Method for manufacturing medium-temperature Longquan powder celadon

A manufacturing method and technology of celadon, applied to clay products, other household utensils, household utensils, etc., can solve the problems of high firing temperature, serious environmental pollution, and high production cost of powder celadon, and achieve lower maturation temperature, uniform color, and Enhance the effect of jade texture

Inactive Publication Date: 2012-05-23
JINGDEZHEN CERAMIC UNIV
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to solve the current technical difficulties in the production of powder celadon with excessively high firing temperature, high energy consumption, high production cost and serious environmental pollution, and to provide a medium-temperature firing at 1220-1240°C with a glazed surface. Manufacturing method of longquan powder celadon with uniform color

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The weight percentage of the medium-temperature Longquan powder celadon body is 10% Xingzi kaoling, 80% Guixi porcelain stone, 9.9% potassium feldspar, and 0.1% water glass.

[0020] The weight percent of medium-temperature Longquan powder celadon glaze is 62.9% of potassium feldspar, 12% of purple gold soil, 20% of fly ash, 2% of calcined talc, 3% of calcined zinc oxide, and 0.1% of sodium tripolyphosphate.

[0021] Weigh and mix the raw materials according to the billet formula requirements, put the material: ball: water ratio of 1:2:0.6 into the ball mill equipment for ball milling for 16 hours, pass the slurry through a 100-mesh sieve after aging for 24 hours, and then go through dehydration, mud refining, etc. Process made into mud.

[0022] Weigh and mix the raw materials according to the requirements of the glaze formula, and put them into a ball mill with a ratio of material:ball:water of 1:2:0.6 for 20 hours, and the fineness will reach less than 0.04% on the s...

Embodiment 2

[0026] The formula weight percent of medium-temperature Longquan powder celadon body is 34% of Xingzi Gaoling, 51% of Guixi porcelain stone, 14.8% of potassium feldspar, and 0.2% of water glass.

[0027] The weight percent of the medium temperature Longquan powder celadon glaze is 67.8% of potassium feldspar, 10% of purple gold soil, 15% of fly ash, 3% of calcined talc, 4% of calcined zinc oxide, and 0.2% of sodium tripolyphosphate.

[0028] Weigh and mix the raw materials according to the billet formula requirements, put the material:ball:water ratio of 1:2:0.8 into the ball mill equipment and ball mill for 16 hours, put the slurry stale for 24 hours, pass through a 100-mesh sieve, and then go through dehydration, mud refining, etc. Process made into mud.

[0029] Weigh and mix the raw materials according to the requirements of the glaze formula, and put them into a ball mill with a ratio of material: ball: water of 1:2:0.8 for 20-30 hours, and the fineness will reach less th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for manufacturing medium-temperature Longquan powder celadon. In the method, a green body and a glaze are mixed with common mineral materials and chemical materials in specific ratios, calcined zinc oxide and calcined talcum are added in the glaze, the Longquan powder celadon is fired at 1,220 to 1,240 DEG C at one time, the problems of high production cost, serious environmental pollution and the like, which are caused by high firing temperature and large energy consumption, of the conventional powder celadon production are solved, the jade textural quality of medium-temperature powder greenish glaze is strengthened.

Description

technical field [0001] The invention belongs to the technical field of traditional ceramic manufacturing, and in particular relates to a method for manufacturing medium-temperature Longquan powder celadon, which is suitable for manufacturing various high-grade Longquan powder green porcelain for daily use and art porcelain. Background technique [0002] Longquan powder celadon is one of the famous celadon varieties created and fired in the heyday of the ancient Longquan kiln. It uses iron as the main coloring element, and the glaze is thicker. After entering the kiln, it is fired with a reducing flame. Jade-like texture. Longquan kiln celadon went from strong to weak, and after thousands of years, it declined in the late Qing Dynasty. After liberation, under the care of Premier Zhou Enlai, production was resumed in Shangyang Town, Longquan City. Now it has formed a certain scale and has become one of the largest celadon manufacturing places in China. Although Longquan cela...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/00
Inventor 吴隽李其江张茂林吴军明
Owner JINGDEZHEN CERAMIC UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com