Method for preparing flax fiber in high cleavage degree

A technology of flax fiber and splitting degree, which is applied in the chemical post-treatment of fibers, fiber treatment, textiles and papermaking, etc. It can solve the problem of splitting degree, spinnability, cohesion not meeting the requirements, flax fiber is not soft enough, spinning To solve the problem of low count, achieve the effect of improving spinnability, good color fastness, and improving spinnability

Inactive Publication Date: 2005-10-26
无锡鼎球绢丝纺有限公司
View PDF1 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Commonly used flax treatment is generally alkali boiling, washing, dehydration, opening, drying, because the obtained flax fiber is not soft enough, the degree of splitting is low, the adaptability is poor, and the spinning count is not high. The flax disclosed in Chinese patent CN93100748.4 In the production method of cotton blended yarn, in the flax fiber treatment process, it is softened with a softener after washing, although the softness of the flax fiber has been improved, the cohesion of the fiber has been increased, and the spinnability of the fiber has been improved. It is only suitable as a raw material for low-count blended spinning. If you want to increase the spinning count up to 120 N Above, the degree of splitting, spinnability and cohesion are not up to the requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] The preparation method of high splitting degree flax fiber, the steps are:

[0021] 1. Enzymatic degumming of flax raw materials. The flax raw material is soaked in the aqueous solution added with the enzyme preparation, and the enzyme preparation is made up of pectinase and cellulase at a ratio of 1:1. The process conditions are controlled as follows:

[0022] Bath ratio 1:1.3-1.5

[0023] Temperature 38-40°C

[0024] pH 7-7.5

[0025] Time 6-7 hours

[0026] Feeding weight of enzyme preparation: 0.3%-0.5%

[0027] 2. Atmospheric oxygen bleaching. The process conditions are controlled as follows:

[0028] Temperature: 90-100℃ Time: 50-60 minutes

[0029] The aqueous solution contains: H 2 o 2 8-10g / L Na 2 CO 3 2-3g / L natronine 0.2-0.4g / L

[0030] 3. Acid-base neutralization and softening. The process conditions are controlled as follows:

[0031] Temperature: 50-60℃ Time: 20-30 minutes

[0032] The aqueous solution contains: silicone oil 15-25g / L acet...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Preparation method of linen fiber of high fission belongs to the domain of weave. The stuff is come unglued by enzyme first, then oxygen bleach it in common pressure, acid and alkali neutralization, drying it and make linen fiber in wet condition. It improves the fission of the fiber and doesn't change its characteristic. The fission increases from 400 - 600 to more than 2000. The cohesion performance and spinnability of the fiber is improved. Blended yarn is high, can reach more than 160N.

Description

technical field [0001] The invention relates to the field of textiles, and refers to a method for preparing flax fibers with high splitting degree. technical background [0002] Commonly used flax treatment is generally alkali boiling, washing, dehydration, opening, drying, because the obtained flax fiber is not soft enough, the degree of splitting is low, the suitability is poor, and the spinning count is not high. The flax disclosed in Chinese patent CN93100748.4 In the production method of cotton blended yarn, in the flax fiber treatment process, it is softened with a softener after washing, although the softness of the flax fiber has been improved, the cohesion of the fiber has been increased, and the spinnability of the fiber has been improved. It is only suitable as a raw material for low-count blended spinning. If you want to increase the spinning count up to 120 N Above, the degree of splitting, spinnability and cohesion are not up to the requirements. Contents of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01C1/00
Inventor 汤雪峰
Owner 无锡鼎球绢丝纺有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap