Method for preparing magnetic recording exchange coupling complex film

An exchange coupling, composite film technology, applied in magnetic recording, data recording, recording information storage, etc., can solve the problems of reducing the thermal stability of the medium film, writing difficulties, etc.

Inactive Publication Date: 2010-03-03
山西师范大学
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Magnetic recording is the core technology of information storage. The development of information technology has higher and higher requirements for magnetic recording. Improving the magnetic recording density is the core of information storage. The perpendicular magnetic recording medium film is the key to achieve 1Tbit/in 2 The key technology of ultra-high recording density requires that the perpendicular magnetic recording medium film has a smaller grain size, but the extremely fine grain size of the magnetic grain may produce a superparamagnetic eff...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing magnetic recording exchange coupling complex film
  • Method for preparing magnetic recording exchange coupling complex film
  • Method for preparing magnetic recording exchange coupling complex film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0102] The present invention will be further described below in conjunction with accompanying drawing:

[0103] figure 1 As shown, it is the structural diagram of the exchange coupling composite dielectric membrane. The dielectric membrane has six layers in total, and each layer is tightly combined with good compactness.

[0104] figure 2 As shown, the state diagram of the exchange coupling composite film prepared by magnetron sputtering, the position and connection relationship of each part should be correct, the installation should be firm, and the operation should be convenient.

[0105] The materials and quantities used in this preparation are determined according to the preset range, in grams, milliliters, centimeters 3 , mm is the unit of measurement.

[0106] The preparation is completed in a strictly clean state. In the furnace cavity, in an argon atmosphere, under a magnetic field, in a water-cooled state, and under a vacuum of 1.0Pa, the entire coating process mu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for preparing magnetic recording exchange coupling complex film. The method takes flat glass as a substrate and takes a silver target, an iron target, a ruthenium target and an iron-platinum alloy target as a target source, and in a magnetron sputtering furnace, at normal temperature of 20 DEG C plus or minus 1 DEG C, in argon atmosphere and magnetic field condition, in a water circulating cooling state and under constant vacuum degree of 1.0Pa, the exchange coupling complex film is prepared by magnetron sputtering, then high temperature annealing is carried out in a vacuum condition, the iron-platinum alloy is phase-changed to ensure a soft magnetic layer and a hard magnetic layer to combine tightly, and the complex film is silver-gray and of the thickness of 55nm, thus reducing the coercive force of the complex film, satisfying the writing field of a magnetic head and increasing the properties of a super-high density magnetic disk. The preparing method has short process flow, does not pollute the environment and is an ideal method for preparing the magnetic recording exchange coupling complex film.

Description

technical field [0001] The invention relates to a method for preparing a magnetic recording exchange coupling composite film, and belongs to the technical field of material structures and preparation methods of magnetic recording information storage devices. Background technique [0002] Magnetic recording is the core technology of information storage. The development of information technology has higher and higher requirements for magnetic recording. Improving the magnetic recording density is the core of information storage. The perpendicular magnetic recording medium film is the key to achieve 1Tbit / in 2 The key technology of ultra-high recording density requires that the perpendicular magnetic recording medium film has a smaller grain size, but the extremely fine grain size of the magnetic grain may produce a superparamagnetic effect, thereby reducing the thermal stability of the dielectric film. To maintain the dielectric film The thermal stability of the magnetocrystal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G11B5/84G11B5/667G11B5/851
Inventor 许小红王芳梁艳张静李小丽江凤仙
Owner 山西师范大学
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap