Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Spraying coating material

A coating and cellulose resin technology, applied in the direction of cellulose coatings, coatings, devices for coating liquid on the surface, etc., can solve problems such as complicated use process

Inactive Publication Date: 2011-05-25
HUIZHOU CHANGRUNFA PAINT
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The present invention can replace the traditional electroplating process, but this coating consists of three parts: primer coating, metal spray coating and top coating, and the application process is relatively complicated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] A kind of spray coating, its percentage by weight is composed of: vinyl chloride resin 7wt , Triethanolamine 0.3wt , silver paste 1.8wt , nitrocellulose resin 10~22wt , Butyl acetate 61.5~82.3t . The material of the above formula is stirred at high speed to form a spray coating, which can be used in various plastic electronic products such as ABS, PC, PC+ABS, etc. The spraying process is simple and the operation is convenient. It can give the product a strong mirror metal texture, and the production The environment complies with ROHS standard.

Embodiment 2

[0011] A kind of spray coating, its percentage by weight is composed of: vinyl chloride resin 8wt , Triethanolamine 0.4wt , silver paste 2wt , nitrocellulose resin 10~22wt , Butyl acetate 61.5~82.3wt . The material of the above formula is stirred at high speed to form a spray coating, which can be used in various plastic electronic products such as ABS, PC, PC+ABS, etc. The spraying process is simple and the operation is convenient. It can give the product a strong mirror metal texture, and the production The environment complies with ROHS standard.

Embodiment 3

[0013] A kind of spray coating, its percentage by weight is composed of: vinyl chloride resin 10wt , Triethanolamine 0.3wt , silver paste 3wt , nitrocellulose resin 10~22wt , xylene, acetic acid mixed solvent 61.5~82.3wt . The material of the above formula is stirred at high speed to form a spray coating, which can be used in various plastic electronic products such as ABS, PC, PC+ABS, etc. The spraying process is simple and the operation is convenient. It can give the product a strong mirror metal texture, and the production The environment complies with ROHS standard.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses spray plating paint, which comprises components with percentage by weight of 10-22 wt% cellulose resin, 6-12 wt% vinyl chloride-acetate copolymer, 0.25-05 wt% micro-molecular directing auxiliary agent, 1.5-4.0 wt% silver slurry and 61.5-82.3 wt% solvent. The spray plating effect of the paint is same as electroplating products, the paint can be used on various plastic adhesive electric products such as ABS, PC, PC+ ABS and the like, and the spraying technology is simple and can be operated conveniently.

Description

technical field [0001] The invention relates to the field of substrate surface finishing, in particular to a spray coating that can be used to replace electroplating. Background technique [0002] Electroplating is an important basis for surface treatment of materials, and it involves a wide range. From the characteristics of industry production, the wastewater, waste gas, and waste residue produced by the electroplating industry have a great impact on human survival. Chinese patent CN1936075 provides a spray coating and process to replace electroplating. It adopts high-performance coating and sprays with special equipment and process to form a high-brightness spray coating material. The entire sprayed coating consists of three parts: the primer layer, the metal sprayed layer and the top coat. This spray coating can be used on various substrates such as metal, plastic, glass, ceramics, wood, etc., and the color can also be selected according to the needs of decorative appea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D101/02B05D1/02C09D127/08
Inventor 程强
Owner HUIZHOU CHANGRUNFA PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com