A manufacturing method and anode foil technology, applied in capacitor electrodes, capacitor parts and other directions, can solve the problems of high manufacturing cost and environmental protection cost, unfavorable promotion, low output, etc., and achieve low production cost and environmental protection cost and good overall stability. , controllable effect

Inactive Publication Date: 2007-09-05
DONGGUAN HEC CONDENSER CO LTD
View PDF0 Cites 35 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method requires that the current density of the initial energization be large enough, which will not only bring a lot of negative effects due to the excessive heat generation of the foil before electrolysis, but also cause serious merging of holes on the foil surface during the first electrolysis, which is not conducive to guaranteeing the product. The appearance, capacity dispersion and increase its electrostatic capacity, and the speed is slower and the output is lower
[0003] In

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] Corrosion foil implementation scheme in the medium-pressure section: imported Showa CH99 model 110um thick light foil, at about 5wt%H3 PO 4 In the bath, the temperature is 50°C, and the treatment is 45Sec: After washing with water, it is charged with direct current in an electrolysis, and the current density is 0.25A / cm 2 , the temperature is 89°C, the treatment is 3×45Sec (a 3V electrolytic cell), and the electrolytic cell solution is composed of 25Wt% H 2 SO 4 +3.5Wt% HCL+1Wt% aluminum ion composition; after washing, treat in 4Wt% ammonia water for 45Sec, the temperature is 75°C; after washing, in 4Wt% NH 4 At 0.10A / cm in Cl secondary electrolyte 2 DC power plus electrolysis 2×(4×45)Sec (two electrolyzers, each tank 4V), the temperature is 90°C; after washing with water, in 3Wt%HNO 3 Medium treatment 45Sec, the temperature is 60 ° C; after washing with 8Wt% HNO 3 +0.1Wt% corrosion inhibitor in the three electrolytes at 0.15A / cm 2 DC power plus electrolysis (4×45+...

Embodiment 2

[0048] Implementation of corrosion foil in the high-pressure section: HEC 115um thickness light foil is used, and the cubic texture requirement is greater than 97%; after being treated with 2Wt% NaOH alkaline pretreatment solution at a temperature of 38°C for 50Sec, it is washed with water and continued to be washed with 3Wt% h 3 PO 4 Acidic treatment solution, at a temperature of 50°C, for 50Sec; after washing with water, apply DC power in an electrolysis with a current density of 0.30A / cm 2 , the temperature is 82°C, the treatment is 2×50Sec (a 2V electrolyzer), and the electrolyzer liquid is composed of 30Wt% H 2 SO 4 +3Wt% HCL+1Wt% aluminum ion composition; after washing, treat in 4Wt% ammonia water for 50Sec, the temperature is 75°C; after washing, in 4Wt% NH 4 At 0.10A / cm in Cl secondary electrolyte 2 DC power plus electrolysis (4×50+2×50) Sec (two electrolytic tanks, one tank 4V, one tank 2V), the temperature is 88 ° C: after washing in 3Wt% HNO 3 Medium treatment ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Production of high-voltage anode anti-corrosion foil is carried out by taking A1 with purity>99.99% and cubic tissue structure>=95% as raw materials, pre-treating, first electrolyzing, first intermediate treating, second electrolyzing, second intermediate treating, third electrolyzing and after-treating. It consists of phosphoric acid, hydrochloric acid, sulfuric acid and nitric acid etc. acid treating liquid, weak base and strong base etc. treating liquid, sulfuric acid, hydrochloric acid, nitric acid, weak-acid chlorine salt and corrosion inhibitor cell liquor. It has good appearance, better electrostatic capacity and capacity difference. It can be used for medium-high voltage section dendritic holes by cell-liquor different properties.

Description

Technical field: [0001] The invention belongs to a method for manufacturing a corroded foil for medium and high voltage anode foils. Background technique: [0002] For the manufacture of corroded foil for traditional medium and high voltage anode foil, the process flow of sulfuric acid system is mostly: light foil → pretreatment → water washing → first electrolysis (porous stage) → water washing → second electrolysis (pore expansion stage) → water washing → third electrolysis ( Hole expansion stage) → water washing → post-processing → water washing → pure water washing → drying → corroding foil (some companies do not need three electrolysis). The hole design method generally adopts tunnel-shaped holes, and the specific volume of the corroded foil is usually increased by increasing the hole density through the first hole. This method requires that the current density of the initial energization be large enough, which will not only bring a lot of negative effects due to the e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C25F3/04H01G9/04
Inventor 陈锦雄
Owner DONGGUAN HEC CONDENSER CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap