A kind of high-performance emulsion type water-based coding ink for polyethylene and preparation method thereof

A polyethylene, high-performance technology, applied in the field of high-performance emulsion-type water-based inkjet ink, can solve the problems of low adhesion, environmental protection, ink reduction, etc., and achieve the effect of stable system performance, good adhesion, and cost reduction

Active Publication Date: 2015-08-19
河北慧彩油墨科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The adhesion of this ink on the surface of polyethylene and polypropylene materials is quite small, the adhesion fastness is very poor, and the organic solvent is used in the formulation, which has negative effects on human health and the environment
The Chinese invention patent application with the application number 03116083.2 discloses a coding ink formula using acrylic resin as the binder, which also has the defect of poor adhesion fastness on the surface of PE materials, and the ink solvents are all non-environmentally friendly organic materials. solvent
[0003] An effective way to reduce the volatile organic compounds of the ink is to make the ink water-based. However, there is currently no water-based inkjet ink that can obtain better adhesion on the surface of PE materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-performance emulsion type water-based coding ink for polyethylene and preparation method thereof
  • A kind of high-performance emulsion type water-based coding ink for polyethylene and preparation method thereof
  • A kind of high-performance emulsion type water-based coding ink for polyethylene and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A high-performance emulsion type water-based inkjet ink for polyethylene, its raw material formula is as follows by weight:

[0030]

[0031] Preparation:

[0032] According to the above raw material ratio, weigh 6 parts by weight of highly chlorinated modified polyethylene resin, put it into 20 parts of butanone, stir at room temperature until the resin is completely dissolved, and obtain solution A. At the same time, dissolve 1 part of Tween-20 with 50 parts of water to obtain solution B. Dissolve 2 parts of water-soluble dye reduction direct black RB with 19 parts of water to obtain solution C. Under the stirring condition that the stirring speed is not lower than 1000RPM, slowly drop the solution A into the solution B for emulsification, and continuously stir vigorously for 4~10h. Finally, add 1 part of dibutyl phthalate, 1 part of dimethylamine hydrochloride and solution C in sequence, and stir well at room temperature to prepare a high-performance emulsion-ty...

Embodiment 2

[0035] A high-performance emulsion-type water-based inkjet ink for polyethylene, its raw material formula is as follows by weight:

[0036]

[0037] Preparation:

[0038] According to the above raw material ratio, weigh 5 parts of chlorosulfonated polyethylene resin, put it into 25 parts of butanone, stir at room temperature until the resin is completely dissolved, and obtain solution A. At the same time, dissolve 0.5 part of Tween-60 and 1 part of Span-40 with 50 parts of water to obtain solution B. Dissolve 1.5 parts of water-soluble dye Direct Black 168 with 15 parts of water to obtain solution C. Under the stirring condition that the stirring speed is not lower than 1000RPM, slowly drop the solution A into the solution B for emulsification, and continuously stir vigorously for 4~10h. Finally, 1 part of dibutyl phthalate, 1 part of tetrabutylammonium bromide and solution C were added in sequence, and stirred thoroughly at room temperature to obtain a high-performance e...

Embodiment 3

[0041] A high-performance emulsion-type water-based inkjet ink for polyethylene, its raw material formula is as follows by weight:

[0042]

[0043] Preparation:

[0044]According to the above raw material ratio, weigh 6 parts of maleic anhydride graft-modified polyethylene resin, put it into 20 parts of methyl ethyl ketone, stir at room temperature until the resin is completely dissolved, and obtain solution A. At the same time, dissolve 0.5 part of Tween-80, 1 part of Span-60 and 0.5 part of OP-10 with 50 parts of water to obtain solution B. Solution C was obtained by dissolving 2 parts of water-soluble dye C.I. Direct Black 62 with 17 parts of water. Under the stirring condition that the stirring speed is not lower than 1000RPM, slowly drop the solution A into the solution B for emulsification, and continuously stir vigorously for 4~10h. Finally, 1.5 parts of dibutyl phthalate, 1.5 parts of tetrabutylammonium bromide and solution C were added in sequence, and stirred t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
adhesivityaaaaaaaaaa
adhesivityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-performance emulsion type water-based code-spraying printing ink for polyethylene, which is prepared from the following components in parts by weight: 5-10 parts of modified polyethylene resin, 10-40 parts of butanone, 1-5 parts of a water-soluble dye, 0.5-2 parts of a conductivity improver, 0.5-2.5 parts of a plasticizer, 0.5-5 parts of an emulsifying agent, and 40-90 parts of water. According to the invention, through selecting an appropriate connecting material and an additive matched with the connecting material, the adhesion property of the code-spraying printing ink on a PE material in the process of spray printing is better, the system performance is stable, and prints are clear; and in addition, the utilization of organic solvents is completely abandoned in an code-spraying printing ink formulation disclosed by the invention, thereby greatly reducing the harm of the code-spraying printing ink to the human body and the environment in the processes of preparation and utilization.

Description

technical field [0001] The invention relates to a high-performance emulsion-type water-based inkjet ink for polyethylene, in particular to an inkjet ink with water as a solvent, which has excellent adhesion when applied on the surface of polyethylene materials. Background technique [0002] As human society pays more and more attention to the safety issues of food, medicine and cosmetics, many countries clearly require that the labels or other packaging of food, medicine and cosmetics must be printed with information such as production date, batch number and shelf life, so that the spray Code inks are widely used. According to relevant market analysis and statistics, in the film products used for packaging food, medicine and cosmetics at home and abroad, the proportion of polyethylene materials has reached as high as 1 / 4, and the usage rate is increasing year by year. However, most of the inkjet inks currently on the market are only suitable for printing on the surface of s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D11/30
Inventor 周勤玲张才合
Owner 河北慧彩油墨科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com