A kind of breathable fish tank and preparation method thereof

A technology for ventilating fish tank and fish tank, which is applied in fish farming, ceramic products, other household appliances, etc., can solve the problems of difficult to achieve anti-seepage and ventilation at the same time, poor air permeability, poor anti-seepage, etc.

Active Publication Date: 2016-04-06
BEIJING RECHSAND SCI & TECH GRP
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the cost of making fish tanks by processing natural stone is very high, and it is not suitable for promotion to ordinary families.
Moreover, among natural stones, stones with sparse textures have poor impermeability, while stones with dense textures have poor air permeability.
That is, it is difficult to meet the requirements of anti-seepage and air permeability at the same time
At present, there is no material with both impermeability and air permeability on the market that can replace stone to make fish tanks

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of breathable fish tank and preparation method thereof
  • A kind of breathable fish tank and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0068] figure 1 For the breathable fish tank of the present invention, the anti-permeation gas fish tank 1 has an open cavity, and the fish tank is covered with pores of 0.002-0.086mm formed between adjacent aggregate particles. The pores can allow gas molecules to pass through smoothly, and the hydrophobic properties of the hydrophobic binder can effectively prevent the penetration of liquid water molecules.

[0069] The aggregate particles are a mixture of quartz sand and slag at a weight ratio of 5:1, the particle size of the quartz sand is 0.02-0.1mm, the particle size of the slag is 0.08-0.15mm, and the hydrophobic binder contains Fluorine epoxy resin binder 2,2-bisphenol-based hexafluoropropane diglycidyl ether, hydrophobic binder and aggregate particles are used at a weight ratio of 1:49.

[0070] Described fish jar 1 is to make by following method:

[0071] a. Mix the aggregate particles with the hydrophobic binder and pour into the mixer to stir evenly;

[0072] ...

Embodiment 2

[0076] The air-permeable fish tank in this embodiment has an open cavity, and the fish tank is covered with pores of 0.003-0.065mm formed between adjacent aggregate particles. The pores within this size range can allow gas molecules to pass through smoothly, and It can effectively prevent the penetration of liquid water molecules.

[0077] The aggregate particles are formed by mixing ceramsite and glass microspheres at a weight ratio of 3:1, the particle diameter of the ceramsite is 0.01-0.075mm, and the particle diameter of the glass microspheres is 0.04-0.08mm.

[0078] The hydrophobic binder is a silicon-containing epoxy resin binder diphenylsilane modified bisphenol A epoxy resin, and the hydrophobic binder and aggregate particles are used in a weight ratio of 3:97.

[0079] The aggregate particles are coated with hydrophobic epoxy resin, and the hydrophobic epoxy resin is 2wt% of the aggregate particles. The hydrophobic epoxy resin is a mixture of polyamide resin modifie...

Embodiment 3

[0090] figure 1 It is a ventilating fish tank in this embodiment, which is a cavity with an opening formed by four side walls, front, rear, left, and right sides and a bottom wall, wherein the front side wall is made of transparent glass. The rest of the side wall and the bottom wall of the fish tank are covered with pores of 0.002-0.086 mm formed between adjacent aggregate particles. The pores within this size range can allow gas molecules to pass through smoothly, and can effectively prevent liquid water molecules. through.

[0091] The aggregate particles are formed by mixing ceramsite and quartz sand at a weight ratio of 1:3, the particle size of the ceramsite is 0.02-0.045mm, and the particle size of the quartz sand is 0.015-0.1mm.

[0092] The hydrophobic binder is a silicone binder methylphenylpolysiloxane resin, and the hydrophobic binder and aggregate particles are used in a weight ratio of 3:97.

[0093] The aggregate particles are coated with hydrophobic polytetr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
pore sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a breathable fish tank. The fish tank has an open cavity. The fish tank is formed by bonding aggregate particles coated with hydrophobic substances and a hydrophobic binder. The adjacent bones Pores are formed between the material particles through which gas molecules can pass and liquid water molecules under high pressure cannot pass through. The pore diameter of the pores is 0.002~0.086mm. The invention simultaneously discloses a preparation method of the fish tank. The fish tank effectively solves the problem that the existing common fish tank cannot have both anti-seepage and air permeability. The invention has low cost, simple manufacture and simple appearance, and is suitable for various places suitable for fish farming.

Description

technical field [0001] The invention relates to a fish tank, in particular to a breathable fish tank. Background technique [0002] At present, various fish tanks are made of glass, ceramics, plastics and other materials on the market, providing consumers with a variety of choices, but the fish tanks made of these materials have no ventilation effect. If fresh water is not replaced in time to ensure sufficient oxygen, water Goldfish are hard to survive. [0003] In order to solve the above problems, Chinese patent CN101422138A discloses a fish tank, which is provided with a fountain in the fish tank, which can not only watch but also increase oxygen. It consists of a fish tank, a switch, a small water pump, a transparent pipe, and a power cord. It is characterized in that the switch is on the wall of the fish tank, the small water pump is at the bottom of the fish tank, the transparent pipe is set in the center of the fish tank and connected to the small water pump, and the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B38/00C04B26/10C04B14/02C04B20/10A01K63/00
Inventor 秦升益贾屹海陈杰陈晓羽
Owner BEIJING RECHSAND SCI & TECH GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap