Power sealing waterproof insulating rubber clay and preparation method thereof

A technology of waterproof insulation and rubber clay, applied in chemical instruments and methods, other chemical processes, etc., can solve the problems of shortened service life of power lines, influence on line safety, high contact resistance, etc., achieve low water absorption, avoid oxidation leakage, good compatibility

Active Publication Date: 2017-10-20
JINZHOU ELECTRIC POWER SUPPLY COMPANY OF STATE GRID LIAONING ELECTRIC POWER SUPPLY +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Underground power line joints often appear in accident repairs such as power company construction or cable digging. Nowadays, power lines generally have insulation skins. After power line joints appear, the joints are exposed or wrapped with tape, which is very easy to Oxidation, leakage occurs, affecting line safety, or causing excessive contact resistance, resulting in shortened service life of power lines

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Raw materials are taken by weighing: natural rubber 100g; liquid polyisobutylene 30g; α-pinene resin 10g; zinc oxide 6g; sulfur 3.5g; stearic acid 3.5g; 0.6g accelerator DM; 1.3g accelerator TMTD; channel carbon black 60g; 0.8g rubber anti-aging agent RD; rosin 10.5g; mix the natural rubber particles and channel black evenly, then add zinc oxide, sulfur, stearic acid, accelerator DM and accelerator TMTD and stir evenly, and finally add Stir liquid polyisobutylene, rubber antioxidant RD, rosin and α-pinene resin evenly, then heat to 100°C for 40 minutes, cool to room temperature, and seal the package.

[0033] Construction method: Fill the rubber mud in the joint of the power line and cover it on the connection surface, roll the rubber mud by hand to make it fully bonded to the power line connection, so as to ensure the tight combination of the rubber mud and the power line connection, and then apply the power tape fixed.

[0034] After construction, after the cement is...

Embodiment 2

[0044] Weigh raw materials: 100g of natural rubber; 30g of liquid polyisobutylene; 10g of α-pinene resin; 6.5g of zinc oxide; 3g of sulfur; 4g of stearic acid; 0.4g accelerator DM; 1.5g accelerator TMTD; 58g of channel black ; 1g rubber antioxidant RD; rosin 10g; Stir the natural rubber particles and channel black evenly, then add zinc oxide, sulfur, stearic acid, accelerator DM and accelerator TMTD and stir evenly, and finally add liquid polyisobutylene in turn , rubber anti-aging agent RD, rosin and α-pinene resin, stir evenly, then heat to 100°C for 60min, cool to room temperature, and seal the package.

[0045] Construction method: Fill the rubber mud in the joint of the power line and cover it on the connection surface, roll the rubber mud by hand to make it fully bonded to the power line connection, so as to ensure the tight combination of the rubber mud and the power line connection, and then apply the power tape fixed.

[0046] After construction, after the cement is ...

Embodiment 3

[0056] Weigh raw materials: natural rubber 100g; liquid polyisobutylene 30g; α-pinene resin 10g; zinc oxide 6.2g; sulfur 3.2g; stearic acid 3.8g; 0.5g accelerator DM; 1.4g accelerator TMTD; Black 59g; 0.9g rubber anti-aging agent RD; rosin 10.2g; mix the natural rubber particles and channel black evenly, then add zinc oxide, sulfur, stearic acid, accelerator DM and accelerator TMTD and stir evenly, and finally Add liquid polyisobutylene, rubber antioxidant RD, rosin and α-pinene resin and stir evenly, then heat to 100°C for 50min, cool to room temperature, and seal the package.

[0057] Construction method: Fill the rubber mud in the joint of the power line and cover it on the connection surface, roll the rubber mud by hand to make it fully bonded to the power line connection, so as to ensure the tight combination of the rubber mud and the power line connection, and then apply the power tape fixed.

[0058] After construction, after the cement is completely cured into a rubbe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
electrical resistivityaaaaaaaaaa
hardnessaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

Electric sealed waterproof electro-insulating rubber dough and its preparation method. The preparation method comprises the following steps: uniformly stirring 100 parts by weight of natural rubber particles and 58-60 parts by weight of channel black, adding 6-6.5 parts by weight of zinc oxide, 3-3.5 parts by weight of sulphur, 3.5-4 parts by weight of stearic acid, 0.4-0.6 part by weight of an accelerator DM and 1.3-1.5 parts by weight of an accelerator TMTD and uniformly stirring, adding 30 parts by weight of liquid polyisobutylene, 0.8-1 part by weight of a rubber antioxidant RD, 10-10.5 parts by weight of rosin and 10 parts by weight of alpha-pinene resin and uniformly stirring, heating to 100 DEG C and keeping for 40-60 min, cooling to room temperature, and sealing and packaging. By the use of the rubber dough, electric line contacts are effectively sealed and electro-insulated. The product has air isolation, water isolation and insulation effects, and protects line contacts exposed to the air or underground line contacts so as to prevent line contacts from oxidation and electric leakage and overlarge contact resistance and guarantee service life of electric lines.

Description

technical field [0001] The invention belongs to the field of cable joint insulation and sealing, and in particular relates to a power sealing waterproof insulating rubber clay and a preparation method thereof. Background technique [0002] With the increase of urban planning and construction, urban distribution network transformation, overhead insulated wires are widely used, and the laying of underground cables has increased in large quantities. Underground power line joints often appear in accident repairs such as power company construction or cable digging. Nowadays, power lines generally have insulation skins. After power line joints appear, the joints are exposed or wrapped with tape, which is very easy to Oxidation, leakage occurs, affecting line safety, or causing excessive contact resistance, resulting in shortened service life of power lines. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a kind of pow...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L7/00C08L23/20C08L93/04C08K13/02C08K3/22C08K3/06C08K5/09C08K3/04C09K3/10
Inventor 景欣刘长庆杨月颖王京赵英瑞
Owner JINZHOU ELECTRIC POWER SUPPLY COMPANY OF STATE GRID LIAONING ELECTRIC POWER SUPPLY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com