Steel bridge deck pavement cold mixing maintenance material and manufacturing method thereof

A steel bridge deck and pavement technology, which is applied to bridges, bridge parts, bridge maintenance, etc., can solve problems such as steel bridge deck pavement and maintenance problems, achieve convenient and simple construction, and improve interlayer bonding strength , The effect of convenient construction

Active Publication Date: 2015-03-25
江苏苏科建设项目管理有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, for the maintenance project of steel bridge deck pavement, the high-temperature mixing epoxy asphalt pavement technology was adopted early in China, and the high-temperature mixing epoxy asphalt concrete has very strict requirements on the construction temperature and time, which is limited to relatively low temperature. High spring and summer construction, and the concrete curing time is as long as about 10 days. At the same time, large mixing equipment and special cementing material adding equipment need to be erected near the construction site, which still cannot solve the problem of steel bridge deck pavement maintenance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Steel bridge deck pavement cold mixing maintenance material and manufacturing method thereof
  • Steel bridge deck pavement cold mixing maintenance material and manufacturing method thereof
  • Steel bridge deck pavement cold mixing maintenance material and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] Take 30 parts of 618 bisphenol A epoxy resin, 8 parts of CYH-277 reactive epoxy toughening agent, and 1 part of epoxy reactive diluent, mix and stir evenly to obtain a mixture of type A, take 60 parts of 203 modified amine curing agent 1 part, 1 part of DMP-30 curing accelerator, 2 parts of KH-550 organosiloxane coupling agent, mix and stir evenly to obtain a mixture of type B, and prepare the mixture of A and B according to the weight ratio of 5:1 , and then stir and mix the prepared resin, according to 0.6~0.9kg / m 2 The dosage is coated on the steel plate in the pit and the four walls of the pit, and at the same time, the basalt gravel with a particle size of 2.36-4.75mm is spread on the surface of the resin, and the dosage is 2-2.5kg / m 2 , forming a resin gravel waterproof layer;

[0056] Thereafter, take the above-mentioned prepared resin and apply it to the cured resin gravel waterproof layer and the surrounding seam area that will be in contact with the resin con...

Embodiment 2

[0059] Take 40 parts of 618 bisphenol A epoxy resin, 6 parts of CYH-277 reactive epoxy toughening agent, and 3 parts of epoxy reactive diluent, mix and stir evenly to obtain a mixture of type A, take 80 parts of 203 modified amine curing agent 2 parts, 2 parts of DMP-30 curing accelerator, 3 parts of KH-550 organosiloxane coupling agent, mixed and stirred evenly to obtain a mixture of type B, and the mixtures of A and B were prepared in a weight ratio of 5:1 , and then stir and mix the prepared resin, according to 0.6~0.9kg / m 2 The dosage is coated on the steel plate in the pit and the four walls of the pit, and at the same time, the basalt gravel with a particle size of 2.36-4.75mm is spread on the surface of the resin, and the dosage is 2-2.5kg / m 2 , forming a resin gravel waterproof layer;

[0060] Thereafter, take the above-mentioned prepared resin and apply it to the cured resin gravel waterproof layer and the surrounding seam area that will be in contact with the resin ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a steel bridge deck pavement cold mixing maintenance material and a manufacturing method thereof. The maintenance material comprises a resin detritus waterproof layer, a resin bonding layer and a resin concrete pavement layer. The resin detritus waterproof layer is coated on a steel bridge panel required maintenance and is formed by solidifying resin and detritus spread on the surface of the resin. The resin bonding layer is coated on the resin detritus waterproof layer. The resin concrete pavement layer is coated on the resin bonding layer and is formed by solidifying the resin and aggregate in a mixed mode. According to the maintenance material, construction is convenient, influence on construction conditions by temperature is small, performance is excellent, maintenance time is short, production is convenient and rapid, construction period is short and influence on traffic is small.

Description

technical field [0001] The invention belongs to the field of building materials, and in particular relates to a steel bridge deck pavement cold-mix curing material and a preparation method thereof. Background technique [0002] At present, the mainstream steel bridge deck pavement technology in China is mainly epoxy asphalt concrete and cast asphalt concrete pavement technology. The pavement of steel bridge decks has always been a worldwide problem, and its service life is shorter than that of ordinary pavements, especially under domestic use conditions, and some serious diseases begin to appear in the second year of use. For example, the Jiangyin Bridge was paved with poured asphalt concrete, and defects such as rutting and cracks began to appear in the second year; the Runyang Bridge was paved with epoxy asphalt technology, opened to traffic in 2005, and entered the stage of frequent maintenance in 2007. [0003] However, after the pouring asphalt concrete and epoxy aspha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): E01D19/12E01C7/32E01D22/00C08L63/02C09J163/02
Inventor 张志祥张辉潘友强张健李晖吴钊朱雷
Owner 江苏苏科建设项目管理有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products