Mixed type foundry waste sand wet reclamation wastewater processing method

A technology of casting waste sand and wet regeneration, which is applied in the fields of water/sewage multi-stage treatment, water/sludge/sewage treatment, chemical instruments and methods, etc. Problems such as high moisture content of mud, to achieve the effect of reducing moisture content, reducing land occupation, and increasing settlement area

Active Publication Date: 2013-10-16
广西兰科资源再生利用有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Treating a large amount of wastewater requires a large amount of space, resulting in high wastewater treatment costs, and the sludge obtained after wastewater treatment has a very high moisture content, which is likely to cause secondary pollution
If the problem of wastewater treatment is not solved, it will restrict the popularization and application of wet sand recycling waste sand technology, and the recycling of waste sand will be empty talk

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mixed type foundry waste sand wet reclamation wastewater processing method
  • Mixed type foundry waste sand wet reclamation wastewater processing method
  • Mixed type foundry waste sand wet reclamation wastewater processing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The wastewater treatment method for wet regeneration of mixed casting waste sand comprises the following steps:

[0027] (1) Demulsification: By adding 0.01% AR demulsifier to the wastewater, the emulsified liquid structure is destroyed, so as to separate the solid and liquid phases in the emulsion;

[0028] (2) Primary flocculation: pump the wastewater into the first-stage spiral flocculation tank, add polyaluminium chloride with a weight concentration of 10%, and add 1 / 800 of the wastewater weight, and flocculate for 20 seconds.

[0029] (3) Secondary flocculation: transfer the material in the primary spiral flocculation tank to the secondary spiral flocculation tank, add polyacrylamide (PAM) solution with a weight concentration of 0.1%, the amount added is 1 / 800 of the weight of the wastewater, and flocculate 80 seconds, then transfer the material in the secondary spiral flocculation tank to the inclined plate thickening box, and let it settle for 30 minutes;

[003...

Embodiment 2

[0032] The wastewater treatment method for wet regeneration of mixed casting waste sand comprises the following steps:

[0033] (1) Demulsification: By adding 0.03% AR demulsifier to the wastewater, the emulsified liquid structure is destroyed, so as to separate the solid and liquid phases in the emulsion;

[0034] (2) Primary flocculation: pump the wastewater into the first-stage spiral flocculation tank, add polyaluminum sulfate solution with a weight concentration of 10%, the amount added is 1 / 1000 of the wastewater weight, and flocculate for 30 seconds.

[0035] (3) Secondary flocculation: Transfer the material in the primary spiral flocculation tank into the secondary spiral flocculation tank, add PAM solution with a weight concentration of 0.2%, and the amount added is 1 / 1000 of the wastewater weight, flocculate for 70 seconds, and then put The material in the secondary spiral flocculation tank is transferred to the inclined plate thickening box, and left to settle for 4...

Embodiment 3

[0038] The wastewater treatment method for wet regeneration of mixed casting waste sand comprises the following steps:

[0039] (1) Demulsification: By adding 0.05% AR demulsifier to the waste water, the emulsified liquid structure is destroyed, so as to separate the solid and liquid phases in the emulsion;

[0040] (2) Primary flocculation: pump the wastewater into the first-stage spiral flocculation tank, add polyferric sulfate solution with a weight concentration of 10%, the amount added is 1 / 1200 of the wastewater weight, and flocculate for 50 seconds.

[0041] (3) Secondary flocculation: transfer the material in the primary spiral flocculation tank to the secondary spiral flocculation tank, and add polydimethyldiallylammonium chloride (PDMDAAC) solution with a weight concentration of 0.3%, and the addition amount is 1 / 1100 of the waste water weight, flocculate for 60 seconds, then transfer the material in the secondary spiral flocculation tank to the inclined plate thicke...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a mixed type foundry waste sand wet reclamation wastewater processing method. Firstly, wastewater is demulsified, and large suspended matters in the wastewater are flocculated in a spiral flocculating tank by virtue of an inorganic flocculating agent; then small suspended matters are flocculated by virtue of an organic flocculating agent; through standing sedimentation in an inclined tube sedimentation tank, a flocculation layer forming at the bottom in a condensed manner is extracted through a sludge pump at the bottom of the sedimentation tank; the organic flocculating agent is secondarily used, and finally, a band type concentration-vacuum-filter pressing all-in-one machine is used for treatment, so that the water content of sludge discharged at an outlet of a filter cake of the band type concentration-vacuum-filter pressing all-in-one machine is less than 40%; therefore, supernate overflowing from the inclined tube sedimentation tank and clear water from a clear water outlet of the band type concentration-vacuum-filter pressing all-in-one machine can achieve the requirement for production cycle water and the standard for direct discharge.

Description

technical field [0001] The invention relates to the recycled waste water of foundry waste sand wet process after treatment, in particular to the method for the recycled waste water of mixed casting waste sand regenerated after treatment. Background technique [0002] Since 2000, the average growth rate of my country's foundry industry has been above 10%, becoming the world's largest producer of castings. In 2011, my country's casting production has exceeded 40 million tons, ranking first in the world. The emission of pollutants in the entire foundry industry in China is as follows: 2 million tons of dust, 4×10 waste gas 6 -8×10 6 10,000 cubic meters, 12 million tons of waste residue, and 50-60 million tons of waste sand. At present, except for a small amount of waste sand that can be reused after dry regeneration, most of the waste sand is mainly discarded and landfilled, which greatly wastes limited resources and causes serious pollution to the environment. [0003] Chi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C02F9/04
Inventor 戴伟平罗桂猛刘临琦
Owner 广西兰科资源再生利用有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap