Low welding crack sensitivity steel with tensile strength at 700MPa level and production method thereof

A technology with low welding cracks and tensile strength, used in temperature control, manufacturing converters, etc., can solve problems such as low strength, achieve excellent welding performance, low production cost, and simplify the welding process.

Active Publication Date: 2010-12-29
武汉钢铁有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Compared with the steel of the invention, the strength of the steel of the invention is lower

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low welding crack sensitivity steel with tensile strength at 700MPa level and production method thereof
  • Low welding crack sensitivity steel with tensile strength at 700MPa level and production method thereof
  • Low welding crack sensitivity steel with tensile strength at 700MPa level and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0037] Embodiment: Carry out 9 embodiments (specification 16mm) by steel chemical composition of the present invention and production technology requirement, and with the steel grade of related technology in the background technology, as Sumitomo Metal (comparison steel 1), Anshan Iron and Steel (comparison steel 2) , Wuyang Iron and Steel Company (comparison steel 3) to conduct a comparative test. The chemical composition of the steels of the examples and the comparison is shown in Table 1, the rolling and heat treatment processes are shown in Table 2, and the mechanical properties are shown in Table 3.

[0038] Table 1 Example and comparative steel chemical composition (wt, %)

[0039]

[0040] Table 2 Example and comparative steel production process

[0041]

[0042] Table 3 Examples and comparative steel properties

[0043]

Yield Strength

/ MPa

tensile strength

/ MPa

Steel toughness

/ J

Elongation

/ %

HV10

Exam...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides low welding crack sensitivity steel with tensile strength at a 700MPa level and a production method thereof. The steel comprises the following two or more chemical components in percentage by weight: C: 0.08-0.12, Si: 0.15-0.40, Mn: 1.00-2.00, P: smaller than or equal to 0.015, S: smaller than or equal to 0.006, Ni: 0.25-0.55, Mo: 0.15-0.28, V: 0.02-0.10, Cu: 0.18-0.30, Cr:0.15-0.30, Ti: 0.008-0.020 and B: 0.0007-0.0027 as well as the balance of Fe and inevitable impurities and also satisfies that Pcm is smaller than or equal to 0.24 percent and satisfies an equation: Pcm=C+Si / 30+Mn / 20+Cu / 20+Cr / 20+Ni / 60+Mo / 15+V / 10+5B (percent). The invention adopts a deep molten iron desulphurization technology, a converter top and bottom converting, vacuum treatment and continuouscasting processes and carries out rolling and hardening, tempering and thermal treatment production according to a general clean steel process.

Description

technical field [0001] The invention relates to a low welding crack sensitivity steel with a tensile strength of 700MPa and a production method thereof, belonging to the field of low alloy steel manufacturing. Background technique [0002] Before the present invention, there was a patent (JP08209238) applied by Japan NKK "Method for manufacturing high-strength steel containing Si, Mn, Mo, Ni, V, Al, Ti, B by heating to obtain excellent welding crack sensitivity", in this patent Although the steel plate possesses low crack sensitivity and high heat input resistance welding performance simultaneously, the content of Nb and V in the steel is limited by the formula 625Nb+250V+210Ceq=40+t (t is the steel plate thickness mm), which is different from that of the steel plate of the present invention. The design ideas of the components are different, and the patent does not show the specific strength level of the steel plate. [0003] The patent (JP54130426) applied by Sumitomo Meta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/58C22C38/54C21C1/02C21C5/30C21C7/10B22D11/00C21D1/25C21D8/02C21D1/18B21B37/74
Inventor 习天辉郭爱民张开广刘文斌芮晓龙董汉雄董中波郭斌黄成红周佩丁庆丰邱保文
Owner 武汉钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com