A tunnel grouting and prestressing technology, which is applied in erecting/assembling bridges, bridge construction, bridges, etc., can solve problems such as serious bleeding, abnormal hardening strength, and unguaranteed grouting quality

Active Publication Date: 2013-11-20
TAIYUAN UNIV OF TECH
View PDF3 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention provides a prestressed tunnel grouting material and a grouting method thereof, which solve the problems of serious bleeding, failure to harden normally and problems caused by post-tensioned prestressed concrete tunnel grouting construction under the environmental

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Prestressed pore pressure slurry and grouting method thereof
  • Prestressed pore pressure slurry and grouting method thereof
  • Prestressed pore pressure slurry and grouting method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0053] Example 1

[0054] For on-site construction, select raw materials and mix them evenly in the following proportions.

[0055]

[0056] According to the water-binder ratio of 0.27, the mixing water temperature is 40℃, add water first and then pressurize the slurry. Use a stirring machine slurry with a rotating speed of 1440r / min and a linear speed of 15m / s. After stirring for 5 minutes, squeeze the slurry immediately. See the technical specifications of the slurry. Table 1.

Example Embodiment

[0057] Example 2

[0058] On-site construction, the raw materials are mixed evenly according to the following ratio.

[0059]

[0060] According to the water-binder ratio of 0.27, the mixing water temperature is 40℃, add water first and then pressurize the slurry. Use a stirring machine slurry with a rotating speed of 1440r / min and a linear speed of 15m / s. After stirring for 5 minutes, squeeze the slurry immediately. See the technical specifications of the slurry. Table 1.

[0061]

Example Embodiment

[0062] Example 3

[0063] On-site construction, the raw materials are mixed evenly according to the above ratio.

[0064]

[0065] According to the water-binder ratio of 0.27, the mixing water temperature is 40℃, add water first and then pressurize the slurry. Use a stirring machine slurry with a rotating speed of 1440r / min and a linear speed of 15m / s. After stirring for 5 minutes, squeeze the slurry immediately. See the technical specifications of the slurry. Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides prestressed pore pressure slurry and a grouting method thereof. The pore pressure slurry is composed of cement, a water reducing agent, a retarder, a coagulant, an antifreezing agent, an expanding agent, active mineral powder and mineral filler powder. The pore grouting method comprises the following steps of: mixing the raw materials according to the composition and content to prepare pressure slurry, firstly adding water, and then, adding the pressure slurry into an agitator according to a certain ratio of water to the pressure slurry, controlling the rotating speed, time and water temperature for pulping, and immediately grouting. The prestressed pore pressure slurry provided by the invention has the advantages of low water-binder ratio, high fluidity and no water seepage, such heat preservation measures as steam curing are not adopted under the environment of minus 5 DEG C to 5 DEG C, the final setting time of the slurry is not larger than 5h, and the 28d strength is not smaller than 50 MPa, so that the prestressed pore pressure slurry is an energy-saving and environment-friendly building material.

Description

technical field [0001] The invention relates to a prestressed tunnel press grout and a grouting method thereof, more specifically, a prestressed tunnel press grout and a grouting method used in an environment of -5°C to +5°C. Background technique [0002] Prestressed concrete is widely used in bridge structures due to its unique economic and technical advantages. Grouting of tunnels is a key process of prestressed concrete construction. Its main functions are: first, to protect the prestressed steel strands from being exposed and avoid corrosion; The second is to make the prestressed steel strand and concrete well combined to ensure the effective transmission of prestress, so that the prestressed steel strand and concrete load together; the third is to eliminate the prestressed concrete structure under repeated loads, due to stress changes on the anchorage The fatigue damage caused by it improves the reliability and durability of the component. [0003] Studies have shown t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/04C04B28/06E01D21/00
Inventor 杨艳青张卫珂李育珍高丽丽逯新宇
Owner TAIYUAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap