Preparation method of waterproof adhesive

A waterproof adhesive and mixture technology, applied in the direction of adhesive additives, adhesive types, polymer adhesive additives, etc., can solve problems such as easy mildew, affecting adhesive bonding performance, breeding bacteria, etc., to achieve improved The effect of water resistance

Pending Publication Date: 2021-12-10
深圳市美之电实业有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the adhesives currently on the market are prone to mildew and bacteria breeding when exposed to water or in a humid environment. On the one hand, the adhesive performance of the adhesive is affected, and on the other hand, the hygiene and aesthetics are poor. Freezing affects the use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of waterproof adhesive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] In the embodiment of the present invention, a waterproof adhesive includes the following components in parts by weight: 70 parts of epoxy resin, 48 parts of epoxy resin curing agent, 9 parts of emulsifier, 5 parts of pH regulator, and 12 parts of anti-mold and antibacterial agent , Anti-aging agent 12 parts, antifreeze agent 11 parts, filler 11 parts, defoamer 9 parts, dispersant 10 parts.

[0019] Further, a preparation method of a waterproof adhesive, comprising the steps of:

[0020] S1: Put epoxy resin, anti-mold and antibacterial agent, anti-aging agent, antifreeze agent and plasticizer into the reaction kettle, heat up to 55 °C at a rate of 3 °C / min, add emulsifier and continue stirring for 30 min, and then Degassing under vacuum;

[0021] S2: adjusting the pH value of the vacuum-degassed epoxy resin to 7 with a pH value regulator to prepare an adhesive;

[0022] S3: Put the adhesive, dispersant, filler, epoxy resin curing agent, and defoamer into a mixer and mi...

Embodiment 2

[0029] A waterproof adhesive, comprising the following components by weight: 60 parts of epoxy resin, 40 parts of epoxy resin curing agent, 7 parts of emulsifier, 3 parts of pH regulator, 9 parts of anti-mold and antibacterial agent, 7 parts of anti-aging agent , 9 parts of antifreeze, 10 parts of plasticizer, 12 parts of defoamer, 12 parts of dispersant;

[0030] Further, a preparation method of a waterproof adhesive, comprising the steps of:

[0031] S1: Put epoxy resin, anti-mold and antibacterial agent, anti-aging agent, antifreeze agent and plasticizer into the reaction kettle, heat up to 60°C at a rate of 4°C / min, add emulsifier and continue stirring for 30min, and then Degassing under vacuum;

[0032] S2: adjusting the pH value of the vacuum-degassed epoxy resin to 7 with a pH value regulator to prepare an adhesive;

[0033] S3: Put the adhesive, dispersant, filler, epoxy resin curing agent, and defoamer into a mixer and mix to prepare a waterproof adhesive.

[0034]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of waterproof adhesives, in particular to a preparation method of a waterproof adhesive, which comprises the following components: epoxy resin, an epoxy resin curing agent, an emulsifier, a pH value regulator, an anti-mildew antibacterial agent, an anti-aging agent, an anti-freezing agent, a plasticizer, a defoaming agent and a dispersing agent. The nano-silver, nano-salt and graphene are adopted to achieve mildew-proof and antibacterial effects, the problem that mildew and bacterium breeding are prone to occurring in water or a humid environment after use is solved, use sanitation and bonding performance are effectively guaranteed, calcium lignosulphonate and ethylene glycol are matched to achieve an anti-freezing effect, the problem that use is affected by freezing in a low-temperature environment is avoided, the bentonite, the silica powder and the silica wax are matched to achieve a waterproof effect, and the overall waterproof performance is effectively improved.

Description

technical field [0001] The invention relates to the technical field of waterproof adhesives, in particular to a preparation method of waterproof adhesives. Background technique [0002] Adhesive is one of the most important auxiliary materials. It is a viscous substance that connects two separated materials with the help of its viscous ability. It is widely used in many fields such as home decoration, wood, and electronic appliances. [0003] However, the adhesives currently on the market are prone to mildew and bacteria breeding when exposed to water or in a humid environment. On the one hand, the adhesive performance of the adhesive is affected, and on the other hand, the hygiene and aesthetics are poor. Freezing affects use. Therefore, those skilled in the art provide a method for preparing a waterproof adhesive to solve the problems raised in the above-mentioned background technology. Contents of the invention [0004] The object of the present invention is to provid...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J163/00C09J11/04C09J11/06C09J11/08
CPCC09J163/00C09J11/04C09J11/06C09J11/08C08K2201/011C08K2003/0806C08L97/005C08L83/04C08K13/02C08K3/08C08K3/042C08K5/053C08K3/346C08K3/36
Inventor 廖沛锟
Owner 深圳市美之电实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com