2 mu m luminous rare earth ion doped germanate laser glass and preparation thereof

A technology of laser glass and germanate, which is applied in the field of germanate glass, can solve the problems of lack of pump sources and achieve excellent luminous properties

Inactive Publication Date: 2009-07-22
SHANGHAI INST OF OPTICS & FINE MECHANICS CHINESE ACAD OF SCI
View PDF0 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ho 3+ The main problem with doped fiber lasers is the lack of an effective pump source

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 2 mu m luminous rare earth ion doped germanate laser glass and preparation thereof
  • 2 mu m luminous rare earth ion doped germanate laser glass and preparation thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] Table 1 shows the glass formulations and some test results of 10 examples of the present invention.

[0026] Table 1: Glass formulations of 10 specific examples

[0027] Component (mol%) 1# 2# 3# 4# 5# 6# 7# 8# 9# 10# GeO 2 65 70 65 70 65 65 65 65 65 65 BaF 2 20 15 20 15 20 20 20 20 20 20 Ga 2 o 3 2 2 2 6 6 13 9 6 6 4 La 2 o 3 5 5 3 6 LaF 3 5 5 5 5 Yb 2 o 3 6 6 3 4 3 3 wxya 3 6 T m 2 o 3 1 1 2 1 TmF 3 1 2 4 1 4 Ho 2 o 3 1 1 1 HoF 3 1 1 1 1 1 Pump wavelength(nm) 980 980 980 980 980 808 808 980 980 808 Luminescence peak wavelength

(μm) ～2 ～2 ～2 ～2 ～2 ～2 ～1.8 ～1.8 ～2 ～2 light intensity high high high middle middle Difference high Difference Difference high

[0028...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses 2-micron luminous rare-earth ion-doped germanate laser glass and a preparation method thereof. The mol percentage composition of the glass is as follows: 60 to 65 percent of GeO2, 15 to 20 percent of BaF2, 2 to 13 percent of Ga2O3, and 2 to 13 percent of Re2O3ReF3; wherein, Re is the rare-earth elements of La, Yb, Tm and Ho. The rare-earth ion doping mode of the glass is: single doping of Tm, double doping of Yb and Tm, double doping of Yb and Ho, double doping of Tm and Ho, or three doping of Yb, Tm and Ho. Rare-earth ions are introduced in the form of rare earth oxides or rare earth fluorides and can all obtain the glass with stability and excellent luminous performance. Test result shows that the germanate glass in the invention has higher transmission rate and wider transmission range. A fluorescence spectrum test shows that the germanate laser glass of the invention can obtain excellent fluorescence emitting approaching to 2-micron. The laser glass of the invention is also suitable for preparing 2-micron optical fiber perform cores.

Description

technical field [0001] The invention relates to germanate glass, in particular to a germanate laser glass doped with 2 μm luminescent rare earth ions and a preparation method thereof. Background technique [0002] For the mid-infrared laser with a wavelength of 2 μm, it is very important in the fields of medical surgery, optical communication, gas monitoring, environmental pollution detection and analysis, and human eye safety lidar, as well as for the pumping source of new mid-infrared band lasers. Value. T m 3+ and Ho 3+ It has been extensively studied as an active ion for lasers in various substrates in the 2 μm region. Doped Tm 3+ and Ho 3+ Ionic fiber lasers are strong candidates as compact and efficient all-solid-state laser sources. [0003] With the adoption of high-power semiconductor lasers and cladding pumping methods, the performance of thulium-doped fiber lasers has also been greatly improved (see prior art: Jianfeng Wu, Zhidong Yao, Jie Zong et al.Highlye...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C3/253C03B5/235
Inventor 张军杰于春雷汪国年王孟衣丽霞徐茸茸胡丽丽
Owner SHANGHAI INST OF OPTICS & FINE MECHANICS CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com