Anti-infiltration mucilage for rubber coated fabric products

An anti-leakage and product technology, applied in the field of glue, can solve the problems of complex lamination process, difficult to achieve anti-leakage, affecting appearance quality, etc., to reduce equipment and workshop capital investment, reduce energy consumption, The effect of short production cycle

Active Publication Date: 2010-07-28
JIHUA 3517 RUBBER PROD
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, leakage is most likely to occur at the overlapping joints of adhesive tape products during production. The general method to prevent leakage is to stick adhesive strips at the overlapping joints. This method has the following problems: First, there is a certain gradient (step) at the overlapping joints. It makes the adhesive strip not fit firmly, and it is difficult to achieve the real anti-leakage effect
The second is that the rubber strip has a certain thickness (about 1.1mm), which affects wearing and affects the appearance quality
The third is that the process of laminating the rubber strip is complicated. First, the glue should be applied to the rubber cloth and the glue strip separately, and then the glue should be dried before lamination and then vulcanized.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] 1. Ingredients:

[0022] Neoprene 100kg, sulfur 0.2kg, accelerator M0.2kg, accelerator NA-220.2kg, zinc oxide 2kg, magnesium oxide 2kg, paraffin wax 4kg, pine tar 4kg, antioxidant H0.2kg, Vaseline 4kg, engine oil 10kg, high wear-resistant carbon black 20kg, calcium carbonate 40kg, coloring agent 0.5kg.

[0023] 2. Mixing and tableting:

[0024] First wrap the neoprene rubber on the open mill without holes, then add other prepared materials and knead evenly to produce a sheet.

[0025] 3. Beating:

[0026] First add 206kg of butyl acetate into the beater, and then add the prepared mixed film for beating. After the glue is ready (no grains and lumps), add 19 kg of mixed oil of 50% each of butyl acetate and No. 120 solvent gasoline, and adjust the glue concentration to 15 seconds.

[0027] 4. After passing the inspection, make a spare and use it up within 72 hours. When the room temperature is lower than 18°C, the glue must be kept warm, and the heat preservation temp...

Embodiment 2

[0029] 1. Ingredients:

[0030] Neoprene 110kg, sulfur 0.5kg, accelerator M0.5kg, accelerator NA-220.5kg, zinc oxide 5kg, magnesium oxide 4kg, paraffin wax 5kg, pine tar 5kg, antioxidant H0.5kg, Vaseline 5kg, engine oil 12kg, high wear-resistant carbon black 28kg, calcium carbonate 50kg, coloring agent 0.8kg.

[0031] 2. Mixing and tableting:

[0032] First wrap the neoprene rubber on the open mill without holes, then add other prepared materials and knead evenly to produce a sheet.

[0033] 3. Beating:

[0034] First add 249.5 kg of butyl acetate into the beater, and then add the prepared mixed film for beating. After the glue is ready (no grains or lumps), add 68 kg of mixed oil of 50% each of butyl acetate and No. 120 solvent gasoline, and adjust the glue concentration to 13 seconds.

[0035] 4. After passing the inspection, make a spare and use it up within 72 hours. When the room temperature is lower than 18°C, the glue must be kept warm, and the heat preservation te...

Embodiment 3

[0037] 1. Ingredients:

[0038] Neoprene 120kg, sulfur 0.7kg, accelerator M0.7kg, accelerator NA-220.7kg, zinc oxide 7kg, magnesium oxide 6kg, paraffin wax 6kg, pine tar 6kg, antioxidant H0.7kg, Vaseline 6kg, engine oil 15kg, high wear-resistant carbon black 35kg, calcium carbonate 60kg, coloring agent 1.0kg.

[0039] 2. Mixing and tableting:

[0040] First wrap the neoprene rubber on the open mill without holes, then add other prepared materials and knead evenly to produce a sheet.

[0041] 3. Beating:

[0042] First add 291kg of butyl acetate into the beater, and then add the prepared mixed film for beating. After the glue is well laid (without particles and lumps), add 132 kg of mixed oil of 50% each of butyl acetate and No. 120 solvent gasoline, and adjust the glue concentration to 10 seconds.

[0043] 4. After passing the inspection, make a spare and use it up within 72 hours. When the room temperature is lower than 18°C, the glue must be kept warm, and the heat pres...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a mucilage for producing rubber coated fabric products, in particular to an anti-infiltration mucilage for rubber coated fabric products. The mucilage is prepared from the following raw materials in portions by weight: 100-120 portions of neoprene, 0.2-0.7 portion of sulfur, 0.2-0.7 portion of accelerator M, 0.2-0.7 portion of accelerator NA-22, 2-7 portions of zinc oxide, 2-6 portions of magnesium oxide, 4-6 portions of paraffin, 4-6 portions of pine tar, 0.2-0.7 portion of anti-aging agent H, 4-6 portions of vaseline, 10-15 portions of machine oil, 20-35 portions of high abrasion furnace black, 40-60 portions of calcium carbonate and 0.5-1.0 portion of colorant. The mucilage is prepared from the neoprene, and ultra-fast accelerators are used in the formula, so that the mucilage can be naturally vulcanized at room temperature, thereby omitting the high-temperature vulcanizing process in the original process, reducing the investment for equipment and barrack capital and reducing the energy consumption at the same time. When being used for the rubber coated fabric products, the invention has the advantage of favorable anti-infiltration effect and enhanced product percent of pass. The colorant is added into the formula, so that the color of the mucilage is the same as that of the rubber coated fabric products, and the mucilage does not affect the product appearance.

Description

technical field [0001] The invention relates to a glue used in the production of adhesive plaster products, in particular to an anti-leakage glue for adhesive plaster products. Background technique [0002] At present, leakage is most likely to occur at the overlapping joints of adhesive tape products during production. The general method to prevent leakage is to stick adhesive strips at the overlapping joints. This method has the following problems: First, there is a certain gradient (step) at the overlapping joints. It makes the rubber strip not fit firmly, and it is difficult to achieve a real anti-leakage effect. Second, because the rubber strip has a certain thickness (about 1.1mm), it affects wearing and affects the appearance quality. The third is that the process of laminating the rubber strips is complicated. First, glue is applied to the rubber cloth and the rubber strips, and the glue is dried before lamination and then vulcanized. Contents of the invention ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L11/00C08K13/02C08K3/22C08K3/26C08K3/04
Inventor 沈水林李颖王锦良蒋艳峰丁鹏
Owner JIHUA 3517 RUBBER PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap