Ball-milling force chemical synthesis method of polyaniline

A technology of chemical synthesis and polyaniline, applied in the field of polymer materials, can solve the problems of polyaniline synthesis and negative effects on properties, limited source of aniline salt monomer, poor conductivity of polyaniline, etc., to achieve environmental friendliness, solvent saving, The effect of avoiding adverse effects

Inactive Publication Date: 2010-07-21
SHANGHAI JIAOTONG UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the conductivity of polyaniline prepared by Jiaxing Huang et al. is not good, and the conductivity of its powder compact is only 10 -2 S / cm order of magnitude
This method mainly has two deficiencies: one, the sources of aniline salt monomers are limited and expensive, and the types of dopants contained in the prepared polyaniline are limited; Necessary cooling measures allow the temperature of the reaction system to rise, which will have a serious negative impact on the synthesis and properties of polyaniline

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] The present invention is described in detail below in conjunction with embodiment, these embodiments are based on the premise of the technical solution of the present invention, have provided detailed implementation and specific operation process, but protection scope of the present invention is not limited to following embodiment.

[0029]In the following examples, the used aniline monomers are all purified by distillation. Adding aniline monomer, dopant, oxidant and balls into a ball mill for low-temperature ball milling, wherein the molar ratio of dopant to aniline monomer is 0.3-1.0, and the molar ratio of oxidant to aniline monomer is 0.2-2.0, The ball milling temperature is -196°C-0°C, the ball milling speed is 100 rpm-1000 rpm, and the ball milling time is 0.5 hours-10 hours. In some embodiments, a small amount of auxiliary solvent is also added, and the molar ratio of the added amount relative to the aniline monomer is 0.5-5.0.

[0030] After the ball milling, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a chemical synthesis method for polyaniline using ball milling, belonging to the technical field of macromolecular materials, which comprises the following steps: firstly, milling aniline monomers, dopants, and oxidants in a ball mill, initiating polymerization reaction, wherein, the molar ratio of the dopants and the aniline monomers is 0.2 to 2; secondly, washing, separating, and drying the products of the ball milling reaction, obtaining doped state polyaniline after removing oligomeric products and residual reactants; and thirdly, using alkali to detract doping to the doped state polyaniline, obtaining doping-polyaniline. The chemical synthesis method for polyaniline using ball milling has the advantages of easily available materials, wide adaptability, high efficiency, environment-friendly, and easy for mass production.

Description

technical field [0001] The present invention relates to a method in the technical field of polymer materials, in particular to a method for ball milling mechanochemical synthesis of polyaniline, that is, a method for preparing polyaniline by using ball milling to induce mechanochemical polymerization of aniline monomers. Background technique [0002] Among the intrinsically conductive polymer materials with conjugated structures, polyaniline is considered to be the most promising due to its structural diversity, unique doping mechanism, excellent physical and chemical properties, low raw material prices, and simple synthesis process. Conductive polymer materials can be used in almost all modern emerging industries and high-tech fields. However, so far, all polyaniline synthesis methods that have been adopted are carried out in the liquid phase, including chemical oxidation polymerization, electrochemical polymerization, air oxidation polymerization, template polymerization, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08G73/02
Inventor 李志强张荻朱申敏
Owner SHANGHAI JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap