Flame-retardant finishing fluid applied to blended fabrics containing polyamide fibers and flame-retardant finishing process

A polyamide fiber, flame retardant finishing technology, applied in the direction of fiber treatment, fiber type, plant fiber, etc., can solve the problems of strong odor, insufficient flame retardant and washing resistance of fabrics, and difficult to remove odor after washing, and achieves odor reduction, The effect of reducing formaldehyde content and reducing taring

Inactive Publication Date: 2019-04-26
MIANYANG GANLION PRINTING & DYEING +1
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the problems of insufficient flame retardant and washable performance of the C / N blended fabrics treated by the existing flame retardant finishing technology, as well as the problems of high environmental odor in the production environment, sticky rolls, and difficult to remove odor after washing, the present invention provides a method for containing The flame retardant finishing liquid of polyamide fiber blended fabrics achieves improved washability and flame retardant effect, and at the same time, the formaldehyde content of the flame retardant treatment liquid is reduced, and the odor of the finishing site is greatly reduced. Lighten, the technical effect of reducing the number of roaster cleaning and improving production efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant finishing fluid applied to blended fabrics containing polyamide fibers and flame-retardant finishing process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Example 1 A flame-retardant finishing solution and flame-retardant finishing process for blended fabrics containing polyamide fibers

[0024] A flame retardant finishing solution for blended fabrics containing polyamide fibers, the prescription of the flame retardant finishing solution is: flame retardant ZR-2 400-g / L, crosslinking agent GX-100 3g / L, phosphoric acid 20g / L, fiber protection agent DH6500 20g / L, wherein, the fabric is a blended fabric composed of cellulose fiber and polyamide fiber, and in the blended fabric, polyamide fiber accounts for 40% by weight.

[0025] A flame-retardant finishing process for blended fabrics containing polyamide fibers, comprising the following steps:

[0026] (1) Prepare flame retardant finishing liquid: according to the prescription of flame retardant finishing liquid as described in the present embodiment, weigh flame retardant, crosslinking agent, phosphoric acid, fiber protective agent;

[0027] (2) Flame retardant finishing...

Embodiment 2

[0035] Example 2 A flame-retardant finishing solution and flame-retardant finishing process for blended fabrics containing polyamide fibers

[0036] A flame retardant finishing solution for blended fabrics containing polyamide fibers, the prescription of the flame retardant finishing solution is: flame retardant ZR-2 450g / L, crosslinking agent GX-100 3.5g / L, phosphoric acid 22g / L, fiber protection agent DH6500 25g / L, wherein, the fabric is a blended fabric composed of cellulose fiber and polyamide fiber, and in the blended fabric, polyamide fiber accounts for 45% by weight.

[0037] A flame-retardant finishing process for blended fabrics containing polyamide fibers, comprising the following steps:

[0038] (1) Prepare flame retardant finishing liquid: according to the prescription of flame retardant finishing liquid as described in the present embodiment, weigh flame retardant, crosslinking agent, phosphoric acid, fiber protective agent;

[0039] (2) Flame retardant finishin...

Embodiment 3

[0047] Example 3 A kind of flame-retardant finishing solution and flame-retardant finishing process for blended fabrics containing polyamide fibers

[0048] A flame retardant finishing solution for blended fabrics containing polyamide fibers, the prescription of the flame retardant finishing solution is: flame retardant ZR-2 500g / L, crosslinking agent GX-100 4g / L, phosphoric acid 23g / L , fiber protection agent DH6500 26g / L, wherein, the fabric is a blended fabric composed of cellulose fiber and polyamide fiber, in the blended fabric, polyamide fiber accounts for 50% by weight, and the blended fabric is a semi-finished product for printing .

[0049] A flame-retardant finishing process for blended fabrics containing polyamide fibers, comprising the following steps:

[0050] (1) Prepare flame retardant finishing liquid: according to the prescription of flame retardant finishing liquid as described in the present embodiment, weigh flame retardant, crosslinking agent, phosphoric ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses flame-retardant finishing fluid applied to blended fabrics containing polyamide fibers and a flame-retardant finishing process. The formula of the flame-retardant finishing fluid comprises 400-500g / L of a flame retardant ZR-2, 3-4g / L of a cross-linking agent GX-100, 20-23g / L of phosphoric acid and 20-26g / L of a fiber protective agent DH6500, wherein the fabric is a blendedfabric composed of cellulosic fibers and polyamide fibers; and in the blended fabric, a weight ratio of the polyamide fibers is 40-50%. According to the flame-retardant finishing fluid and the flame-retardant finishing process disclosed by the invention, the treated blended fabric composed of the cellulosic fibers and polyamide fibers achieves an effect of improving the washable and flame-retardant effects, the content of formaldehyde in the flame-retardant finishing fluid is reduced, and odor in the finishing site is greatly alleviated. Meanwhile, tarring of the flame-retardant roasted non-crosslinked flame retardant is greatly alleviated, the cleaning frequency of the baking machine is reduced, and the production efficiency is improved.

Description

technical field [0001] The invention relates to the field of fabric preparation, in particular to a flame-retardant finishing solution and a flame-retardant finishing process for blended fabrics containing polyamide fibers. Background technique [0002] The blended fabric of cellulose fiber and polyamide fiber has the characteristics of high wear resistance, high strength and high wearing comfort, which is a necessity for military clothing. However, due to their flammability, they often bring disasters to us. Special labor protective clothing, military uniforms, etc. put forward strict requirements for heat insulation and fire prevention. From the long-term trend, the demand for flame retardant is one of the basic needs in daily life. [0003] There are two main domestic production methods for washable and flame-retardant C / N blended fabrics: one is to use probenzene for flame-retardant, which has a better flame-retardant effect, but has poor light fastness, and the heat o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M13/00D06M15/00D06M11/70D06M101/06D06M101/34
CPCD06M11/70D06M13/00D06M15/00D06M2101/06D06M2101/34D06M2200/30
Inventor 胡志强石岷山王善光
Owner MIANYANG GANLION PRINTING & DYEING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products