Biaxially oriented nylon film (BOPA) matt film and manufacturing method thereof

A technology of matting film and matting layer, which is applied in the direction of chemical instruments and methods, synthetic resin layered products, layered products, etc., can solve the problem of increasing investment cost and production cost, insufficient amount of matting material on the surface of the film, and lack of matting effect and other problems, to achieve the effect of good extinction effect, unique optical properties, and good processing performance

Active Publication Date: 2014-11-19
厦门长塑实业有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

According to this method, the production of BOPA matting film needs to be divided into two steps. First, the ordinary BOPA film is produced, and then the matting material is applied to the surface of the BOPA film with a coating machine to achieve the purpose of matting. However, the production process of this method is cumbersome and the output is low. Increased investment cost and production cost
Moreover, if the amount of matting material applied to the surface of the film is insufficient, the desired matting effect cannot be obtained.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Biaxially oriented nylon film (BOPA) matt film and manufacturing method thereof
  • Biaxially oriented nylon film (BOPA) matt film and manufacturing method thereof
  • Biaxially oriented nylon film (BOPA) matt film and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Such as figure 2 The shown BOPA matting film of three-layer structure composed of surface layer 11, core layer 22 and matting layer 33, the components of the above-mentioned surface layer 11 are by weight percentage 0.6%wt smooth agent and 0.8%wt anti-blocking agent, the rest The components of the film-grade nylon-6 resin; the components of the core layer 22 are all nylon-6 resins; the components of the matting layer 33 are 99%wt matting material and 1%wt smoothing agent.

Embodiment 2

[0028] Such as figure 2 The shown BOPA matting film composed of three-layer structure by the surface layer 11, the core layer 22 and the matting layer 33, the components of the above-mentioned surface layer 11 are by weight percentage 1%wt smooth agent and 1%wt anti-blocking agent, the rest The components of the film-grade nylon-6 resin; the components of the above-mentioned core layer 22 are all nylon-6 resins; the components of the above-mentioned matting layer 33 contain 100%wt matting material and 0%wt smoothing agent by weight percentage .

Embodiment 3

[0030] Such as figure 2 The shown BOPA matting film of three-layer structure is composed of surface layer 11, core layer 22 and matting layer 33. The components of the above-mentioned surface layer 11 are smooth agents of 1%wt by weight, and the remaining components are film-grade nylon- 6 resin; the components of the above-mentioned core layer 22 are all nylon-6 resin; the components of the above-mentioned matting layer 33 are 98.5%wt matting material and 1.5%wt smoothing agent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a BOPA matt film, which has a three-layer structure consisting of a surface layer, a core layer and a matt layer, wherein the surface layer comprises 0 to 1 weight percent of antiblocking agent, 0 to 1 weight percent of slipping agent and the balance of nylon-6 resin; the core layer is nylon-6 resin; the matt layer comprises 98.5 to 100 weight percent of matt material and 0 to 1.5 weight percent of slipping agent; and the three-layer structure of the BOPA matt film is formed by extrusion and bidirectional drawing. The invention also provides a method for manufacturing the BOPA matt film.

Description

Technical field: [0001] The invention relates to a matting film and a manufacturing method thereof, in particular to a biaxially stretched nylon matting film (BOPA matting film for short) and a manufacturing method thereof. Background technique: [0002] BOPA matting film is a fashionable and high-grade composite and packaging material, which can give people a soft, comfortable and hazy visual effect. After being stimulated by sunlight and screens for a long time, people can eliminate eye fatigue when watching books, pictures, color-printed pictures and packaging compounded with matting film. Moreover, BOPA matting film can be used in food packaging (biscuits, dried fruits, tea, cakes, etc.) after compounding to create an image of a natural product. Corona matting film is suitable for printing, lamination, low-temperature bronzing, etc. It is laminated with paper or other substrates after being glued on the glossy surface. It is usually used for surface lamination of books...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B27/06B32B27/34B32B27/18B32B27/16B32B33/00
Inventor 林凤龙梁文东
Owner 厦门长塑实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com