Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Solid oxide fuel cell cathode material

A fuel cell cathode and solid oxide technology, which is applied to fuel cell parts, battery electrodes, circuits, etc., can solve the problems of inability to meet the basic requirements of medium temperature oxide fuel cell cathode materials, and achieves reduction of synthesis time and synthesis. effect of temperature

Inactive Publication Date: 2007-07-04
HEILONGJIANG UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the problem that the existing cathode materials cannot meet the basic requirements of intermediate temperature oxide fuel cell cathode materials, the present invention develops a new type of solid oxide fuel cell cathode material, that is, the development of K 2 NiF 4 The structure of a new intermediate temperature oxide fuel cell cathode material makes it have a relatively high oxygen ion-electron mixed conductivity in the medium and low temperature region (the mixed conductivity of the material in the air at 800°C is close to 100Scm -1 ), while having good chemical stability (sintered at 1000°C for 24 hours in an air atmosphere, the material does not chemically react with the YSZ electrolyte) and thermal stability (that is, the thermal expansion coefficient matched with the electrolyte)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Solid oxide fuel cell cathode material
  • Solid oxide fuel cell cathode material
  • Solid oxide fuel cell cathode material

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0013] Specific embodiment 1: The general composition formula of the solid oxide fuel cell cathode material in this embodiment is A 1+x A 1-x 'B1-y B y 'O 4±δ , where A is the main group of alkaline earth metals, A' is a rare earth element, B and B' are transition group metal elements, 0

[0014] A and A' in this embodiment represent alkaline earth elements (Ca, Sr, or Ba, etc.) and rare earth elements (La, Ce, Pr, Nd, Pm, Sm, Eu, or Gd, etc.) in the periodic table, respectively. B and B' are transition group metal elements (Cr, Mn, Fe, Co, Ni, Cu, Zn, Mo, W, V, Nb or Ta, etc.).

specific Embodiment approach 2

[0015] Specific embodiment 2: The difference between this embodiment and specific embodiment 1 is that when A is Sr, A' is Sm, B is Ni, B' is Co, and δ=o, the solid oxide fuel cell cathode material The structural formula is Sr 1-x SM 1+x Ni 1-y co y o 4 .

specific Embodiment approach 3

[0016] Specific embodiment three: the difference between this embodiment and specific embodiment two is that when x=0.5 and y=0, the structural formula of the solid oxide fuel cell cathode material is Sr 0.5 SM 1.5 NiO 4 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Disclosed is a cathode material for solid oxidate fuel battery. The composition general formula of the invented cathode material is A1+xA1-x'B1-yBy'O4 + / -delta, wherein A is main group alkali earth metal, A' is rare-earth element, B and B' are transient elements, and 0 H01M 4 / 86 H01M 8 / 02 4 6 1 2005 / 8 / 19 1731607 2006 / 2 / 8 1324740 2007 / 7 / 4 2007 / 7 / 4 2007 / 7 / 4 Heilongjiang University Harbin 150080 Zhao Hui Huo Lihua Cheng Xiaoli Sun Liping Gao Shan chan jun 23109 The Patent Agency of Songhuajiang Prefecture of Heilongjiang Province No.6 Hexing Street, Dongli District, Harbin, Heilongjiang Province 150040

Description

Technical field: [0001] The invention relates to a cathode material, in particular to a solid oxide fuel cell cathode material. Background technique: [0002] The development of intermediate temperature oxide fuel cells has recently attracted attention. As the operating temperature decreases (600-800°C), the electrochemical performance of traditional cathode materials also decreases, and the polarization resistance increases. Research shows that La 0.85 Sr 0.15 MnO 3 (LSM) polarization resistance jumps from a few ohms at 1000°C to several thousand ohms at 800°C. Therefore, finding new cathode materials that can be used under medium temperature conditions has become an important task for the development of medium temperature fuel cells. The main solution at present is to develop oxygen ion-electron hybrid conductive materials. Generally speaking, the basic requirements for the cathode materials of intermediate temperature oxide fuel cells are: the material has a relativ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/86H01M8/02
CPCY02E60/50
Inventor 赵辉霍丽华程晓丽孙丽萍高山
Owner HEILONGJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com