Double anti-wear automobile lubricating oil

A kind of automotive lubricating oil, dual technology, applied in the field of automotive lubricating oil, can solve the problems of insufficient oil film thickness, insufficient simulation, high shear rate, etc., and achieve the effect of extending the oil change period, improving start-up wear, and reducing wear

Active Publication Date: 2011-11-02
QUANZHOU CITY OUMEI LUBRICANT PRODS
View PDF6 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, under high-speed and high-torque conditions, due to the high load of the engine, the oil temperature will be high during long-term operation, and under high-speed operation conditions, the shear rate of the engine oil is high, greater than 10 8 / s, the high temperature and high shear rate of conventional engine oil is generally 150°C, and the shear rate is 10 6 / s, and the bench test and driving test of general engine oil are not enough to simulate this state
The viscosity of lubricating oil becomes smaller at high temperature and high shear rate, which easily leads to insufficient oil film thickness, and in the critical state, the function of some additives does not meet the requirements, resulting in increased wear of friction pairs
In the case of ultra-high torque and extremely high shear rate, the wear of the friction pair still needs to be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Double anti-wear automobile lubricating oil
  • Double anti-wear automobile lubricating oil
  • Double anti-wear automobile lubricating oil

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Add 35-94 mass parts of A in three times, first add 30% of A to the pre-adjusted kettle J, heat to 50 °C at a heating rate of 80-120 °C / hour, add 6.8 mass parts of B, 0.05 mass parts of C and 2 parts by mass of E, and adjust at a constant temperature of 50°C for 30 minutes to form a semi-finished material M; add 40% of A into the production blending kettle L, heat it to 80°C at a heating rate of 80-120°C / hour, and add it while stirring 0.3 parts by mass of G, 1 part by mass of D, 2 parts by mass of F and 5.5 parts by mass of H, stirred for 30 minutes, added the remaining 30% of A, stirred for 30 minutes; put the semi-finished material M into the production blending kettle L, stirred After 40 minutes, take samples for analysis, add 0.005-1 parts by mass of pour point depressant, 10-100 ppm of antifoaming agent and 1-100 ppm of demulsifier according to requirements, and stir for another 30 minutes. Table 1 shows the usage result data of the lubricant composition prepared ...

Embodiment 2

[0028] 35-94 mass parts of A are added in three times. First, 30% of A is added to the pre-adjusted kettle J, heated to 50 °C at a heating rate of 80-120 °C / hour, and 6.8 mass parts of B, 0.1 mass parts of C and 5 parts by mass of E, mixed at a constant temperature of 50°C for 30 minutes to form a semi-finished material M; add 40% of A to the production blending kettle L, heat to 80°C at a heating rate of 80-120°C / hour, and add 0.5 mass Parts of G, 1.5 parts by mass of D, 5 parts by mass of F and 7 parts by mass of H, stirred for 30 minutes, added the remaining 30% of A, stirred for 30 minutes; put the semi-finished material M into the production mixing tank L, stirred for 40 minutes Finally, sampling and analysis, according to the requirements, add 0.005-1 mass parts pour point depressant, 10-100ppm antifoaming agent and 1-100ppm demulsifier, and then stir for 30 minutes. Table 2 shows the usage result data of the lubricant composition prepared in Example 2.

[0029] Table 2...

Embodiment 3

[0033]35-94 mass parts of A are added in three times. First, 30% of A is added to the pre-adjusted kettle J, heated to 50 °C at a heating rate of 80-120 °C / hour, and 6.8 mass parts of B, 0.1 mass parts of C and 8 parts by mass of E are mixed at a constant temperature of 50°C for 30 minutes to form a semi-finished material M; 40% of A is added to the production blending kettle L, heated to 80°C at a heating rate of 80-120°C / hour, and added while stirring 2 parts by mass of D, 5 parts by mass of F and 10 parts by mass of H, stirred for 30 minutes, added the remaining 30% of A, stirred for 30 minutes; put the semi-finished material M into the production blending kettle L, stirred for 40 minutes, and took a sample for analysis , add 0.005-1 parts by mass of pour point depressant, 10-100ppm of antifoaming agent and 1-100ppm of demulsifier according to requirements, and stir for another 30 minutes. Table 3 shows the usage result data of the lubricant composition prepared in Example ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosity indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses double anti-wear automobile lubricating oil. The lubricating oil comprises, by mass, A), 35-94 parts of a low-viscosity base oil having a high viscosity index, B), 2-15 parts of a engine oil composite agent, C), 0.01-3 parts of a organic molybdenum mixture, D), 0.5-5 parts of a saturated and high-viscosity complex lipid, E), 0.5-10 parts of a diester, F), 0.5-10 parts of ahigh-viscosity polyolefin, G), less than or equal to 2 parts of a alcohol blocked phenolic ester having high molecular weight and H) 2-10 parts of a viscosity index improver with high shearing performance. The double anti-wear automobile lubricating oil provided by the present invention is used for engines of the automobiles, such that starting wear of the engine is substantially improved, the wear of the engine in a operation condition of high rotary speed and high torsional moment is reduced. In addition, according to the present invention, a starting noise level is reduced by 12%; an outside noise level is reduced by 6.8% and an interior noise level is reduced by 8.4% during a high-speed operation; a oil change period of the engine oil is prolonged more than one time.

Description

technical field [0001] The invention relates to a lubricant for vehicles, in particular to an anti-wear lubricant for vehicles. Background technique [0002] The general requirement of modern engines is to generate more power under the premise of small size and light weight, as well as more and more stringent energy-saving and environmental protection requirements, resulting in a substantial increase in engine power per liter, while the piston and connecting rod are shortened. The loads on piston rings and cylinder walls, valve lifters and cams, crankshafts and bearing bushes, etc., which have the most severe working conditions, are greatly increased. Conventional lubricating oils are constantly improving in quality to meet the requirements of comprehensive engine lubrication, sludge dispersion and anti-corrosion and anti-wear. For example, the invention patent publication number is CN101838575A "an energy-saving engine oil additive composition", etc., all provide engine oi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C10M169/04C10N40/25C10N30/06
Inventor 吕金水
Owner QUANZHOU CITY OUMEI LUBRICANT PRODS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap