Method for manufacturing imitating jade tap and its product and mould

A production method and faucet technology, which are applied to sliding valves, valve details, multi-way valves, etc., can solve the problems of affecting the water outlet flow of the faucet, easily broken and damaged, and difficult to dismantle the mold, and achieve diversified appearance and color, low cost, and production. low cost effect

Inactive Publication Date: 2008-01-16
张长春
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Some have low strength and are easy to break and damage; some are difficult to remove the formwork and have a low yield
[0003] Chinese patent application 200610031039.5 relates to "a plastic faucet and its production process and mold". There are also several connecting pipes in the body, the inner end of each connecting pipe is connected with the valve core seat, and the outer end of each connecting pipe is respectively connected with the above-mentioned water inlet pipe or water outlet pipe, although the above-mentioned faucet is low in cost and weight Light; but the connecting pipe used in this faucet is a silicone hose, so that during the injection molding process, because the plastic is in a liquid state, the temperature is high and the pressure is high; thus these silicone hoses are squeezed, and after the plastic is cured , these connecting pipes are squeezed and deformed in the body, which affects the water flow of the entire faucet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for manufacturing imitating jade tap and its product and mould
  • Method for manufacturing imitating jade tap and its product and mould
  • Method for manufacturing imitating jade tap and its product and mould

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0065] The technological process of the manufacturing method of this imitation jade faucet is as follows:

[0066] A. Parts production: parts of imitation jade faucet, including connecting pipe 5, spring 8, valve core seat 4, water inlet seat 6, water outlet seat 7, water inlet pipe 2, water outlet pipe 3, valve cover, pressure cap, valve Core, handle. Among them, the spring 8, the water inlet pipe 2, the water outlet pipe 3, the valve cover, the pressure cap, the valve core, the connecting pipe 5, and the handle are ordinary parts, which can be made by general processing technology, or can be directly purchased in the market:

[0067] Use wood to make the same model as valve core seat 4, water inlet seat 6, and water outlet seat 7, make a wooden frame with wood, and install the above-made models of valve core seat 4, water inlet seat 6, and water outlet seat 7 on the wood. On the wooden board of the frame, the feeding trough is made of wooden strips, and the various models a...

Embodiment 2

[0073] In the present embodiment, the prepared imitation jade material according to Example 2 in Table 1 is melted and injected into the mold, and the curing time is 5 minutes.

Embodiment 3

[0075] In this embodiment, the prepared imitation jade material according to Example 3 in Table 1 is melted and injected into the mold, and the curing time is 20 minutes.

[0076] Table 1: the composition of the imitation jade material that the present invention adopts (by weight)

[0077]

[0078] Wherein the resin described in Example 1 is unsaturated polyester resin agate S-793C; the filler is aluminum hydroxide; the accelerator is cobalt naphthenate; the pigment is a general organic colorant ; Described catalyst is methyl ethyl ketone peroxide.

[0079] The resin described in Example 2 is unsaturated polyester resin 196; the filler is glass powder; the accelerator is cobalt naphthenate; the pigment is a commercially available organic colorant; the The catalyst is methyl ethyl ketone peroxide.

[0080] The resin described in Example 3 is unsaturated polyester resin agate S-793C; the filler is aluminum hydroxide and glass powder, and the weight ratio of the two is 5:5; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a making method of a jade-like water tap and the product and a die thereof, relating to a water tap, which solves the problem on current water tap that water discharging amount is not agreeable. The making method of the jade-like water tap comprises the following steps: A. assembling the die; B. closing the die; C. injecting; D. assembling. The jade-like water tap comprises a body inside which a circular tube and a valve core seat are arranged. A water inlet pipe and a water outlet pipe are fixedly connected to the body and both are communicated with the valve core seat through respective connecting tubes. The body is made of resin and the connecting tubes are provided with reinforcing structures inside to strengthen the intensity of the connecting tubes. An upper die body and a lower die body of the jade-like water tap are made of plaster and the joint interface of the upper die body and the lower die body is provided with a silicon glue layer; the positioning holes of the valve core seat, the water inlet seat and the water outlet seat are provided with positioning devices. With the method, rate of finished water taps is high and the products are elegant in appearance and good in taste.

Description

technical field [0001] The invention relates to a manufacturing method of a faucet and a product thereof; in particular, to a manufacturing method of an imitation jade faucet, a product thereof and a mold used for manufacturing the faucet. Background technique [0002] Existing faucets can be made of metal materials and non-metal materials; using metal materials to make faucets is mainly that the body part of the faucet is made of metal materials, and then loaded into the valve core, valve stem, handle and other parts; using this This manufacturing method not only needs to consume a lot of metal materials; increases the cost of the faucet; and because the mold uses a sand core during the production process, these products will have blisters and pores, and the defective rate is high. Existing faucets are made of non-metallic materials, such as ceramic faucets and plastic faucets. Some have low strength and are easily broken and damaged; some are difficult to demold and have ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B29C69/00B29C45/14B29C45/26B29C65/56F16K3/08F16K11/074F16K27/04B29K105/06B29K67/00B29K505/02B29K509/08
Inventor 张长春
Owner 张长春
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap