A bronzing paste and emulsion technology, applied in dyeing method, transfer printing method, textile and papermaking, etc., can solve the problems of no bronzing effect, poor washing fastness, hard hand feeling, etc. Soft-touch effect
Active Publication Date: 2013-08-21
GUANGZHOU SHENGQIN IND
View PDF5 Cites 22 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
But for a long time, clothing bronzing has defects such as hard hand feeling, poor washing fastness, and bronzing effect is not as shiny as bronzing on plastic.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0030] Bronzing paste, made from raw materials comprising the following parts by weight:
[0031] Acrylate Emulsion 61,
[0032] deionized water 3,
[0033] Solvent 4,
[0034] Stabilizer 2,
[0035] Hot melt adhesive powder 11,
[0036] Silica 0.6,
[0037] Defoamer 0.3,
[0038] pH regulator 0.2,
[0039] Preservatives 0.12,
[0040] Emulsifying wetting agent 0.4;
[0041] Thickener 0.5.
Embodiment 2
[0043] Bronzing paste, made from raw materials comprising the following parts by weight:
[0044] Acrylate Emulsion 79,
[0045] deionized water 5,
[0046] Solvent 9,
[0047] Stabilizer 4,
[0048] Hot melt adhesive powder 19,
[0049] Silica 2.9,
[0050] Defoamer 0.45,
[0051] pH regulator 0.45,
[0052] Preservatives 0.19,
[0053] Emulsifying wetting agent 0.9
[0054] thickener 1.9.
Embodiment 3
[0056] Bronzing paste, made from raw materials comprising the following parts by weight:
[0057] Acrylate Emulsion 67,
[0058] deionized water 3,
[0059] Solvent 7,
[0060] Stabilizer 2,
[0061] Hot melt adhesive powder 18,
[0062] Silica 1,
[0063] Defoamer 0.4,
[0064] pH regulator 0.3,
[0065] Preservatives 0.15,
[0066] emulsifying wetting agent 0.6,
[0067] Thickener 0.8.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses bronzing pulp. The bronzing pulp is prepared from the following raw materials in parts by weight: 60-80 parts of acrylic ester emulsion, 2-6 parts of deionized water, 3-10 parts of a solvent, 1-5 parts of a stabilizer, 10-20 parts of EVA (Ethylene-Vinyl Acetate) hot melt adhesive powder, 0.5-3 parts of silica, 0.2-0.5 part of a polyurethane defoaming agent, 0.1-0.5 part of a pH regulator, 0.1-0.2 part of a preservative, 0.3-1 part of an emulsion wetting agent and 0.4-2 parts of a thickener. The bronzing pulp has the beneficial effects that the bronzing pulp is water-based pulp, the raw materials are easy to obtain and environment-friendly, the production is convenient, the technology is mature, and substances harmful to the environment can not be produced; and the bronzing pulp is soft in handfeel, firm in fastness, outstanding in resistance to tension fracture and diversified in application mode, enriches the styles of textiles, and endows the textiles with the noble quality.
Description
technical field [0001] The invention relates to the field of textile printing materials, in particular to bronzing paste and a preparation method thereof. Background technique [0002] Prior Art In clothing printing, bronzing has become a fashion symbol because of its brilliance. But for a long time, clothing bronzing has defects such as hard hand feeling, poor washing fastness, and the bronzing effect is not as shiny as bronzing on plastics. As consumers favor bronzing effects, these problems are becoming more and more prominent. Therefore, customers urgently need to solve these problems. Contents of the invention [0003] Aiming at the deficiencies in the above-mentioned prior art, the purpose of the present invention is to provide a bronzing paste with soft hand feeling, firm fastness and outstanding cracking resistance. [0004] Another object of the present invention is to provide a method for preparing the above bronzing paste. [0005] In order to achieve the ab...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.