Composite flame retardant insulation water-proof seal adhesive tape and its preparing method

A waterproof sealing, composite flame-retardant technology, applied in the direction of adhesives, film/sheet adhesives, etc., to achieve strong conformability, convenient coating, and good strength

Inactive Publication Date: 2007-02-14
CHINA KINWA HIGH TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the technical problem of requiring both insulation and flame-retardant waterproof sealing, the present invention provides a composite flame-retardant insulating waterproof sealing tape and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite flame retardant insulation water-proof seal adhesive tape and its preparing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] The composition raw materials of the outer flame-retardant insulating elastic material A are weighed according to the following proportions (parts by weight): 30 parts of EPDM4045, 40 parts of CPE, 10 parts of fly ash, 8 parts of viscous engine oil, and 10 parts of decabromodiphenyl ether , 10 parts of pentabromotoluene, 6 parts of antimony oxide, 3 parts of carbon black, 3 parts of paraffin, 1 part of stearic acid, 0.5 part of antioxidant RD, 0.5 part of antioxidant 1010, 1 part of accelerator TMTD; In the open mill, knead repeatedly at 140 ° C until it is completely melted and mixed; then put it on a three-roll calender at 130 ° C, the distance between the rolls is 0.1 cm; pull it at a speed of 1 m / min and cut it into a width of 5 cm. layer strip.

[0013] The composition raw materials of inner flame-retardant sealing waterproof self-adhesive material B are weighed according to the following ratio (parts by weight): 20 parts of polyisobutylene, 18 parts of terpene res...

Embodiment 2

[0016] The raw materials of the outer layer flame-retardant insulating elastic material A are weighed according to the following proportions (parts by weight): 50 parts of EPDM4045, 60 parts of CPE, 20 parts of fly ash, 15 parts of sticky machine oil, 15 parts of decabromodiphenyl ether, 15 parts of pentabromotoluene, 10 parts of antimony oxide, 8 parts of carbon black, 8 parts of paraffin, 3 parts of stearic acid, 2 parts of antioxidant RD, 1.5 parts of antioxidant 1010, 3 parts of accelerator TMTD; In the open mill, knead repeatedly at 160°C until it is completely melted and mixed; then put it on a three-roll calender at 130°C, with a roller spacing of 0.3cm; pull it at a speed of 1m / min and cut it into an outer layer with a width of 5cm Strip.

[0017] The composition raw material of internal flame-retardant sealing waterproof self-adhesive material B is weighed according to the following proportioning (parts by weight): 30 parts of polyisobutylene, 22 parts of terpene resi...

Embodiment 3

[0020] The composition raw materials of the outer flame-retardant insulating elastic material A are weighed according to the following proportions (parts by weight): 40 parts of EPDM4045, 50 parts of CPE, 15 parts of fly ash, 12 parts of sticky machine oil, and 13 parts of decabromodiphenyl ether , 13 parts of pentabromotoluene, 8 parts of antimony oxide, 6 parts of carbon black, 6 parts of paraffin, 1.5 parts of stearic acid, 1 part of antioxidant RD, 1 part of antioxidant 1010, and 1 part of accelerator TMTD; In the open mill, knead repeatedly at 150 ° C until it is completely melted and mixed; then put it on a three-roll calender at 130 ° C, the distance between the rolls is 0.2 cm; pull at a speed of 1 m / min and pay attention to cutting into a width of 5 cm. layer strip.

[0021] The composition raw materials of inner layer flame-retardant sealing waterproof self-adhesive material B are weighed according to the following proportioning (parts by weight): 25 parts of polyiso...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
oxygen indexaaaaaaaaaa
Login to View More

Abstract

The composite flame retardant insulating waterproof sealing adhesive tape includes outer layer A and inner layer B rolled and compounded together. The outer layer A consists of elastic flame retardant insulating glue EPDM4045, CPE, stabilizer, reinforcing agent, flame retardant, antiageing agent, antioxidant and promoter; and the inner layer B consists of adhesive insulating waterproof polyisobutylene, butyl rubber, adhesive terpene resin, carbon black, light calcium carbonate and stearic acid. The outer layer materials are mixed in an open stirrer and the mixture is rolled and cut to form tape; the inner layer materials are mixed, cut into strip and extruded into sheet; and the tape and the sheet are rolled and compounded to form the composite flame retardant insulating waterproof sealing adhesive tape. The adhesive tape may be used for flame retardant insulating waterproof sealing of electric joint for no-fire condition.

Description

technical field [0001] The invention belongs to the technical field of insulating sealing tape and its preparation, and in particular relates to a composite flame-retardant insulating and waterproof sealing tape and a preparation method thereof. Background technique [0002] At present, strips made of heat-shrinkable materials are mostly used for insulation treatment of various types of wire and cable joints. Based on the characteristics of heat-shrinkable materials, it is necessary to use open flame heating when applying strips made of heat-shrinkable materials. However, in some special occasions, open flame operations are not allowed: such as coal mines, oil fields, chemical industry and other places where fire is absolutely prohibited; the materials used in these places require both insulation and must be flame-retardant and waterproof. The insulating sealing tape made of heat-shrinkable material does not have the function of meeting the above-mentioned requirements at t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J7/02C09J9/00
Inventor 莫志深于黎宋春雷张宏放那天海曾宝华
Owner CHINA KINWA HIGH TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com