Process for manufacturing antibacterial and abrasion-resistant lace from apocynum venetum fibers

Abstract

The invention relates to a process for manufacturing antibacterial and abrasion-resistant lace from apocynum venetum fibers. The process has the advantages that after a special design for fiber preprocessing, yarn spinning, lace forming and weaving and low-temperature heating post-processing and special optimization for relevant parameters, technical difficult problems that large quantities of chemical antibacterial agents are used in the prior art, damage environments and injure users, and laces are not graceful, are hardened and stiff, and are complicated in pattern, troublesome in process, high in production cost and difficult to popularize are solved, characteristics of fabrics made from natural fibers can be kept, and excellent technical effects such as graceful style, lightness, thinness and breathability of the lace are realized.

Description

technical field

[0001] The invention relates to the technical field of lace, in particular to a preparation process of lace, more specifically to a preparation process of antibacterial and wear-resistant apocynum fiber lace. Background technique

[0002] In the past two decades, lace fabrics have been fashionable, luxurious, graceful and elegant, and are very popular among women. However, traditional lace fabrics are light and thin, and are often only suitable for spring and summer fashion, not for autumn and winter fashion. The market is very restricted.

[0003] Bubble lace is invented from the inspiration of seersucker in woven fabrics. It makes the original ordinary and single lace fabric have a special fabric surface effect similar to bubbles, showing the lovely side of lace fabric, and at the same time has a stronger three-dimensional Sensation, wearing not close to the body and so on.

[0004] The previous bubble lace was formed by chemical action, using the princip...

Examples

Embodiment 1

[0039] A kind of preparation technology of the lace lace of antibacterial wear-resisting polyester linen fiber, it is characterized in that, the preparation technology of the lace lace of described antibacterial wear-resisting apocynum fiber comprises the following steps successively: fiber pretreatment, worsted yarn, lace forming weaving and After low temperature heating.

Embodiment 2

[0041] A kind of preparation technology of the lace lace of antibacterial wear-resisting polyester linen fiber, it is characterized in that, the preparation technology of the lace lace of described antibacterial wear-resisting apocynum fiber comprises the following steps successively: fiber pretreatment, worsted yarn, lace forming weaving and Low-temperature heating post-treatment; fiber pretreatment steps: first, select apocynum fiber, flax fiber, nettle fiber, and polyester fiber as fiber raw materials according to the weight ratio of 1:2:1:7; wherein, the above-mentioned polyester fiber spinning process The antibacterial masterbatch is added to the polyester fiber, and the antibacterial masterbatch accounts for 0.8 to 0.95% of the total weight of the polyester fiber. The antibacterial masterbatch is made of silver-loaded composite inorganic antibacterial powder, surfactants, and antioxidants. The weight percentages are respectively It is 0.5-0.8%, 2-3%, and the balance; the ...

Embodiment 3

[0046] A kind of preparation technology of the lace lace of antibacterial wear-resisting polyester linen fiber, it is characterized in that, the preparation technology of the lace lace of described antibacterial wear-resisting apocynum fiber comprises the following steps successively: fiber pretreatment, worsted yarn, lace forming weaving and Low-temperature heating post-treatment; fiber pretreatment steps: first, select apocynum fiber, flax fiber, nettle fiber, and polyester fiber as fiber raw materials according to the weight ratio of 1:2:1:7; wherein, the above-mentioned polyester fiber spinning process The antibacterial masterbatch is added to the polyester fiber, and the antibacterial masterbatch accounts for 0.8 to 0.95% of the total weight of the polyester fiber. The antibacterial masterbatch is made of silver-loaded composite inorganic antibacterial powder, surfactants, and antioxidants. The weight percentages are respectively It is 0.5-0.8%, 2-3%, and the balance; the ...

technical field

[0001] The invention relates to the technical field of lace, in particular to a preparation process of lace, more specifically to a preparation process of antibacterial and wear-resistant apocynum fiber lace. Background technique

[0002] In the past two decades, lace fabrics have been fashionable, luxurious, graceful and elegant, and are very popular among women. However, traditional lace fabrics are light and thin, and are often only suitable for spring and summer fashion, not for autumn and winter fashion. The market is very restricted.

[0003] Bubble lace is invented from the inspiration of seersucker in woven fabrics. It makes the original ordinary and single lace fabric have a special fabric surface effect similar to bubbles, showing the lovely side of lace fabric, and at the same time has a stronger three-dimensional Sensation, wearing not close to the body and so on.

[0004] The previous bubble lace was formed by chemical action, using the princip...

Examples

Embodiment 1

[0039] A kind of preparation technology of the lace lace of antibacterial wear-resisting polyester linen fiber, it is characterized in that, the preparation technology of the lace lace of described antibacterial wear-resisting apocynum fiber comprises the following steps successively: fiber pretreatment, worsted yarn, lace forming weaving and After low temperature heating.

Embodiment 2

[0041] A kind of preparation technology of the lace lace of antibacterial wear-resisting polyester linen fiber, it is characterized in that, the preparation technology of the lace lace of described antibacterial wear-resisting apocynum fiber comprises the following steps successively: fiber pretreatment, worsted yarn, lace forming weaving and Low-temperature heating post-treatment; fiber pretreatment steps: first, select apocynum fiber, flax fiber, nettle fiber, and polyester fiber as fiber raw materials according to the weight ratio of 1:2:1:7; wherein, the above-mentioned polyester fiber spinning process The antibacterial masterbatch is added to the polyester fiber, and the antibacterial masterbatch accounts for 0.8 to 0.95% of the total weight of the polyester fiber. The antibacterial masterbatch is made of silver-loaded composite inorganic antibacterial powder, surfactants, and antioxidants. The weight percentages are respectively It is 0.5-0.8%, 2-3%, and the balance; the ...

Embodiment 3

[0046] A kind of preparation technology of the lace lace of antibacterial wear-resisting polyester linen fiber, it is characterized in that, the preparation technology of the lace lace of described antibacterial wear-resisting apocynum fiber comprises the following steps successively: fiber pretreatment, worsted yarn, lace forming weaving and Low-temperature heating post-treatment; fiber pretreatment steps: first, select apocynum fiber, flax fiber, nettle fiber, and polyester fiber as fiber raw materials according to the weight ratio of 1:2:1:7; wherein, the above-mentioned polyester fiber spinning process The antibacterial masterbatch is added to the polyester fiber, and the antibacterial masterbatch accounts for 0.8 to 0.95% of the total weight of the polyester fiber. The antibacterial masterbatch is made of silver-loaded composite inorganic antibacterial powder, surfactants, and antioxidants. The weight percentages are respectively It is 0.5-0.8%, 2-3%, and the balance; the ...