Photosensitive composition containing acridine oxide

A technology of photosensitive composition and oxide, which is applied in the field of light curing, can solve the problems of large amount of addition and poor deep curing, and achieve the effects of reducing odor, simple preparation process, high surface curing and deep curing performance

Inactive Publication Date: 2013-04-24
HANGZHOU INST OF ADVANCED MATERIAL BEIJING UNIV OF CHEM TECH
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] During the use of α-hydroxy ketones, there are problems of poor deep curing due to short ultraviolet absorpt

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Photosensitive composition containing acridine oxide
  • Photosensitive composition containing acridine oxide
  • Photosensitive composition containing acridine oxide

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Composition ratio:

[0024] Epoxy acrylic resin 60g;

[0025] 1,6-hexanediol diacrylate 25g;

[0026] Structural formula (I) compound 2g;

[0027] Dacocur1173 3g;

[0028] Leveling agent 0.05g;

[0029] The preparation process of the composition is as follows: add 2g of the compound of structural formula (I), 3g of Dacocur1173, 60g of epoxy acrylic resin, 25g of 1,6-hexanediol diacrylate, and 0.05g of leveling agent into a glass flask equipped with stirring . Stir at room temperature until the material is uniform to obtain the composition.

Embodiment 2

[0031] Composition ratio:

[0032] Epoxy acrylic resin 60g;

[0033] 1,6-hexanediol diacrylate 25g;

[0034] Structural formula (Ⅲ) compound 1g;

[0035] Dacocur184 4g;

[0036] Leveling agent 0.05g;

[0037] Composition preparation: with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of light curing, concretely to a photosensitive composition containing acridine oxide. The composition comprises 1-3 mass parts of the acridine oxide, 1-6 mass parts of Dacocur1173, Dacocur184 or a mixture of both, 10-80 mass parts of ethene unsaturated compound monomer and 10-80 mass parts of ethene unsaturated compound prepolymer. The invention provides the composition containing the acridine oxide together with an alpha-hydroxy ketone photoinitiator; and the composition has relatively high surface-curing and deep-curing performances and high photosensitive activity, can reduce use of the alpha-hydroxy ketone compound and therefore reduce odor resistance, is simple in preparation technology, and can substitute traditional photoinitiators and be used in light-curing formulas.

Description

technical field [0001] The invention relates to the field of photocuring technology, in particular to a photosensitive composition containing acridine oxides. Background technique [0002] UV curing refers to the curing process of monomer, oligomer or polymer matrix induced by ultraviolet light. This technology is widely used in modern microelectronics technology. The photocurable composition in the UV curing system is mainly composed of single It consists of three parts: body, prepolymer and photoinitiator, among which photoinitiator is the most important factor affecting the photosensitive performance of photocurable composition. [0003] The photoinitiators often used in this field are α-hydroxy ketones, representative commercial products Dacocur1173 (2-hydroxy-2-methyl-1-phenylpropan-1 ketone) and Dacocur184 (2-hydroxy-1 -phenylcyclohexyl-1 ketone) are frequently used photoinitiators, and their structural formula is shown below: [0004] [0005] During the use of α...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G03F7/027G03F7/004
Inventor 宋国强胡春青李川
Owner HANGZHOU INST OF ADVANCED MATERIAL BEIJING UNIV OF CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap