Preparation method of elastic memory alloy material for spectacle frame

A technology of alloy materials and spectacle frames, which is applied in the field of preparation of elastic memory alloy materials for spectacle frames, can solve the problems that spectacle frames cannot meet the requirements, and achieve the effects of changing the shape of inclusions, moderate cost, and excellent elastic memory performance

Active Publication Date: 2013-04-24
浙江极铝科技有限公司
View PDF8 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In summary, the above-mentioned various spectacle frames reported in the prior art all have defects of one kind or another. With the improvement of people's living standards, people increasingly require decorative and better performance of the spectacle frames. can not meet the requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A preparation method of an elastic memory alloy material for spectacle frames, the chemical composition of the alloy material consists of the following components in weight percentage: Zr 10%, Nb 8%, Al 11%, Cu 6%, Mg 5%, Zn 4%, Ag 1%, Ce 1.5%, O ≤ 0.05%, N ≤ 0.01%, H ≤ 0.02%, and the balance is Ti and unavoidable impurities. The preparation method includes the following preparation methods:

[0022] 1) Melting and pouring: put metal ingots, intermediate alloys and other raw materials into the induction furnace to melt according to the above ratio. After the melt is uniform, test and adjust the composition to make it meet the above range. The heat is 35°C, and it is poured into a copper water-cooled crystallizer for continuous casting, and the casting speed is controlled to be 0.5 m / min to obtain a continuous casting billet, which is a 50×50mm square billet;

[0023] 2) Hot rolling: heat the continuous casting slab to 980°C, keep it warm for 25 minutes, and then roll it...

Embodiment 2

[0027] A method for preparing an elastic memory alloy material for spectacle frames. The chemical composition of the alloy material consists of the following components in weight percentage: Zr 12%, Nb 6%, Al 13%, Cu 4%, Mg 7%, Zn 2%, Ag 2%, Ce 0.5%, O ≤ 0.05%, N ≤ 0.01%, H ≤ 0.02%, and the balance is Ti and unavoidable impurities. The preparation method includes the following preparation methods:

[0028] 1) Melting and pouring: put metal ingots, intermediate alloys and other raw materials into the induction furnace to melt according to the above ratio. After the melt is uniform, test and adjust the composition to make it meet the above range. The heat is 45°C, and it is poured into a copper water-cooled crystallizer for continuous casting, and the casting speed is controlled to be 0.3 m / min to obtain a continuous casting billet, which is a 50×50mm square billet;

[0029] 2) Hot rolling: heat the continuous casting slab to 1020°C, keep it warm for 15 minutes, and then roll it...

Embodiment 3

[0033] A preparation method of an elastic memory alloy material for spectacle frames, the chemical composition of the alloy material is composed of the following components in weight percentage: Zr 11%, Nb 7%, Al 12%, Cu 5%, Mg 6%, Zn 3%, Ag 1.5%, Ce 1.0%, O ≤ 0.05%, N ≤ 0.01%, H ≤ 0.02%, and the balance is Ti and unavoidable impurities. The preparation method includes the following preparation methods:

[0034] 1) Smelting and pouring: put metal ingots, intermediate alloys and other raw materials into the induction furnace to melt according to the above ratio. After the melt is uniform, test and adjust the composition to make it meet the above range. The heat is about 40°C, and it is poured into a copper water-cooled crystallizer for continuous casting, and the casting speed is controlled at 0.4 m / min to obtain a continuous casting billet, which is a 50×50mm square billet;

[0035] 2) Hot rolling: heat the continuous casting slab to 1000°C, keep it warm for 20 minutes, and th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of an elastic memory alloy material for a spectacle frame. The alloy material can comprise the following chemical components in percentage by weight: 10-12% of Zr, 6-8% of Nb, 11-13% of Al, 4-6% of Cu, 5-7% of Mg, 2-4% of Zn, 1-2% of Ag, 0.5-1.5% of Ce, no less than 0.05% of O, no less than 0.01% of N, no less than 0.02% of H and the balance of Ti and inevitable impurities; and the preparation method comprises the following steps: (1), melting and casting; (2), hot rolling: heating a continuous casting blank to about 980-1020 DEG C, preserving the heat of the continuous casting blank for about 15-25 minutes, and then rolling the continuous casting blank and obtaining a 10X10 mm wire after rolling, wherein the final rolling temperature is substantially 860 DEG C; (3), cold pulling; and (4), heat treatment: heating the cold-pulled material to about 260-280 DEG C and preserving the heat of the cold-pulled material for 4-6 minutes.

Description

technical field [0001] The invention relates to the technical field of alloy materials, in particular to a method for preparing an elastic memory alloy material for spectacle frames. Background technique [0002] The traditional spectacle frame material uses BZN15-20, which is widely used in spectacle manufacturing because of its excellent craftsmanship and performance, but its nickel content is as high as 13.5-16.5%, which increases the cost. In order to reduce the cost, CN101967580A A lens construction material is disclosed which has reduced nickel content to 7-9%. However, because Ni element can cause allergic reaction and carcinogenicity to some people, the above-mentioned patent application still containing nickel element cannot overcome this problem. [0003] In addition, the existing spectacle frame materials are simple in composition and poor in corrosion resistance. After a general spectacle frame is used for 3-6 months, it will become old and black due to the corr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C14/00C22C1/03C22F1/18
Inventor 韩晓春
Owner 浙江极铝科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com