Preparing method for silver-plated fibers

A silver-plated fiber and fiber technology, which is applied in fiber treatment, biochemical fiber treatment, textiles and papermaking, etc., can solve the problems of insufficient bonding force between the silver plating layer and the substrate fiber, and achieve excellent conductivity and antibacterial properties, not easy to peel off, Effect of increasing surface roughness

Inactive Publication Date: 2016-07-06
SHANGHAI AOMI NEW MATERIAL TECH CO LTD
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of the deficiencies in the prior art, the purpose of the present invention is to provide a method for preparing silver-plated fibers, which solves the defect that the bonding force between the silver coating and the base fiber in the existing silver-plated fibers is not enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparing method for silver-plated fibers

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A kind of preparation method concrete process of silver-plated fiber is as follows:

[0022] In the first step, the polyester fiber is immersed in 5g / L sodium hydroxide aqueous solution, stirred and reacted at 130°C for 60 minutes, taken out, and rinsed with deionized water.

[0023] In the second step, immerse the fiber obtained in the first step into 10 g / L tin dichloride aqueous solution, take it out after soaking at room temperature for 2 minutes, and rinse it with deionized water.

[0024] In the third step, immerse the polyester fiber gained in the second step activation treatment in the silver salt solution, the composition of the silver salt solution is: silver nitrate 3g / L, ammoniacal liquor 3.5mL / L, formalin 1.3mL / L; 20- After stirring and reacting at 30°C for 180 minutes, take it out and rinse it with hot water.

[0025] Tests show that this silver-plated fiber has excellent antibacterial effect, and the antibacterial rate against Staphylococcus aureus is gr...

Embodiment 2

[0027] In the first step, the polyester fiber is immersed in 10g / L potassium hydroxide aqueous solution, stirred and reacted at 120°C for 90 minutes, taken out, and rinsed with deionized water.

[0028] In the second step, the fibers treated in the first step are immersed in 10 g / L tin dichloride aqueous solution, soaked at room temperature for 2 minutes, taken out, and rinsed with deionized water.

[0029] The 3rd step, the terylene fiber that second step activation process is immersed in the silver salt solution, the composition of this silver salt solution is: silver nitrate 7.5g / L, ammoniacal liquor 8.7mL / L, formalin 3mL / L; 20 Take it out after stirring and reacting at -30°C for 180 minutes, and rinse it with hot water.

[0030] Tests show that this silver-plated fiber has excellent antibacterial effect, and the antibacterial rate against Staphylococcus aureus is greater than 99.9%. It retains the characteristics of the original fiber, feels soft, and the plating layer is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of silver-plated fiber, which comprises the following steps: the first step: chemical modification treatment on the surface of the substrate to increase the active groups and roughness on the surface of the substrate fiber; the second step: activation treatment, Active points are directly introduced into the surface of the substrate fiber; the third step: electroless silver plating treatment, a layer of silver is plated on the surface of the substrate fiber. The silver-plated polyester fiber prepared by the invention has good electrical conductivity and excellent antibacterial property, retains the characteristics of the original fiber, has soft hand feeling, and the plating layer is not easy to peel off.

Description

technical field [0001] The present invention relates to a kind of preparation method of material, more specifically, it relates to a kind of preparation method of silver-plated fiber. Background technique [0002] It is well known that silver has the best electrical conductivity among all metals. In addition, metallic silver also has an excellent broad-spectrum antibacterial effect, and its chemical properties are stable and harmless to the human body. In view of these characteristics of metallic silver, silver-plated fibers are widely used in daily life, for example, electromagnetic shielding fabrics, antibacterial and deodorant fabrics, etc. [0003] The production process of silver-plated fiber can be roughly divided into chemical plating and vacuum coating. Vacuum coating is not suitable for large-scale industrial production because it requires special equipment. In the electroless plating process, in order to ensure that the silver layer can be plated on the surface o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M11/83D06M11/38D06M11/76D06M11/20D06M101/32
CPCD06M11/83D06M11/20D06M11/38D06M16/00D06M2101/32
Inventor 杨所平
Owner SHANGHAI AOMI NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap