: Shanghai Argo Chemical Co., Ltd.; soaping agent SN: Shanghai Langsi Chemical Co., Ltd.; color fixing agent KY-R: Zhejiang Transfar Co., Ltd. .

[0033] The dyeing process is as follows:

[0034] (1...

Embodiment 2

[0047] The dyeing process of the invention is used to dye the micro-denier polyester / viscose fiber (65 / 35) blended fabric.

[0048] The components and dosage of dyeing materials are as follows:

[0049] New dye black CP-N 8%, Yuanming powder 100g / L, degreasing agent 1g / L, cleaning agent 1.5g / L, color fixing agent 3g / L.

[0050] Among them, the new dye black CP-N was purchased from: Shanghai Yayun Chemical Co., Ltd., the cleaning agent was purchased from: Qingdao Guowei Textile Chemical Co., Ltd., the degreasing agent MRZ was purchased from: Shanghai Argo Chemical Co., Ltd., the color fixing agent KY- R was purchased from: Zhejiang Transfar Co., Ltd.

[0051] The dyeing process is as follows:

[0052](1) One-bath dyeing of micro-denier polyester and viscose fiber

[0053] Add the micro-denier polyester / viscose fiber blended fabric and 35°C±2 water into the dyeing vat, control the bath ratio to 1:4.5, add degreasing agent to the dyeing vat in turn (take 10 minutes to add), ne...

Embodiment 3

[0061] Adopt dyeing process of the present invention to dye 50S single jersey (65%T / 35%R), the color code name of jersey is ZMHY-126 black, and fabric gram weight 150g / m 2 .

[0062] The components and dosage of dyeing materials are as follows:

[0063] New dye black CP-N 5%, Yuanming powder 100g / L, degreasing agent 1g / L, cleaning agent 1.5g / L, color fixing agent 3g / L.

[0064] Among them, the new dye black CP-N was purchased from: Shanghai Yayun Chemical Co., Ltd., the cleaning agent was purchased from: Qingdao Guowei Textile Chemical Co., Ltd., the degreasing agent MRZ was purchased from: Shanghai Argo Chemical Co., Ltd., the color fixing agent KY- R was purchased from: Zhejiang Transfar Co., Ltd.

[0065] The dyeing process is as follows:

[0066] (1) Dyeing

[0067] Add jersey and water at 35°C±2 to the dye vat, control the bath ratio to 1:4.5, add degreaser (completely added in 10 minutes), new dye black CP-N (completely added in 30 min) and yuan Staring powder (comp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a dyeing method of a blended fabric, and belongs to the technical field of fabric dyeing. Compared with a traditional dyeing process, the dyeing process only comprises the four processes of dyeing, cleaning, water washing and color fixing, one-bath dyeing of the blended fabric is achieved, a dyed fabric is free of defects such as color spots and dark spots, the degree of dyeing is high, the color fastness is good, the cost is saved, the dyeing time is shortened, and the production efficiency is greatly improved.

Description

technical field [0001] The invention belongs to the technical field of fabric dyeing, in particular to a method for dyeing blended fabrics. Background technique [0002] In the field of fabric dyeing and finishing, various fibers in blended fabrics have coloring problems due to large performance differences. Polyester fiber, such as micro-denier polyester fiber, has high strength, wear resistance, excellent resilience and heat setting characteristics, can maintain the bending deformation formed when heated, and is light and thin, so it is a popular material in sportswear, but , its level dyeing and dyeing depth are poor, so it is easy to cause uneven dyeing during the dyeing process. The basic chemical composition of viscose fiber is the same as that of cotton fiber, so it is close to cotton fiber in some properties, for example, it has better softness; at the same time, viscose fiber has the smoothness of silk fiber, and its hygroscopicity and air permeability And the glo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06P1/38D06P1/16D06P1/673D06P3/872D06P1/00
CPCD06P1/38D06P1/16D06P1/6735D06P3/8252D06P1/0032Y02P70/62
Inventor 张皓陈室全
Owner QINGDAO XUEDA GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap