UV antifogging coating for protective mask and preparation method of UV antifogging coating

A technology for protective masks and anti-fog coatings, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve the problems of mirror fogging, affecting user experience, blocking vision, etc., achieves rapid curing, excellent surface anti-fog performance, and reduces cost effect

Pending Publication Date: 2022-05-10
DONGLAI COATING TECH SHANGHAI
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when the protective mask is in use, the mirror surface is prone to fogging due to factors such as temperature differences, which seriously blocks the field of vision and affects the user experience.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • UV antifogging coating for protective mask and preparation method of UV antifogging coating
  • UV antifogging coating for protective mask and preparation method of UV antifogging coating
  • UV antifogging coating for protective mask and preparation method of UV antifogging coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A kind of UV anti-fog paint for protective mask, its component and mass parts are as follows:

[0032]

[0033] In this embodiment, the hydrophilic acrylate oligomer is selected from polyurethane acrylate oligomer, the hydrophilic reactive diluent is selected from ethoxylated trimethylolpropane triacrylate (15EO-TMPTA), and the reactive diluent The agent is dipentaerythritol hexaacrylate, the photoinitiator is initiator 2959, the solvent is ethyl acetate, and the leveling agent is BYK-333.

[0034] The protective mask is obtained by the following method with UV anti-fog coating:

[0035] Put the hydrophilic acrylate oligomer, hydrophilic reactive diluent, high-functional reactive diluent, solvent, and photoinitiator into the reactor in turn, stir at 400 rpm for 25 minutes, then reduce the speed to 150 rpm, and then add the leveling agent. Stir for 10 minutes, adjust the viscosity, let it stand for 12 minutes, and filter to obtain the UV anti-fog coating for protecti...

Embodiment 2

[0037] A kind of UV anti-fog paint for protective mask, its component and mass parts are as follows:

[0038]

[0039] In this embodiment, the hydrophilic acrylate oligomer is selected from polyurethane acrylate oligomer, the hydrophilic reactive diluent is selected from ethoxylated trimethylolpropane triacrylate (15EO-TMPTA), and the reactive diluent The agent is dipentaerythritol hexaacrylate, the photoinitiator is initiator 2959, the solvent is ethyl acetate, and the leveling agent is BYK-333.

Embodiment 3

[0041] A kind of UV anti-fog paint for protective mask, its component and mass parts are as follows:

[0042]

[0043] In this embodiment, the hydrophilic acrylate oligomer is selected from polyurethane acrylate oligomer, the hydrophilic reactive diluent is selected from ethoxylated trimethylolpropane triacrylate (15EO-TMPTA), and the reactive diluent The agent is dipentaerythritol hexaacrylate, the photoinitiator is initiator 2959, the solvent is ethyl acetate, and the leveling agent is BYK-333.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a UV anti-fog coating for a protective mask and a preparation method of the UV anti-fog coating. The anti-fog coating comprises the following components in parts by weight: 20-50 parts of hydrophilic acrylate oligomer; 15 to 45 parts of a hydrophilic reactive diluent; 1-10 parts of a high-functionality reactive diluent; 1-8 parts of a photoinitiator; 19.5 to 40 parts of a solvent; and 0.1-0.5 part of a leveling agent. The preparation method comprises the following steps: mixing the hydrophilic acrylate oligomer, the hydrophilic active diluent, the high-functional-group active diluent, the solvent and the photoinitiator, and then adding the flatting agent to obtain the UV anti-fog coating for the protective mask. Compared with the prior art, the prepared UV-cured super-hydrophilic anti-fog coating can be rapidly cured, the coating stability is good, the content of hydrotropic substances of the raw materials is high, the hydrophilic performance is excellent, the water resistance and the wear resistance are excellent due to the high-functional-group reactive diluent, the industrially-produced UV diluent with polyhydroxy groups is adopted to replace hydrophilic acrylate oligomer, and the cost is low.

Description

technical field [0001] The invention relates to the technical field of anti-fog coatings, in particular to a UV anti-fog coating for protective masks and a preparation method thereof. Background technique [0002] Fog is a common natural phenomenon in the meteorological environment. When the water vapor in the air reaches or approaches the dew point temperature, it will condense into tiny liquid droplets to form fog. As a result of the atomization of water droplets on the surface of transparent materials, not only the decrease of light transmittance will affect the vision, but sometimes even cause harm. [0003] In order to prevent fogging on the surface of transparent materials, various measures have been taken to eliminate the condensation of fog droplets. A more ideal choice is to coat a layer of UV anti-fog coating on the surface of the transparent material to prevent the condensation of foggy water droplets, thereby maintaining the optical transparency of the transpar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/14C09D7/20
CPCC09D175/14C09D7/20
Inventor 朱忠敏汤新春
Owner DONGLAI COATING TECH SHANGHAI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap