Short-fiber oil agent for aromatic polyamide fiber

A kind of aromatic polyamide, oil agent technology, applied in the direction of fiber type, fiber treatment, textile and papermaking, etc., can solve the problems of antistatic, cohesion and poor heat resistance, to enhance antistatic performance, reduce static electricity , the effect of reducing tarification

Active Publication Date: 2011-07-20
CHINA PETROCHEMICAL CORP +1
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] The present invention aims at the disadvantages of antistatic property, poor compatibility and heat resistance of the oil agent in the prior art, and proposes a new short fiber oil agent for aromatic polyamide fiber. The oil agent has good antistatic property, Cohesion, dyeing uniformity and post-processing, the spun aramid staple fiber can be suitable for different purposes

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Short-fiber oil agent for aromatic polyamide fiber
  • Short-fiber oil agent for aromatic polyamide fiber
  • Short-fiber oil agent for aromatic polyamide fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Get 20 grams of pentaerythritol nonanoate, 20 grams of polyoxyethylene (the number of moles is 10) glycerol dioleate, 30 grams of polyether (m=10, n=20, R 1 is n-octyl, R 2 is H atom, z=1) in the synthesis kettle, fully stirred at 30±2°C for 20 minutes; then sequentially added 10 grams of alkyl polyoxyethylene ether phosphate ester salt (R 4 for C 8 Alkyl, M is metal element potassium, X=3), 19 grams of alkyl polyoxyethylene ether sulfates, (R 5 for C 6 Alkyl group, M is metal element potassium, Y=6), 1 gram of polyether modified silicone oil (R 6 for C 4 Hydrocarbons, m2=10, n2=10, p=40, q=60, r=4), then fully stirred at 30±2°C for 20 minutes, and filtered to obtain the invented oil agent A.

Embodiment 2

[0038] Get 30 grams of pentaerythritol oleate, 20 grams of polyoxyethylene (20 moles) glycerol dioleate, 20 grams of polyether (m=20, n=40, R 1 is n-butyl, R 2 is H atom, z=1) in the synthesis kettle, fully stirred at 30±2°C for 20 minutes; then sequentially added 15 grams of alkyl polyoxyethylene ether phosphate ester salt (R 4 for C 12 Alkyl, M is metal element potassium, X=6), 12 grams of alkyl polyoxyethylene ether sulfates, (R 5 for C 12 Alkyl group, M is metal element potassium, Y=6), 3 grams of polyether modified silicone oil (R 6 for C 4 Hydrocarbons, m2=20, n2=20, p=40, q=80, r=4), then fully stirred at 30±2°C for 20 minutes, and filtered to obtain the invented oil agent B.

Embodiment 3

[0040] Get 30 grams of pentaerythritol caprate, 20 grams of polyoxyethylene (20 moles) sorbitan monolaurate, 20 grams of polyether (m=20, n=40, R 1 is n-butyl, R 2 12 alkyl groups, z=1) in the synthesis kettle, fully stirred at 30±2°C for 20 minutes; then sequentially added 15 grams of alkyl polyoxyethylene ether phosphate ester salt (R 4 for C 12 Alkyl, M is metal element potassium, X=6), 12 grams of alkyl polyoxyethylene ether sulfates, (R 5 for C 12 Alkyl group, M is metal element potassium, Y=6), 3 grams of polyether modified silicone oil (R 6 for C 2 Hydrocarbon, m2=30, n2=20, p=40, q=40, r=2), then fully stirred at 30±2°C for 20 minutes, and filtered to obtain the invented oil agent C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses a short-fiber oil agent for aromatic polyamide fiber, which is characterized in that: (a), prepared from 3 to 40 weight percent of polyol fatty acid ester; (b), 5 to 70 weight percent of polyoxyethylene polyolfatty acid ester; (c), 5 to 40 weight percent of fatty alcohol ethylene oxide-propylene oxide random copolyether or polyether ester; (d), 1 to 40 weight percent of fatty alcohol polyethenoxy ether organic phos fatty acid ester; (e), 1 to 30 weight percent of fatty alcohol polyethenoxy ether sulfuric acid ester salt and 0.1 to 10 weight percent of polyether modified silicon oil. The oil agent can solve the defects of the poor main performance, i.e. poor electrostatic resistance, poor heat resistance, poor saturation, and the like of the prior oil agent, aims to provide an aramid short-fiber oil agent which has poor main performance, i.e. poor electrostatic resistance, poor heat resistance, poor saturation, and the like of the prior oil agent, aims to provide an aramid short-fiber oil agent which has excellent electrostatic resistance, smoothness, softness and dyeing uniformity, enables the aramid short fiber to have excellent post processing performance, and the like.

Description

technical field [0001] The invention relates to a lubricating oil composition characterized by an oxygen-containing polymer mixture as an additive, in particular to an oil agent for aromatic polyamide fiber short fibers. Background technique [0002] Aromatic polyamide fibers (Aromatic polyamide fibers) are aramid fibers, and their molecules are linear polymers formed by directly connecting two aromatic rings with amide bonds. There are two main types, one is aramid fiber 1313 (product of DuPont Company The name is Nomex), the chemical name is poly-m-phenylene isophthalamide (Poly-m-phenylene isophthalamide, PMIA) fiber, and the molecular formula is: [0003] [0004] It has good heat resistance and flame resistance. It can be used for more than ten years at 220 ° C. The fabric does not deform at 260 ° C. It will gradually carbonize and not melt when it is above 370 ° C. It can be used to make space suits, racing suits, fire suits, heat-resistant Anti-corrosion filter cl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M101/34D06M15/63D06M15/53D06M13/224
Inventor 张瑞波李克文时东兴陈小民杨玉敏
Owner CHINA PETROCHEMICAL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com