A kind of composite concrete foaming agent and its preparation method and application

A technology for concrete and foaming agent, applied in the field of building materials, can solve the problems of decreased flexural strength, decreased compressive strength, delayed setting, etc., and achieves the effects of increasing the amount of foaming, simple production, and easy availability of raw materials

Inactive Publication Date: 2012-02-22
刘兴山
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Practice has proved that for every 1% increase in foaming air content, the compressive strength of concrete will decrease by about 5%, and the flexural strength will decrease by 2%-3%.
The strength of foam concrete is too low or does not meet the engineering requirements, which limits its application and promotion
In addition, a large amount of foaming agent will also cause slow setting or late setting of concrete, occupying tools and molds will affect its turnover, and even delay the construction period, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of composite concrete foaming agent and its preparation method and application
  • A kind of composite concrete foaming agent and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] The present invention will be further described below in conjunction with the examples. It should be understood that these examples are only for the purpose of illustration, and in no way limit the protection scope of the present invention.

[0019] Composite blowing agent implementation mode is expressed by the ratio of each raw material and text in Table 1, and its weight unit is calculated by heart:

[0020] Table 1

[0021]

[0022]

[0023] Take embodiment 2 as example to illustrate that the preparation method of composite concrete foaming agent of the present invention is as follows:

[0024] Take each raw material by weighing in table 1, get water 54.65kg, with wherein 30% water is heated to 70-80 ℃ after polyvinyl alcohol is diluted stand-by; Remaining water is put into heat container, processing industry caustic soda 4kg; Add 20kg of rosin, stir and pyrolyze at a temperature of 70-80°C, wait for about 100 minutes for the raw materials to fully dissolve a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
porosityaaaaaaaaaa
Login to view more

Abstract

The invention provides a compound concrete foaming agent and its preparation method and application. 1.5-2.5 parts of anhydrous sodium carbonate, 3.5-4.5 parts of industrial caustic soda, 3-5 parts of triethanolamine, 0.2-0.5 parts of industrial grade hydrochloric acid, 53.5-55.8 parts of water; the B component is: triethanolamine 0.2- 0.5 parts, 8-10 parts of sodium sulfate, 12-15 parts of sodium nitrite, 10-25 parts of calcium chloride, 54.7-64.5 parts of water. The composite concrete foaming agent of the present invention can not only increase the amount of foaming agent, but also compensate the concrete strength and solidification time; it can not only produce ultra-low-capacity foamed concrete, but also use a large amount of waste residues such as industrial and construction waste , to produce lightweight foamed concrete.

Description

technical field [0001] The invention belongs to the field of building materials, and relates to a composite concrete foaming agent and its preparation method and application, in particular to a foaming agent that can increase the amount of foaming agent and compensate the strength and solidification time of concrete. It is a composite foaming agent for producing ultra-low-capacity foamed concrete, and a large amount of waste residues such as industrial and construction waste can be used to produce lightweight foamed concrete. Background technique [0002] To prepare lightweight foamed concrete, it is first necessary to prepare a foaming agent with a large amount of foam and strong foam stabilizing ability. After foaming by mechanical means, it is mixed with concrete and cast into shape. The lightweight foamed (or foamed) concrete produced by the foaming agent is a porous material with a porosity of up to 85% and a thermal conductivity of 0.15-0.21 / (m.k). At present, there a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B24/34
CPCC04B28/10C04B2103/0006C04B40/0046
Inventor 刘兴山靳雪征刘冰
Owner 刘兴山
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap