A ternary copper and contact wire technology, applied in the field of cable wires and wires, can solve the problems of large fluctuations in process performance, increased production costs, and low productivity, and achieve the effects of improved corrosion resistance, reduced production costs, and increased productivity

Active Publication Date: 2008-01-09
邢台鑫晖铜业特种线材有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are still some problems in the production process of magnesium-copper alloy stranded wire, that is, because magnesium is a corrosive and active element, magnesium will cause strong corrosion to the furnace wall of the copper melting furnace and the holding furnace during the alloy melting process. , usually the furnace life is only 7 to 30 days, frequent furnace maintenance will increase production costs and low productivity
In addition, due to factors such as furnace wall damage, the process performance fluctuates greatly, resulting in a blank yield of only about 70%.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ternary copper-alloy stranded conductor and contact line preparing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1 Embodiment 2

[0029] Example 1 Example 2 Example 3 Example 4 Example 5 Example 6

[0030] Magnesium 0.13 0.10 0.30 0.40 0.43 0.50

[0031] Tin 0.10 0.15 0.35 0.30 0.10 0.40

[0032] Copper margin margin margin margin margin margin

[0033] The total amount of impurities in the above raw materials is not more than 0.30.

[0034] 1. Stranded wire preparation, see Figure 2:

[0035] a. Smelting: take copper, magnesium and tin raw materials according to the ratio of the embodiment and put them into a copper melting furnace for smelting. Of course, copper and magnesium can also be smelted into a copper-magnesium intermediate alloy at first, and then copper and tin raw materials are added to melt The temperature of the copper furnace is controlled at 1150±30°C.

[0036] b. Heat preservation: the alloy liquid melted by the steel melting furnace flows into the heat preservation furnace for heat preservation, the temperature is 1140±20°C, and the alloy liquid melted and heat preserved is ful...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
Login to view more

Abstract

Characters are that ternary copper alloy is prepared from materials according to following weight percent: magnesium 0.10-0.50, stannum 0.10-0.4, impurity less than 0.30, and other as copper. Through procedures of melting, heat preservation, casting bars, and cold rolling, twisted line and contact wire are prepared from the ternary copper alloy. In procedure for producing twisted alloy line, and contact wire, the invention raises furnace life of melting copper furnace and ratio between product and roughcast. The ratio is near to a hundred percent, and furnace life is raised to three times so as to lower cost and raise productivity. Through measurement by relevant department, mechanical and physical properties etc. indexes of the hard twisted alloy line reaches to or exceeds relevant indexes of current twisted line of magnesium copper. Product is accorded with requirement of technical standard completely.

Description

technical field [0001] The invention relates to a wire, in particular to a twisted wire, a contact wire, etc. used on an electrified railway catenary, and belongs to the technical field of cable wires. Background technique [0002] According to relevant literature reports, in 1996, the operating mileage of electrified railways in my country was 10,000 kilometers, and the electrification rate accounted for 17.8%. , but compared with Germany, France, Japan and other advanced countries, there is still a big gap compared with the operating mileage of electrified railways accounting for one-third and the operating volume undertaking two-thirds. In order to meet the needs of economic development, my country's electrified railways are developing in the direction of high speed and heavy loads. The annual demand for catenary conductors is 6,000 tons and current-carrying catenary cables are 6,000 tons. In recent years, with the continuous increase of railway speed for many times, the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01B13/00H01B5/00H01B7/10
Inventor 张进东
Owner 邢台鑫晖铜业特种线材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap