Permanent antistatic PA6/PPO (Polyamide 6/Polyphenylene Oxide) alloy and preparation method thereof

An antistatic and antistatic masterbatch technology, which is applied in the field of permanent antistatic PA6/PPO alloy and its preparation, can solve the problems of low electrical conductivity, etc., and achieve the effects of low cost, small amount of addition, and good heat resistance

Inactive Publication Date: 2013-05-29
SHANGHAI SUNNY
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, PA6 / PPO alloy has good electrical insulation like most polymer materials, and its surface resistivity is generally 10 13 -10 15 Ω·m, the conductivity is much lower than that of metal materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Permanent antistatic PA6/PPO (Polyamide 6/Polyphenylene Oxide) alloy and preparation method thereof
  • Permanent antistatic PA6/PPO (Polyamide 6/Polyphenylene Oxide) alloy and preparation method thereof
  • Permanent antistatic PA6/PPO (Polyamide 6/Polyphenylene Oxide) alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-5

[0030] The raw material formula of embodiment 1-5 is as follows:

[0031]

[0032] Put the above components into a high mixer according to the proportion and mix them for 2-5 minutes, discharge the material, and then use a screw extruder to extrude and granulate. The processing temperature is 150-200°C, and the screw speed is 25-35HZ.

[0033]

[0034] According to the samples prepared in Examples 1-5, the surface resistivity test was carried out for comparison.

[0035] The test performance comparison is shown in the table below:

[0036] project

[0037] Surface resistivity

[0038] The surface resistivity of the permanent antistatic masterbatch prepared according to the above formula and method reaches 10 2 -10 3 Ω·m, can be widely used in modified PA6 / PPO alloy; compared with the prior art, the present invention has long-lasting antistatic effect, small amount of addition but good antistatic effect, little influence on PA6 / PPO alloy performance...

Embodiment 5

[0039] The permanent antistatic masterbatch prepared in Example 5 has the lowest surface resistivity and the highest cost performance.

Embodiment 6-7

[0052] Embodiment 6-7 is permanent antistatic PA6 / PPO alloy and preparation method thereof

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a permanent antistatic master batch and a preparation method thereof. The antistatic master batch comprises the following components in percentage by weight: 1-15 percent of alkali metal salt, 0.5-2 percent of antioxidant, 0.5-2 percent of heat stabilizer, 0-10 percent of assisting antistatic agent and 71-95 percent of polyether block-containing high polymer material, wherein the polyether block-containing high polymer material is a compound consisting of polyethylene glycol oxide and poly(ether ester amide) in the weight ratio 5:1. The preparation method comprises the following steps of: weighing raw materials according to the parts by weight, and putting into a high mixer for mixing for 2-5 minutes; discharging; and extruding and pelletizing with a double screw extruder to obtain the master batch, wherein the processing temperature is 150-200 DEG C, and the number of revolutions of a screw is 25-35 HZ. The invention further relates to a permanent antistatic PA6 / PPO (Polyamide 6 / Polyphenylene Oxide) alloy and a preparation method thereof. The antistatic master batch and the alloy provided by the invention have the advantages of durable antistatic effect, permanent antistatic effect, various colors, low cost and high heat resistance.

Description

technical field [0001] The invention relates to a permanent antistatic masterbatch and a preparation method thereof, and also relates to a permanent antistatic PA6 / PPO alloy and a preparation method thereof. Background technique [0002] Because nylon 6 (PA6) has good comprehensive mechanical properties, high heat resistance, good wear resistance, self-lubrication, good flame retardancy, excellent chemical corrosion resistance, excellent barrier properties and other properties Become the most widely used engineering plastics. Polyphenylene ether (PPO) has the advantages of high rigidity, high heat resistance, good water resistance, flame retardant, high strength and excellent electrical properties. It also has the advantages of wear resistance, non-toxicity, and pollution resistance. Its dielectric constant and Dielectric loss is one of the smallest varieties among engineering plastics, almost not affected by temperature and humidity, and can be used in low, medium and high...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L71/00C08L77/12C08K13/02C08K3/16C08K3/24C08K5/46C08K5/524C08K5/57C08K5/098C08K3/36B29B9/06B29C47/92C08L71/12C08L77/02C08L51/08B29C48/92
CPCB29C48/04B29C48/40B29C48/92B29C2948/9259B29C2948/92704B29C2948/92885B29C2948/92895
Inventor 郭建鹏孟成铭杨涛才勇
Owner SHANGHAI SUNNY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com