Treatment method of reducing hydrogen loss of optical fiber and devices in use for the method

A processing method and processing equipment technology, applied in the field of reducing the hydrogen loss of optical fiber and the equipment used in the institute, can solve the problems of excess, additional loss increase, and reduction of winding tension, etc., and achieve low manufacturing cost, less land occupation, and safety high performance effect

Active Publication Date: 2006-04-19
FENGHUO COMM SCI & TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] This causes an increase in the additional loss after the hydrogen loss
Although the defects in the optical fiber can be reduced by optimizing the drawing process, such as lowering the drawing temperature, lowering the drawing tension, etc., the additional attenuation after hydrogen loss still exceeds the level allowed by the low water peak optical fiber standard

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Treatment method of reducing hydrogen loss of optical fiber and devices in use for the method
  • Treatment method of reducing hydrogen loss of optical fiber and devices in use for the method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0035] Put the drawn optical fiber into the figure 1 In the shown optical fiber deuterium processing chamber 8, the pure inert gas purging equipment is passed through the inert gas inlet 3 for 15 minutes, and then the temperature in the optical fiber deuterium processing chamber is heated to 25 to 50°C, and the optimum temperature is 40°C. Subsequently, the processing chamber is evacuated, and a mixed gas of deuterium and nitrogen is introduced into the deuterium processing chamber from the deuterium inlet 1, wherein the concentration of deuterium is 0.5% to 3%, and the optimal deuterium concentration is 2%. Optical fiber deuterium processing The pressure of the mixed gas in the chamber is 1.01×10 5 Pa to 2.02×10 5 Pa, the optimum pressure is 1.15×10 5 Pa, maintain this state for 10 to 30 hours, and the optimal time is 20 hours, then feed the inert gas by the inert gas inlet 3 and cool the temperature in the deuterium treatment chamber to room temperature, then the gas in th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
additional attenuationaaaaaaaaaa
Login to View More

Abstract

The main characteristic of method and device in this invention is to do deuterate process for fibre-optical formed by drawing in normal temp to reduce and remove the fault in fibre-optical thus to reduce fibre-optical hydrogen loss. The fibre-optical processed by this invention has additional less than or equal to 0.01 dB / km when hydrogen loss is 1383 nm.

Description

technical field [0001] The invention relates to a treatment method for reducing hydrogen loss of optical fibers and equipment used in the method, in particular to a deuterium treatment process for optical fibers and deuterium treatment equipment used in the process. Background technique [0002] At present, optical fiber communication technology continues to develop in the direction of high speed and large capacity. The specific technological development approaches mainly include increasing the transmission rate of a single channel and increasing the number of channels of wavelength division multiplexing (WDM). In order to increase the number of channels multiplexed by WDM, there are two ways, one is to reduce the channel spacing; the other is to expand the available frequency band of the optical fiber. Optical fiber manufacturing technology has been working hard to expand the usable frequency band of optical fiber. [0003] Since Corning Corporation of the United States m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C25/00C03C25/66
Inventor 雷道玉陆大方李诗愈王冬香李海清陈伟成煜严勇虎
Owner FENGHUO COMM SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com