Method for preparing ptfe ultrafine powder by combining electron beam with ozone and hydrogen peroxide

A technology of hydrogen peroxide and superfine powder, applied in the chemical industry, can solve the problems of high production cost and increase production cost, and achieve the effects of stable product performance, easy control and strong practicability

Inactive Publication Date: 2015-10-28
佛山市顺德区顺泰昌粉末五金塑料有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] However, the production cost of irradiation with electron beam and Co-60 gamma ray radiation equipment is very high, and the need for high standards of safety protection further increases the production cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A kind of method that electron beam combines ozone and hydrogen peroxide to prepare PTFE superfine powder, comprises the steps:

[0045] 1) Pack the dried PTFE raw material in a low-temperature resistant container, put it in liquid nitrogen, and take it out after quenching;

[0046] 2) Grinding the polytetrafluoroethylene raw material after the quenching treatment with a pulverizer, and the particle size after pulverization is 100-1000 μm;

[0047] 3) Put the pulverized polytetrafluoroethylene raw material into the sealed cavity on the circulating trolley of the electron accelerator;

[0048] 4) Seal the electron accelerator, and open the air intake mechanism, and pass ozone on the surface of the polytetrafluoroethylene on the circulating trolley, and the weight ratio of the introduced ozone to the polytetrafluoroethylene raw material in the tray is 0.3%;

[0049] 5) Turn on the electron accelerator, which generates high-energy electron beams to irradiate the PTFE raw...

Embodiment 2

[0053] A kind of method that electron beam combines ozone and hydrogen peroxide to prepare PTFE superfine powder, comprises the steps:

[0054] 1) Pack the dry polytetrafluoroethylene raw material in a low-temperature-resistant container, place it in liquid nitrogen, and take it out after quenching;

[0055] 2) Grinding the PTFE raw material after quenching treatment with a pulverizer, the particle size after pulverization is 100-1000 μm;

[0056] 3) Place the pulverized polytetrafluoroethylene raw material in the sealed cavity on the circulating trolley of the electron accelerator;

[0057] 4) Turn on the spraying device, and the spraying device sprays hydrogen peroxide on the polytetrafluoroethylene raw material on the circulating trolley, and the weight ratio of the sprayed hydrogen peroxide to the polytetrafluoroethylene raw material on the circulating trolley is 5%;

[0058] 5) Turn on the electron accelerator, which generates high-energy electron beams to irradiate the...

Embodiment 3

[0062] A kind of method that electron beam combines ozone and hydrogen peroxide to prepare PTFE superfine powder, comprises the steps:

[0063] 1) Pack the dried PTFE raw material in a low-temperature resistant container, put it in liquid nitrogen, and take it out after quenching;

[0064] 2) Grinding the polytetrafluoroethylene raw material after the quenching treatment with a pulverizer, and the particle size after pulverization is 100-1000 μm;

[0065] 3) Put the pulverized polytetrafluoroethylene raw material into the sealed cavity on the circulating trolley of the electron accelerator;

[0066] 4) Seal the electron accelerator, and open the air intake mechanism, and pass ozone on the surface of the polytetrafluoroethylene on the circulating trolley, and the weight ratio of the introduced ozone to the polytetrafluoroethylene raw material in the tray is 0.3%;

[0067] 5) Turn on the spraying device, and the spraying device sprays hydrogen peroxide on the polytetrafluoroet...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparation of ultrafine PTFE (polytetrafluoroethylene) powder by combining electron beams with ozone and hydrogen peroxide. The method comprises the steps of: packaging a dried PTFE raw material with a low temperature resistant container and putting the container in liquid nitrogen to undergo quenching, and then taking it out; comminuting the quenched PTFE raw material by a comminutor; putting the comminuted PTFE raw material on a cycling trolley of an electron accelerator; closing the electron accelerator, introducing ozone to the surface of the PTFE on the cycling trolley, starting a spraying device, which sprays hydrogen peroxide to the PTFE raw material on the cycling trolley, starting the electron accelerator, irradiating the PTFE raw material, putting the irradiated PTFE into an airflow pulverization system to undergo complete pulverizing and classification, thus obtaining the ultrafine PTFE powder. The preparation method provided in the invention is simple, can reduce the irradiation time and irradiation dose, thereby reducing the cost, and increases the degradation rate of PTFE.

Description

technical field [0001] The invention relates to the technical field of chemical industry, in particular to a method for preparing PTEE ultrafine powder by electron beam irradiation combined with ozone and hydrogen peroxide. Background technique [0002] Polytetrafluoroethylene (PTFE) ultrafine powder is a low molecular weight fine powder, also known as "PTFE wax". The average particle size of PTFE ultrafine powder is less than 5μm, and the specific surface area is greater than 10m 2 / g, the friction coefficient is about 0.06-0.07, it has good lubricity and can be well dispersed in many materials. [0003] The purity of PTFE products is 100%, the molecular weight is less than 10,000, and the PTFE micropowder series with a particle size of 0.5 μm not only maintains the original excellent properties of PTFE, but also has many unique properties, such as no self-coagulation, no Electrostatic effect, good compatibility, low molecular weight, good dispersibility. High self-lubric...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B02C21/00B02C19/06C08J3/28
Inventor 顾建忠吴明红蔡建球
Owner 佛山市顺德区顺泰昌粉末五金塑料有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com